biostudies-literatureUnknown8(1)Qiao ZWater-based superamphiphobic coatings that are environmentally friendly have attracted tremendous attention recently, but their performances are severely limited by dispersibility and mechanical durability. Herein, a dispersion of poly(tetrafluoroethylene)/SiO<sub>2</sub>@cetyltrimethoxysilane&sodium silicate-modified aluminum tripolyphosphate (PTFE/SiO<sub>2</sub>@CTMS&Na<sub>2</sub>SiO<sub>3</sub>-ATP) superamphiphobic coatings was formed by mechanical dispersion of poly(tetrafluoroethylene) emulsion (PTFE), modified silica emulsion (SiO<sub>2</sub>@CTMS), sodium silicate (Na<sub>2</sub>SiO<sub>3</sub>), and modified aluminum tripolyphosphate (modified ATP). The four kinds of emulsions were mixed together to effectively solve the dispersity of waterborne superamphiphobic coatings. RobustACS omega804-818https://www.ebi.ac.uk/biostudies/studies/S-EPMC9835640biostudies-literatureFabrication of Robust Waterborne Superamphiphobic Coatings with Antifouling, Heat Insulation, and Anticorrosion.PMC9835640Ren GTuo YGao YLu CChen XQiao ZfalseFabrication of Robust Waterborne Superamphiphobic Coatings with Antifouling, Heat Insulation, and Anticorrosion.Water-based superamphiphobic coatings that are environmentally friendly have attracted tremendous attention recently, but their performances are severely limited by dispersibility and mechanical durability. Herein, a dispersion of poly(tetrafluoroethylene)/SiO<sub>2</sub>@cetyltrimethoxysilane&sodium silicate-modified aluminum tripolyphosphate (PTFE/SiO<sub>2</sub>@CTMS&Na<sub>2</sub>SiO<sub>3</sub>-ATP) superamphiphobic coatings was formed by mechanical dispersion of poly(tetrafluoroethylene) emulsion (PTFE), modified silica emulsion (SiO<sub>2</sub>@CTMS), sodium silicate (Na<sub>2</sub>SiO<sub>3</sub>), and modified aluminum tripolyphosphate (modified ATP). The four kinds of emulsions were mixed together to effectively solve the dispersity of waterborne superamphiphobic coatings. Robust2023-01-01T00:00:00Z2023 Jan2025-04-18T13:25:04.666Z2025-04-06T23:04:18.983ZS-EPMC98356403664343210.1021/acsomega.2c06145