{"database":"biostudies-literature","file_versions":[],"scores":null,"additional":{"omics_type":["Unknown"],"volume":["117(33)"],"submitter":["Bachmann M"],"pubmed_abstract":["Adsorption and coadsorption of carbon monoxide and oxygen on different types of Au clusters on R(15 × 3)C/W(110) and R(15 × 12)C/W(110), respectively, are studied with respect to the catalytic behavior for oxidation of CO as well as of surface carbon. Carburization of the W(110) surface results in a weakening of the adsorption bond for molecularly adsorbed CO. Dissociation of carbon monoxide, which occurs on W(110), is reduced on the low-carbon coverage R(15 × 12) surface and completely suppressed on the carbon-saturated R(15 × 3) phase. Deposition of gold results in a blocking of adsorption sites for molecularly adsorbed CO and reopening of the dissociation channel. Probably the latter is associated with the existence of double-layer gold clusters and islands. At room temperature the gold clusters on both carburized templates are stable in CO atmosphere as shown by in-situ STM measurements. In contrast, exposure to oxygen alters the clusters on the R(15 × 12) surface, implying dissociation of oxygen not only on the substrate but also on or in immediate vicinity of the gold clusters. On the Au-free carburized templates oxygen adsorbs dissociatively and is released as CO at temperatures beyond 800 K due to reaction with carbon atoms from the templates. Deposition of gold enhances the desorption rate of the formed CO at the low-temperature end of the recombinative CO desorption range, indicating a promoting effect of gold for oxidation of surface carbon. In contrast, low-temperature CO oxidation catalyzed by the deposited Au clusters is not observed. Two reasons could be identified: (1) weakly bound CO with desorption temperatures between 100 and 200 K (as reported for other related systems) is not observed, and (2) oxygen atoms are bonded too strongly to the templates."],"journal":["The journal of physical chemistry. C, Nanomaterials and interfaces"],"pagination":["17024-17032"],"full_dataset_link":["https://www.ebi.ac.uk/biostudies/studies/S-EPMC3753032"],"repository":["biostudies-literature"],"pubmed_title":["Adsorption and Reactions of Carbon Monoxide and Oxygen on Bare and Au-Decorated Carburized W(110)."],"pmcid":["PMC3753032"],"pubmed_authors":["Bachmann M","Memmel N","Bertel E","Bikaljevic D"],"additional_accession":[]},"is_claimable":false,"name":"Adsorption and Reactions of Carbon Monoxide and Oxygen on Bare and Au-Decorated Carburized W(110).","description":"Adsorption and coadsorption of carbon monoxide and oxygen on different types of Au clusters on R(15 × 3)C/W(110) and R(15 × 12)C/W(110), respectively, are studied with respect to the catalytic behavior for oxidation of CO as well as of surface carbon. Carburization of the W(110) surface results in a weakening of the adsorption bond for molecularly adsorbed CO. Dissociation of carbon monoxide, which occurs on W(110), is reduced on the low-carbon coverage R(15 × 12) surface and completely suppressed on the carbon-saturated R(15 × 3) phase. Deposition of gold results in a blocking of adsorption sites for molecularly adsorbed CO and reopening of the dissociation channel. Probably the latter is associated with the existence of double-layer gold clusters and islands. At room temperature the gold clusters on both carburized templates are stable in CO atmosphere as shown by in-situ STM measurements. In contrast, exposure to oxygen alters the clusters on the R(15 × 12) surface, implying dissociation of oxygen not only on the substrate but also on or in immediate vicinity of the gold clusters. On the Au-free carburized templates oxygen adsorbs dissociatively and is released as CO at temperatures beyond 800 K due to reaction with carbon atoms from the templates. Deposition of gold enhances the desorption rate of the formed CO at the low-temperature end of the recombinative CO desorption range, indicating a promoting effect of gold for oxidation of surface carbon. In contrast, low-temperature CO oxidation catalyzed by the deposited Au clusters is not observed. Two reasons could be identified: (1) weakly bound CO with desorption temperatures between 100 and 200 K (as reported for other related systems) is not observed, and (2) oxygen atoms are bonded too strongly to the templates.","dates":{"release":"2013-01-01T00:00:00Z","publication":"2013 Aug","modification":"2021-02-21T00:30:20Z","creation":"2019-03-27T01:15:01Z"},"accession":"S-EPMC3753032","cross_references":{"pubmed":["23991229"],"doi":["10.1021/jp404528p"]}}