Antibacterial Activity of Solvothermal Obtained ZnO Nanoparticles with Different Morphology and Photocatalytic Activity against a Dye Mixture: Methylene Blue, Rhodamine B and Methyl Orange.

ABSTRACT: In this paper, we report the synthesis of ZnO nanoparticles (NPs) by forced solvolysis of Zn(CH₃COO)₂·2H₂O in alcohols with a different number of -OH groups. We study the influence of alcohol type (n-butanol, ethylene glycol and glycerin) on the size, morphology, and properties of the obtained ZnO NPs. The smallest polyhedral ZnO NPs (<30 nm) were obtained in n-butanol, while in ethylene glycol the NPs measured on average 44 nm and were rounded. Polycrystalline particles of 120 nm were obtained in glycerin only after water refluxing. In addition, here, we report the photocatalytic activity, against a dye mixture, of three model pollutants: methyl orange (MO), methylene blue (MB), and rhodamine B (RhB), a model closer to real situations where water is polluted with many chemicals. All samples exhibited good photocatalytic activity against the dye mixture, with degradation efficiency reaching 99.99%. The sample with smallest nanoparticles maintained a high efficiency >90%, over five catalytic cycles. Antibacterial tests were conducted against Gram-negative strains Salmonella enterica serovar Typhimurium, Pseudomonas aeruginosa, and Escherichia coli, and Gram-positive strains Enterococcus faecalis, Bacillus subtilis, Staphylococcus aureus, and Bacillus cereus. The ZnO samples presented strong inhibition of planktonic growth for all tested strains, indicating that they can be used for antibacterial applications, such as water purification.

SUBMITTER: Motelica L

PROVIDER: S-EPMC10058279 | biostudies-literature | 2023 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Antibacterial Activity of Solvothermal Obtained ZnO Nanoparticles with Different Morphology and Photocatalytic Activity against a Dye Mixture: Methylene Blue, Rhodamine B and Methyl Orange.

Motelica Ludmila L Oprea Ovidiu-Cristian OC Vasile Bogdan-Stefan BS Ficai Anton A Ficai Denisa D Andronescu Ecaterina E Holban Alina Maria AM

International journal of molecular sciences 20230316 6

In this paper, we report the synthesis of ZnO nanoparticles (NPs) by forced solvolysis of Zn(CH3COO)2·2H2O in alcohols with a different number of -OH groups. We study the influence of alcohol type (n-butanol, ethylene glycol and glycerin) on the size, morphology, and properties of the obtained ZnO NPs. The smallest polyhedral ZnO NPs (<30 nm) were obtained in n-butanol, while in ethylene glycol the NPs measured on average 44 nm and were rounded. Polycrystalline p ...[more]

PMID: 36982751

Similar Datasets

Project description:In this study, a variety of ZnO-based heterojunctions with disparate wt.% doping of WO3 and BiOI have been prepared for the photodestruction of methyl orange (MO) dye in aqueous solution. The composites were analysed by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, optical studies, and nitrogen adsorption-desorption isotherms. The SEM images revealed non-uniform surfaces of the ZnO-BiOI based composites while mostly nodular morphology was observed for all three samples of ZnO-WO3. As the WO3 loading increased, more clustering was detected. The analysed samples exhibited characteristic peaks representative of the triclinic phase of WO3 and the hexagonal wurtzite structure of ZnO, while the diffractogram observed from the materials displayed distinct peaks corresponding to the crystalline phases of both BiOI and ZnO in their pure forms. Further evidence of the samples' characteristics includes the presence of distinct crystalline patterns without any impurity peaks, a red shift in the absorption spectra of the heterostructure, the detection of only the reference elements, and mostly Type IV isotherm adsorption. This study identified the ZnO-[10%]BiOI and ZnO-[10%]WO3 heterojunctions as the best performing photocatalysts, as MO was completely destroyed in 120 and 90 min, respectively. Thus, confirming 10% wt. as the optimal doping concentration for the best photo-activity in this study. The impact of varying process parameters demonstrates that at an elevated photocatalyst mass of 40 mg, both heterojunctions effectively degraded MO. The photodegradation efficiency of MO was more pronounced in strong acidic conditions (pH 2) when compared to high alkaline conditions (pH 11) for the ZnO-[10%]BiOI heterostructure. However, a decrease in performance was observed for both strong acidic and high alkaline pH values when the ZnO-[10%]WO3 heterostructure was applied. The kinetic analysis of the photodegradation study reveals that all the photodegradation experiments can be represented by the pseudo-first-order kinetic model. The findings from this investigation propose that the ZnO-[10%]BiOI heterojunction photocatalyst holds significant potential for the effective treatment of dye-contaminated wastewater.

Project description:Heterogeneous photocatalysis has been considered one of the most effective and efficient techniques to remove organic contaminants from wastewater. The present work was designed to examine the photocatalytic performance of metal (Cu and Ni) doped ZnO nanocomposites in methyl orange (MO) dye degradation under UV light illumination. The wurtzite hexagonal structure was observed for both undoped/doped ZnO and a crystalline size ranging between 8.84 ± 0.71 to 12.91 ± 0.84 nm by X-ray diffraction (XRD) analysis. The scanning electron microscope (SEM) and energy dispersive X-ray (EDX) revealed the irregular spherical shape with particle diameter (34.43 ± 6.03 to 26.43 ± 4.14 nm) and ensured the purity of the individual elemental composition respectively. The chemical bonds (O-H group) and binding energy (1021.8 eV) were identified by Fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS) results respectively. The bandgap energy was decreased from 3.44 to 3.16 eV when Ni dopant was added to the ZnO lattice. The comparative photocatalytic activity was observed in undoped and doped nanocomposites and found to be 76.31%, 81.95%, 89.30%, and 83.39% for ZnO, Cu/ZnO, Ni/ZnO, and Cu/Ni/ZnO photocatalysts, respectively, for a particular dose (0.210 g) and dye concentration (10 mg L-1) after 180 min illumination of UV light. The photocatalytic performance was increased up to 94.40% with the increase of pH (12.0) whereas reduced (35.12%) with an increase in initial dye concentration (40 mg L-1) using Ni/ZnO nanocomposite. The Ni/ZnO nanocomposite showed excellent reusability and was found 81% after four consecutive cycles. The best-fitted reaction kinetics was followed by pseudo-first-order and found reaction rate constant (0.0117 min-1) using Ni/ZnO nanocomposite. The enhanced photodegradation efficiency was observed due to decreases in bandgap energy and the crystalline size of the photocatalyst. Therefore, Ni/ZnO nanocomposite could be used as an emerging photocatalyst to degrade bio-persistent organic dye compounds from textile wastewater.

Dataset Information

Antibacterial Activity of Solvothermal Obtained ZnO Nanoparticles with Different Morphology and Photocatalytic Activity against a Dye Mixture: Methylene Blue, Rhodamine B and Methyl Orange.

Publications

Antibacterial Activity of Solvothermal Obtained ZnO Nanoparticles with Different Morphology and Photocatalytic Activity against a Dye Mixture: Methylene Blue, Rhodamine B and Methyl Orange.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets