Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

ABSTRACT: Polyurethane is widely used to toughen epoxy resins due to its excellent comprehensive properties and compatibility. However, some demerits of polyurethanes limit their applications, such as the harsh storage condition of isocyanate-terminated polyurethane (ITPU), the limited amount of ITPU in epoxy resin, and using solvents during the preparation of polyurethane-modified epoxy resins. To address these issues, in this study, we reported a facile and green approach for preparing epoxy-terminated polyurethane (EPU)-modified epoxy resins with different EPU contents. It was found that the toughness of the epoxy resin was significantly improved after the addition of EPU. When the EPU content was 30 wt%, the elongation at break and toughness were improved by 358.36% and 73.56%, respectively. In comparison, the toughening effect of EPU outperformed that of ITPU. Moreover, the high content of EPU did not significantly decrease the glass transition temperature and had little effect on the thermal stability of the epoxy resin.

SUBMITTER: Zhang K

PROVIDER: S-EPMC10346895 | biostudies-literature | 2023 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

Zhang Kun K Huang Jinrui J Wang Yigang Y Li Wenbin W Nie Xiaoan X

Polymers 20230624 13

Polyurethane is widely used to toughen epoxy resins due to its excellent comprehensive properties and compatibility. However, some demerits of polyurethanes limit their applications, such as the harsh storage condition of isocyanate-terminated polyurethane (ITPU), the limited amount of ITPU in epoxy resin, and using solvents during the preparation of polyurethane-modified epoxy resins. To address these issues, in this study, we reported a facile and green approach for preparing epoxy-terminated ...[more]

PMID: 37447449

Similar Datasets

Project description:In this work, ammonium polyphosphate (APP) was surface-modified by bio-based arginine (Arg) for the first time to enhance its flame retardance for fire-safety epoxy resin (EP). The structure of Arg modified APP (Arg-APP) was characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), 1H nuclear magnetic resonance (1H-NMR), and scanning electron microscopy (SEM). The results illustrated that Arg was attached on the surface of APP through a cation exchange reaction. With Arg acting as the efficient carbon source, the char-forming ability of Arg-APP was significantly improved as illustrated by thermogravimetric analysis (TGA). The flame retardance of EP/APP and EP/Arg-APP composites was evaluated using the limit oxygen index (LOI), vertical burning tests (UL-94), and cone calorimeter tests (CCT). The results showed that at the same weight loading (15 wt%), Arg-APP had better flame retardance and smoke suppression performance compared with pristine APP, which can be attributed to Arg-APP constituting an integrated intumescent flame retardant (IFR) and facilitating formation of char residues with significantly expanded structures and higher carbonization degrees. When the weight loading of Arg-APP reached 25 wt%, the EP/Arg-APP composite could achieve an LOI value as high as 34.7%, pass V-0 requirements in UL-94 tests, and decrease the peak heat release rate and total smoke production by 83.5% and 61.1% compared with neat EP in CCT, respectively, indicating the superior flame retardance performance of Arg-APP. Finally, the effects of the flame retardant additives on the mechanical properties of EP were evaluated by the differential scanning calorimetry (DSC) tests and tensile-strain tests. At the same additive weight loading (15 wt%), the EP/Arg-APP composite showed higher glass-transition temperature and better tensile-strain properties compared with EP/APP composite, which can be attributed to the Arg shell structure improving the compatibility between APP and the organic substrate. In conclusion, this work presents a convenient and environmentally friendly method to improve the practical performance of APP.

Dataset Information

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

Publications

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets