Antimicrobial activity of ion-substituted calcium phosphates: A systematic review.

ABSTRACT: In this systematic review, the antimicrobial effect of ion-substituted calcium phosphate biomaterials was quantitatively assessed. The literature was systematically searched up to the 6th of December 2021. Study selection and data extraction was performed in duplo by two independent reviewers with a modified version of the OHAT tool for risk of bias assessment. Any differences were resolved by consensus or by a referee. A mixed effects model was used to investigate the relation between the degree of ionic substitution and bacterial reduction. Of 1016 identified studies, 108 were included in the analysis. The methodological quality of included studies ranged from 6 to 16 out of 18 (average 11.4). Selenite, copper, zinc, rubidium, gadolinium, silver and samarium had a clear antimicrobial effect, with a log reduction in bacteria count of 0.23, 1.8, 2.1, 3.6, 5.8, 7.4 and 10 per atomic% of substitution, respectively. There was considerable between-study variation, which could partially be explained by differences in material formulation, study quality and microbial strain. Future research should focus on clinically relevant scenarios in vitro and the translation to in vivo prevention of PJI.

SUBMITTER: Kamphof R

PROVIDER: S-EPMC10248076 | biostudies-literature | 2023 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Antimicrobial activity of ion-substituted calcium phosphates: A systematic review.

Kamphof Robert R Lima Rui N O RNO Schoones Jan W JW Arts Jacobus J JJ Nelissen Rob G H H RGHH Cama Giuseppe G Pijls Bart G C W BGCW

Heliyon 20230526 6

In this systematic review, the antimicrobial effect of ion-substituted calcium phosphate biomaterials was quantitatively assessed. The literature was systematically searched up to the 6th of December 2021. Study selection and data extraction was performed in duplo by two independent reviewers with a modified version of the OHAT tool for risk of bias assessment. Any differences were resolved by consensus or by a referee. A mixed effects model was used to investigate the relation between the degre ...[more]

PMID: 37303579

Similar Datasets

Project description:PurposeThis study developed light cured dental composites with added monocalcium phosphate monohydrate (MCPM), tristrontium phosphate (TSrP) and antimicrobial polylysine (PLS). The aim was to produce composites that have enhanced water sorption induced expansion, can promote apatite precipitation and release polylysine.Materials and methodsExperimental composite formulations consisted of light activated dimethacrylate monomers combined with 80 wt% powder. The powder phase contained a dental glass with and without PLS (2.5 wt%) and/or reactive phosphate fillers (15 wt% TSrP and 10 wt% MCPM). The commercial composite, Z250, was used as a control. Monomer conversion and calculated polymerization shrinkage were assessed using FTIR. Subsequent mass or volume changes in water versus simulated body fluid (SBF) were quantified using gravimetric studies. These were used, along with Raman and SEM, to assess apatite precipitation on the composite surface. PLS release was determined using UV spectroscopy. Furthermore, biaxial flexural strengths after 24 hours of SBF immersion were obtained.ResultsMonomer conversion of the composites decreased upon the addition of phosphate fillers (from 76 to 64%) but was always higher than that of Z250 (54%). Phosphate addition increased water sorption induced expansion from 2 to 4% helping to balance the calculated polymerization shrinkage of ~ 3.4%. Phosphate addition promoted apatite precipitation from SBF. Polylysine increased the apatite layer thickness from ~ 10 to 20 μm after 4 weeks. The novel composites showed a burst release of PLS (3.7%) followed by diffusion-controlled release irrespective of phosphate addition. PLS and phosphates decreased strength from 154 MPa on average by 17% and 18%, respectively. All formulations, however, had greater strength than the ISO 4049 requirement of > 80 MPa.ConclusionThe addition of MCPM with TSrP promoted hygroscopic expansion, and apatite formation. These properties are expected to help compensate polymerization shrinkage and help remineralize demineralized dentin. Polylysine can be released from the composites at early time. This may kill residual bacteria.

Dataset Information

Antimicrobial activity of ion-substituted calcium phosphates: A systematic review.

Publications

Antimicrobial activity of ion-substituted calcium phosphates: A systematic review.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets