Functionalisation of Electrospun Cellulose Acetate Membranes with PEDOT and PPy for Electronic Controlled Drug Release.

ABSTRACT: Controlled drug release via electrical stimulation from drug-impregnated fibres was studied using electrospun cellulose acetate (CA) membranes and encapsulated ibuprofen (IBU). This research outlines the influence of polypyrrole (PPy) and poly(3,4-ethylenedioxythiophene) (PEDOT)-functionalised CA membranes and their suitability for dermal electronic-controlled drug release. Micro Raman analysis confirmed polymer functionalisation of CA membranes and drug incorporation. Scanning electron microscopy (SEM) images evidenced the presence of PPy and PEDOT coatings. The kinetic of drug release was analysed, and the passive and active release was compared. In the proposed systems, the drug release is controlled by very low electrical potentials. A potential of -0.3 V applied to membranes showed the ibuprofen retention, and a positive potential of +0.3 V, +0.5 V, or +0.8 V, depending on the conductive polymer and membrane configuration, enhanced the drug release. A small adhesive patch was constructed to validate this system for cutaneous application and verified an "ON/OFF" ibuprofen release pattern from membranes.

SUBMITTER: Lago B

PROVIDER: S-EPMC10180495 | biostudies-literature | 2023 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Functionalisation of Electrospun Cellulose Acetate Membranes with PEDOT and PPy for Electronic Controlled Drug Release.

Lago Beatriz B Brito Miguel M Almeida Cristina M M CMM Ferreira Isabel I Baptista Ana Catarina AC

Nanomaterials (Basel, Switzerland) 20230427 9

Controlled drug release via electrical stimulation from drug-impregnated fibres was studied using electrospun cellulose acetate (CA) membranes and encapsulated ibuprofen (IBU). This research outlines the influence of polypyrrole (PPy) and poly(3,4-ethylenedioxythiophene) (PEDOT)-functionalised CA membranes and their suitability for dermal electronic-controlled drug release. Micro Raman analysis confirmed polymer functionalisation of CA membranes and drug incorporation. Scanning electron microsco ...[more]

PMID: 37177038

Similar Datasets

Project description:Chitosan nanofibrous membranes have immense potential in tissue engineering and drug delivery applications because of their increased surface area, high degree of biocompatibility, and their ability to mimic the extracellular matrix. However, their use is often limited due to their extreme hydrophilic nature causing them to lose their nanofibrous structure in vivo. In the present study, chitosan membranes were modified either by acylation reactions using fatty acids of different chain lengths or tert-butyloxycarbonyl (tBOC) protecting groups to increase the hydrophobicity of the membranes and protect the nanofibrous structure. The modified membranes were characterized using scanning electron microscopy, attenuated total reflectance Fourier transform infrared spectroscopy, water contact angle and elemental analysis to confirm the addition of the modification groups. These membranes were then evaluated to control the release of a hydrophobic osteogenic drug-simvastatin (SMV). The interaction between SMV and the polymer was determined using molecular modeling. Pure SMV and SMV loaded membranes were examined for their in vitro cytotoxicity and osteogenic potential using preosteoblast mouse bone marrow stromal cells. From results, it was evident that as the fatty acid chain length increased from two to six methylene groups, the hydrophobicity of the membranes increased (59.2 ± 8.2° to 94.3 ± 8.5° water contact angle). The amount of drug released from the membranes could be controlled by changing the amount of initial drug loaded and/or the type of modifications. After 4 weeks, for a 500 μg loading, the short chain fatty acid modified membranes released 17.8 ± 3.2% of the drug whereas a long chain fatty acid released only 4.8 ± 0.8%. Similarly, for a 50 μg loading, short chain modified membranes released more (73.3 ± 33.3%) of the loaded drug as compared to the long chain membranes (43.0 ± 3.5%). The long chain fatty acid membranes released SMV for extended time periods of up to 90 days. This data was further supported by molecular modeling, which revealed that SMV was more compatible with more hydrophobic membranes. Cell studies showed that pure SMV from 75 to 600 ng/ml range possessed osteogenic potential in a dose dependent manner and the amount of SMV released from the most hydrophobic FA treated membranes was not cytotoxic and supported osteogenic differentiation. Therefore, this study demonstrates our ability to control the release of a hydrophobic drug from modified chitosan membranes as per the clinical need.

Project description:The antibacterial activity of garlic (Allium sativum) is believed to be due to its organosulfur compounds, which can supposedly be used further in biomedical applications. This paper reported the use of electrospinning to encapsulate a garlic extract and glycerine in nanofibrous mats. Polyvinylpyrrolidone (PVP) and cellulose acetate (CA) were the building blocks of the composite fibres that served as the hydrophilic matrix to encapsulate the garlic extract with glycerine added mainly to improve the mechanical characteristics of the composite fibres. The combinations of the fibres were PVP/CA, PVP/CA/garlic, PVP/CA/glycerine, and PVP/CA/glycerine/garlic. The characterizations included the morphology, chemical interaction, swelling degree, weight loss, acidity level, wettability, in vitro antibacterial test, and release behaviour test. The composite nanofibrous mats were uniform, bead-free with a size ranging from 350 nm to 900 nm. The Fourier-transform infrared spectra proved the presence of the garlic extract and glycerine in the fibres. The swelling degree test showed that the fibrous mats generally did have maximum swelling degrees above 100% except for the PVP/CA fibrous mat, whose maximum value was not achieved within 48 hours. The fibrous mat with glycerine showed generally larger weight loss compared to the fibrous mats without glycerine. The result of the contact angle measurement proved that the composite fibres are all hydrophilic with the PVP/CA/glycerine/garlic fibres being the least hydrophilic. The pH level of the fibre mats was from 3.7 to 4.0 due to the use of acetic acid. The Young's modulus and ultimate tensile strength of the mats were significantly reduced due to the presence of glycerine. The encapsulation of the garlic extract in the fibres did not eliminate the antibacterial activity of the garlic extract, as proven in the in vitro antibacterial test. The release of the garlic extract from the composite PVP/CA/glycerine/garlic fibres was found to be the largest due to the large diameter of the fibres, while the blend of PVP with CA successfully reduced the rate of release due to the insolubility of CA. We successfully encapsulated the garlic extract and glycerine in the PVP/CA nanofibrous mats with antibacterial activity.

Dataset Information

Functionalisation of Electrospun Cellulose Acetate Membranes with PEDOT and PPy for Electronic Controlled Drug Release.

Publications

Functionalisation of Electrospun Cellulose Acetate Membranes with PEDOT and PPy for Electronic Controlled Drug Release.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets