Microstructure and Hot Deformation Behavior of Twin Roll Cast Mg-2Zn-1Al-0.3Ca Alloy.


ABSTRACT: In the present work, the microstructure, texture, mechanical properties as well as hot deformation behavior of a Mg-2Zn-1Al-0.3Ca sheet manufactured by twin roll casting were investigated. The twin roll cast state reveals a dendritic microstructure with intermetallic compounds predominantly located in the interdendritic areas. The twin roll cast samples were annealed at 420 °C for 2 h followed by plane strain compression tests in order to study the hardening and softening behavior. Annealing treatment leads to the formation of a grain structure, consisting of equiaxed grains with an average diameter of approximately 19 µm. The twin roll cast state reveals a typical basal texture and the annealed state shows a weakened texture, by spreading basal poles along the transverse direction. The twin roll cast Mg-2Zn-1Al-0.3Ca alloy offers a good ultimate tensile strength of 240 MPa. The course of the flow curves indicate that dynamic recrystallization occurs during hot deformation. For the validity range from 250 °C to 450 °C as well as equivalent logarithmic strain rates from 0.01 s-1 to 10 s-1 calculated model coefficients are shown. The average activation energy for plastic flow of the twin roll cast and annealed Mg-2Zn-1Al-0.3Ca alloy amounts to 180.5 kJ/mol. The processing map reveals one domain with flow instability at temperatures above 370 °C and strain rates ranging from 3 s-1 to 10 s-1. Under these forming conditions, intergranular cracks arose and grew along the grain boundaries.

SUBMITTER: Kittner K 

PROVIDER: S-EPMC6479906 | BioStudies | 2019-01-01

SECONDARY ACCESSION(S): 10.13140/RG.2.1.5029.3927

REPOSITORIES: biostudies

Similar Datasets

2017-01-01 | S-EPMC5556021 | BioStudies
2014-01-01 | S-EPMC5456430 | BioStudies
2020-01-01 | S-EPMC7772342 | BioStudies
2016-01-01 | S-EPMC5456789 | BioStudies
2015-01-01 | S-EPMC5458924 | BioStudies
2017-01-01 | S-EPMC5503366 | BioStudies
2020-01-01 | S-EPMC7177373 | BioStudies
1000-01-01 | S-EPMC6317036 | BioStudies
2017-01-01 | S-EPMC5503308 | BioStudies
2016-01-01 | S-EPMC5456840 | BioStudies