Highly thermostable mixed lanthanide organic frameworks with high quantum yield for warm white light-emitting diodes

ABSTRACT: A mixed lanthanide organic framework was prepared via hydrothermal methods using m-phthalic acid (m-H2BDC), 1,10-phenanthroline (1,10-Phen), and Ln3+ ions, formulated as [HNMe2][Eu0.095Tb1.905(m-BDC)3(phen)2] (ZTU-6). The structure and stability of ZTU-6 were characterised by X-ray diffraction (XRD) and thermogravimetric analysis (TGA), which revealed a three-dimensional pcu topology with high thermal stability. Fluorescence tests showed that ZTU-6 emitted orange light with a high quantum yield of 79.15%, and it can be effectively encapsulated in a light-emitting diode (LED) device emitting orange light. In addition, ZTU-6 was found to be compatible with BaMgAl10O17:Eu2+ (BAM) blue powder and [(Sr,Ba)2SiO4:Eu2+] silicate yellow and green powder to create a warm white LED with a high colour rendering index (CRI) of 93.4, a correlated colour temperature (CCT) of 3908 K, and CIE coordinates of (0.38, 036).

SUBMITTER: Shen Y

PROVIDER: S-EPMC10239934 | biostudies-literature | 2023 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Electroluminescent Warm White Light-Emitting Diodes Based on Passivation Enabled Bright Red Bandgap Emission Carbon Quantum Dots.

Project description:The development of efficient red bandgap emission carbon quantum dots (CQDs) for realizing high-performance electroluminescent warm white light-emitting diodes (warm-WLEDs) represents a grand challenge. Here, the synthesis of three red-emissive electron-donating group passivated CQDs (R-EGP-CQDs): R-EGP-CQDs-NMe2, -NEt2, and -NPr2 is reported. The R-EGP-CQDs, well soluble in common organic solvents, display bright red bandgap emission at 637, 642, and 645 nm, respectively, reaching the highest photoluminescence quantum yield (QY) up to 86.0% in ethanol. Theoretical investigations reveal that the red bandgap emission originates from the rigid π-conjugated skeleton structure, and the -NMe2, -NEt2, and -NPr2 passivation plays a key role in inducing charge transfer excited state in the π-conjugated structure to afford the high QY. Solution-processed electroluminescent warm-WLEDs based on the R-EGP-CQDs-NMe2, -NEt2, and -NPr2 display voltage-stable warm white spectra with a maximum luminance of 5248-5909 cd m-2 and a current efficiency of 3.65-3.85 cd A-1. The warm-WLEDs also show good long-term operational stability (L/L 0 > 80% after 50 h operation, L 0: 1000 cd m-2). The electron-donating group passivation strategy opens a new avenue to realizing efficient red bandgap emission CQDs and developing high-performance electroluminescent warm-WLEDs.

| S-EPMC6662328 | biostudies-literature

Vinylene-Linked Emissive Covalent Organic Frameworks for White-Light-Emitting Diodes.

Project description:Covalent organic frameworks (COFs) have gained considerable attention due to their highly conjugated π-skeletons, rendering them promising candidates for the design of light-emitting materials. In this study, we present two vinylene-linked COFs, namely, VL-COF-1 and VL-COF-2, which were synthesized through the Knoevenagel condensation of 2,4,6-trimethyl-1,3,5-triazine with terephthalaldehyde or 4,4'-biphenyldicarboxaldehyde. Both VL-COF-1 and VL-COF-2 exhibited excellent chemical and thermal stability. The presence of vinylene linkages between the constituent building blocks in these COFs resulted in broad excitation and emission properties. Remarkably, the designed VL-COFs demonstrated bright emission, fast fluorescence decay, and high stability, making them highly attractive for optoelectronic applications. To assess the potential of these VL-COFs in practical devices, we fabricated white-light-emitting diodes (WLEDs) coated with VL-COF-1 and VL-COF-2. Notably, the WLEDs coated with VL-COF-1 achieved high-quality white light emission, closely approximating standard white light. The promising performance of VL-COF-coated WLEDs suggests the feasibility of utilizing COF materials for stable and efficient lighting applications.

| S-EPMC10535042 | biostudies-literature

Organic-Inorganic Hybrid Cuprous-Based Metal Halides for Warm White Light-Emitting Diodes.

Project description:Single-component emitters with stable and bright warm white-light emission are highly desirable for high-efficacy warm white light-emitting diodes (warm-WLEDs), however, materials with such luminescence properties are extremely rare. Low-dimensional lead (Pb) halide perovskites can achieve warm white photoluminescence (PL), yet they suffer from low stability and PL quantum yield (PLQY). While Pb-free air-stable perovskites such as Cs2 AgInCl6 emit desirable warm white light, sophisticated doping strategies are typically required to increase their PL intensity. Moreover, the use of rare metal-bearing compounds along with the typically required vacuum-based thin-film processing may greatly increase their production cost. Herein, organic-inorganic hybrid cuprous (Cu+ )-based metal halide MA2 CuCl3 (MA = CH3 NH3 + ) that meets the requirements of i) nontoxicity, ii) high PLQY, and iii) dopant-free is presented. Both single crystals and thin films of MA2 CuCl3 can be facilely prepared by a low-cost solution method, which demonstrate bright warm white-light emission with intrinsically high PLQYs of 90-97%. Prototype electroluminescence devices and down-conversion LEDs are fabricated with MA2 CuCl3 thin films and single crystals, respectively, which show bright luminescence with decent efficiencies and operational stability. These findings suggest that MA2 CuCl3 has a great potential for the single-component indoor lighting and display applications.

| S-EPMC9631088 | biostudies-literature

Lanthanide complexes with d-f transition: new emitters for single-emitting-layer white organic light-emitting diodes.

Project description:White organic light-emitting diodes (WOLEDs) is a new generation of lighting technology and has stimulated wide-ranging studies. Despite the advantage of simple device structure, single-emitting-layer WOLEDs (SEL-WOLEDs) still face the challenges of difficult material screening and fine energy level regulation. Herein, we report efficient SEL-WOLEDs with a sky-blue emitting cerium(III) complex Ce-TBO2Et and an orange-red emitting europium(II) complex Eu(Tp2Et)2 as the emitters, showing a maximum external quantum efficiency of 15.9% and Commission Internationale de l'Eclairage coordinates of (0.33, 0.39) at various luminances. Most importantly, the electroluminescence mechanism of direct hole capture and hindered energy transfer between the two emitters facilitate a manageable weight doping concentration of 5% for Eu(Tp2Et)2, avoiding the low concentration (<1%) of the low-energy emitter in typical SEL-WOLEDs. Our results indicate that d-f transition emitters may circumvent fine energy level regulation and provide development potential for SEL-WOLEDs.

| S-EPMC10328933 | biostudies-literature

Warm White Light-Emitting Diodes Based on a Novel Orange Cationic Iridium(III) Complex.

Project description:A novel orange cationic iridium(III) complex [(TPTA)₂Ir(dPPOA)]PF₆ (TPTA: 3,4,5-triphenyl-4H-1,2,4-triazole, dPPOA: N,N-diphenyl-4-(5-(pyridin-2-yl)-1,3,4-oxadiazol-2-yl)aniline) was synthesized and used as a phosphor in light-emitting diodes (LEDs). [(TPTA)₂Ir(dPPOA)]PF₆ has high thermal stability with a decomposition temperature (Td) of 375 °C, and its relative emission intensity at 100 °C is 88.8% of that at 25°C. When only [(TPTA)₂Ir(dPPOA)]PF₆ was used as a phosphor at 6.0 wt % in silicone and excited by a blue GaN (GaN: gallium nitride) chip (450 nm), an orange LED was obtained. A white LED fabricated by a blue GaN chip (450 nm) and only yellow phosphor Y₃Al₅O12:Ce3+ (YAG:Ce) (1.0 wt % in silicone) emitted cold white light, its CIE (CIE: Commission International de I'Eclairage) value was (0.32, 0.33), color rendering index (CRI) was 72.2, correlated color temperature (CCT) was 6877 K, and luminous efficiency (ηL) was 128.5 lm∙W-1. Such a cold white LED became a neutral white LED when [(TPTA)₂Ir(dPPOA)]PF₆ was added at 0.5 wt %; its corresponding CIE value was (0.35, 0.33), CRI was 78.4, CCT was 4896 K, and ηL was 85.2 lm∙W-1. It further became a warm white LED when [(TPTA)₂Ir(dPPOA)]PF₆ was added at 1.0 wt %; its corresponding CIE value was (0.39, 0.36), CRI was 80.2, CCT was 3473 K, and ηL was 46.1 lm∙W-1. The results show that [(TPTA)₂Ir(dPPOA)]PF₆ is a promising phosphor candidate for fabricating warm white LEDs.

| S-EPMC5554038 | biostudies-literature

Highly Efficient and Stable White Light-Emitting Diodes Using Perovskite Quantum Dot Paper.

Project description:Perovskite quantum dots (PQDs) are a competitive candidate for next-generation display technologies as a result of their superior photoluminescence, narrow emission, high quantum yield, and color tunability. However, due to poor thermal resistance and instability under high energy radiation, most PQD-based white light-emitting diodes (LEDs) show only modest luminous efficiency of ≈50 lm W-1 and a short lifetime of <100 h. In this study, by incorporating cellulose nanocrystals, a new type of QD film is fabricated: CH3NH3PbBr3 PQD paper that features 91% optical absorption, intense green light emission (518 nm), and excellent stability attributed to the complexation effect between the nanocellulose and PQDs. The PQD paper is combined with red K2SiF6:Mn4+ phosphor and blue GaN LED chips to fabricate a high-performance white LED demonstrating ultrahigh luminous efficiency (124 lm W-1), wide color gamut (123% of National Television System Committee), and long operation lifetime (240 h), which paves the way for advanced lighting technology.

| S-EPMC6918104 | biostudies-literature

Quantum Dot-Acrylic Acrylate Oligomer Hybrid Films for Stable White Light-Emitting Diodes.

Project description:White light-emitting diodes (LEDs) have been achieved using photopolymerization. Red and green CdSe/ZnS core-shell quantum dots (QDs) are dispersed in photopolymerized aliphatic acrylic acrylate resins, cured by using 36 W UV light for 1.5 min producing QD-acrylate nanocomposites, and then a hybrid LED device is achieved using the QD-acrylate nanocomposite with two emission wavelengths excited by using a blue InGaN LED chip. The cured QD-acrylate nanocomposite films are characterized by using ultraviolet-visible, fluorescence, scanning electron microscopy, atomic force microscopy, and thermogravimetric analysis measurements. Photopolymerization is conveniently employed to adjust several parameters of the CIE-1931 coordinate (x, y), color temperature, and color rending index (CRI). Good white balance of the red-green hybrid device achieves a luminance of 7976 lm/m2 at a 30 mA working current. The light emission efficiency, CRI, and color temperature of 14%, 47, and 11 204 K, respectively, are attained at this working current.

| S-EPMC6648638 | biostudies-literature

Atomically thin quantum light-emitting diodes.

Project description:Transition metal dichalcogenides are optically active, layered materials promising for fast optoelectronics and on-chip photonics. We demonstrate electrically driven single-photon emission from localized sites in tungsten diselenide and tungsten disulphide. To achieve this, we fabricate a light-emitting diode structure comprising single-layer graphene, thin hexagonal boron nitride and transition metal dichalcogenide mono- and bi-layers. Photon correlation measurements are used to confirm the single-photon nature of the spectrally sharp emission. These results present the transition metal dichalcogenide family as a platform for hybrid, broadband, atomically precise quantum photonics devices.

| S-EPMC5052681 | biostudies-literature

Yellow fluorescent graphene quantum dots as a phosphor for white tunable light-emitting diodes.

Project description:In recent decades, quantum dots have been considered to be highly promising photoluminescent materials for white light devices. During the application of quantum dots in the fabrication of white LEDs, the spectrum and color temperature of the devices are modulated; these devices often involve quantum dots with different emission wavelengths. In this study, yellow-green emitting graphene quantum dots (GQDs) were fabricated using a simple, low-cost and eco-friendly method. The obtained GQDs were cast in UV-curable siloxane. Then, a polymer film with superior optical transparency and excellent monodisperse properties of GQDs was formed. Via the simple adjustment of thickness and the GQD concentration of the color convert matrix, tunable color temperatures (3196-10 870 K) of the GQD-based white light-emitting diodes (LEDs) were achieved. The CIE (Commission Internationale de L'Eclairage) coordinates of the GQD-based white light-emitting diodes matched well with the blackbody radiation curve. Using the fluorescent polymeric matrix in white LEDs, good quality emission and gratifying stability could be obtained. Moreover, this indicates that this technology has the potential for applications in high-end lighting.

| S-EPMC9061975 | biostudies-literature

Origin of White Electroluminescence in Graphene Quantum Dots Embedded Host/Guest Polymer Light Emitting Diodes.

Project description:Polymer light emitting diodes (PLEDs) using quantum dots (QDs) as emissive materials have received much attention as promising components for next-generation displays. Despite their outstanding properties, toxic and hazardous nature of QDs is a serious impediment to their use in future eco-friendly opto-electronic device applications. Owing to the desires to develop new types of nano-material without health and environmental effects but with strong opto-electrical properties similar to QDs, graphene quantum dots (GQDs) have attracted great interest as promising luminophores. However, the origin of electroluminescence from GQDs incorporated PLEDs is unclear. Herein, we synthesized graphene oxide quantum dots (GOQDs) using a modified hydrothermal deoxidization method and characterized the PLED performance using GOQDs blended poly(N-vinyl carbazole) (PVK) as emissive layer. Simple device structure was used to reveal the origin of EL by excluding the contribution of and contamination from other layers. The energy transfer and interaction between the PVK host and GOQDs guest were investigated using steady-state PL, time-correlated single photon counting (TCSPC) and density functional theory (DFT) calculations. Experiments revealed that white EL emission from the PLED originated from the hybridized GOQD-PVK complex emission with the contributions from the individual GOQDs and PVK emissions.

| S-EPMC4463941 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data