Investigation of TiO₂ Deposit on SiO₂ Films: Synthesis, Characterization, and Efficiency for the Photocatalytic Discoloration of Methylene Blue in Aqueous Solution.

ABSTRACT: TiO₂-SiO₂ thin films were created on Corning glass substrates using a simple method. Nine layers of SiO₂ were deposited; later, several layers of TiO₂ were deposited, and their influence was studied. Raman spectroscopy, high resolution transmission electron spectroscopy (HRTEM), an X-ray diffractometer (XRD), ultraviolet-visible spectroscopy (UV-Vis), a scanning electron microscope (SEM), and atomic force microscopy (AFM) were used to describe the sample's shape, size, composition, and optical characteristics. Photocatalysis was realized through an experiment involving the deterioration of methylene blue (MB) solution exposed to UV-Vis radiation. With the increase of TiO₂ layers, the photocatalytic activity (PA) of the thin films showed an increasing trend, and the maximum degradation efficiency of MB by TiO₂-SiO₂ was 98%, which was significantly higher than that obtained by SiO₂ thin films. It was found that an anatase structure was formed at a calcination temperature of 550 °C; phases of brookite or rutile were not observed. Each nanoparticle's size was 13-18 nm. Due to photo-excitation occurring in both the SiO₂ and the TiO₂, deep UV light (λ = 232 nm) had to be used as a light source to increase photocatalytic activity.

SUBMITTER: Acosta-Silva YJ

PROVIDER: S-EPMC10146845 | biostudies-literature | 2023 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Investigation of TiO2 Deposit on SiO2 Films: Synthesis, Characterization, and Efficiency for the Photocatalytic Discoloration of Methylene Blue in Aqueous Solution.

Acosta-Silva Yuliana de Jesús YJ Toledano-Ayala Manuel M Gallardo-Hernández Salvador S Godínez Luis A LA Méndez-López Arturo A

Nanomaterials (Basel, Switzerland) 20230419 8

TiO2-SiO2 thin films were created on Corning glass substrates using a simple method. Nine layers of SiO2 were deposited; later, several layers of TiO2 were deposited, and their influence was studied. Raman spectroscopy, high resolution transmission electron spectroscopy (HRTEM), an X-ray diffractometer (XRD), ultraviolet-visible spectroscopy (UV-Vis), a scanning electron microscope (SEM), and atomic force microscopy (AFM) were used to describe the samp ...[more]

PMID: 37110988

Similar Datasets

Project description:SiO2@TiO2 core-shell nanoparticles were successfully synthesized via a simple, reproducible, and low-cost method and tested for methylene blue adsorption and UV photodegradation, with a view to their application in wastewater treatment. The monodisperse SiO2 core was obtained by the classical Stöber method and then coated with a thin layer of TiO2, followed by calcination or hydrothermal treatments. The properties of SiO2@TiO2 core-shell NPs resulted from the synergy between the photocatalytic properties of TiO2 and the adsorptive properties of SiO2. The synthesized NPs were characterized using FT-IR spectroscopy, HR-TEM, FE-SEM, and EDS. Zeta potential, specific surface area, and porosity were also determined. The results show that the synthesized SiO2@TiO2 NPs that are hydrothermally treated have similar behaviors and properties regardless of the hydrothermal treatment type and synthesis scale and better performance compared to the SiO2@TiO2 calcined and TiO2 reference samples. The generation of reactive species was determined by EPR, and the photocatalytic activity was evaluated by the methylene blue (MB) removal in aqueous solution under UV light. Hydrothermally treated SiO2@TiO2 showed the highest adsorption capacity and photocatalytic removal of almost 100% of MB after 15 min in UV light, 55 and 89% higher compared to SiO2 and TiO2 reference samples, respectively, while the SiO2@TiO2 calcined sample showed 80%. It was also observed that the SiO2-containing samples showed a considerable adsorption capacity compared to the TiO2 reference sample, which improved the MB removal. These results demonstrate the efficient synergy effect between SiO2 and TiO2, which enhances both the adsorption and photocatalytic properties of the nanomaterial. A possible photocatalytic mechanism was also proposed. Also noteworthy is that the performance of the upscaled HT1 sample was similar to one of the lab-scale synthesized samples, demonstrating the potentiality of this synthesis methodology in producing candidate nanomaterials for the removal of contaminants from wastewater.

Project description:In this study, we successfully synthesized a TiO2/CuO nanocomposite using the aqueous extract of Impatiens tinctoria A.rich. leaf extract as a capping, reducing, and stabilizing agent for the first time in an environmentally friendly, low-cost, straightforward, and sustainable technique. Numerous characterization techniques such as ultraviolet-visible diffuse reflectance spectroscopy (UV-vis-DRS), photoluminescence (PL), Raman spectroscopy, Fourier-transform infrared (FTIR), energy dispersive X-ray (EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET), and high resolution TEM (HRTEM) were used to characterize the obtained TiO2/CuO nanocomposite. XRD verified that the TiO2/CuO nanocomposite has an average crystallite size of about 21 nm. The TEM result revealed an average particle size of 29 nm for the biosynthesized TiO2/CuO NC. The HRTEM analysis showed the presence of polycrystalline structures with the predominant lattice fringes 0.352 and 0.19 which were attributed to anatase phase TiO2 in the crystal plane of (101) and (200), respectively. The lattice fringes for monoclinic CuO were observed with values of 0.213 and 0.252 for the lattice planes of (111) and (111̅), respectively. The photoluminescence spectroscopic analysis revealed that the TiO2/CuO NC showed the lowest intensity compared to the pristine TiO2 and CuO indicating the reduction of exciton recombination in the case of the TiO2/CuO NC. The BET analysis showcased the formation of mesoporous materials with a surface area of 87.5 m2/g. The photocatalytic degradation performance of the biosynthesized TiO2, CuO, and TiO2/CuO nanomaterials against the potentially harmful MB dye was tested using the light source of a 150 tungsten-halogen lamp with a wavelength range of 360-2800 nm. The factors affecting photodegradation efficiencies like catalyst dose (20 mg), dye concentration(15 ppm), pH (9), and reaction time (90 min) were optimized for the degradation of the MB dye. The TiO2/CuO catalyst showed the highest degradation efficiency of 99% under the optimized conditions. The degradation rate of the MB dye in the presence of the TiO2/CuO NC was evaluated and found to be fitted to the pseudo-first-order kinetics with a rate constant of 0.03 min-1. The reusability test of the TiO2/CuO catalyst showed its good stability.

Dataset Information

Investigation of TiO₂ Deposit on SiO₂ Films: Synthesis, Characterization, and Efficiency for the Photocatalytic Discoloration of Methylene Blue in Aqueous Solution.

Publications

Investigation of TiO<sub>2</sub> Deposit on SiO<sub>2</sub> Films: Synthesis, Characterization, and Efficiency for the Photocatalytic Discoloration of Methylene Blue in Aqueous Solution.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets