The synthesis and development of poly(ε-caprolactone) conjugated polyoxyethylene sorbitan oleate-based micelles for curcumin drug release: an in vitro study on breast cancer cells.

ABSTRACT:

Background

it is now known that curcumin (Cur) has a broad range of biological properties; however, photosensitivity, as well as low bioavailability and short half-life, have limited its clinical application. To overcome these problems the synthesis of poly(ε-caprolactone)-Tween 80 (PCL-T) copolymers was performed.

Methods

the copolymers of PCL-T were created using the solvent evaporation/extraction technique. Then Cur was loaded in PCL-T micelles (PCL-T-M) by a self-assembly method. The characterization of copolymer and micelles was assessed by gel permeation chromatography (GPC), Fourier transform infrared spectroscopy (FT-IR), proton nuclear magnetic resonance spectroscopy (¹HNMR), differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and dynamic light scattering (DLS) methods. The MTT [3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide] assay was used to indicate the cytotoxicity of the free Cur, PCL-T-M, and Cur-loaded PCL-T-M.

Results

TEM analysis showed monodispersed and spherical shapes with a size of about 90 nm. Cur was released from PCL-T-M at pH 7.4 (45%) and 5.5 (90%) during 6 days. After 24 and 48 h, the IC50 of the free Cur, PCL-T-M, and Cur-loaded PCL-T-M on MCF-7 cells were 80.86 and 54.45 μg mL^-1, 278.30 and 236.19 μg mL^-1, 45.47 and 19.05 μg mL^-1, respectively.

Conclusion

this study showed that, in the same concentration, the effectiveness of the Cur-loaded PCL-T-M is more than the free Cur, and the nano-system has been able to overcome delivery obstacles of Cur drug. Thus, PCL-T-M can be a candidate as a drug carrier for the delivery of Cur and future therapeutic investigations on breast cancer.

SUBMITTER: Shadmani N

PROVIDER: S-EPMC10401665 | biostudies-literature | 2023 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The synthesis and development of poly(ε-caprolactone) conjugated polyoxyethylene sorbitan oleate-based micelles for curcumin drug release: an <i>in vitro</i> study on breast cancer cells.

Shadmani Nasim N Gohari Sepehr S Kadkhodamanesh Azin A Ghaderinia Parivash P Hassani Maryam M Sharifyrad Motahare M

RSC advances 20230804 34

<h4>Background</h4>it is now known that curcumin (Cur) has a broad range of biological properties; however, photosensitivity, as well as low bioavailability and short half-life, have limited its clinical application. To overcome these problems the synthesis of poly(ε-caprolactone)-Tween 80 (PCL-T) copolymers was performed.<h4>Methods</h4>the copolymers of PCL-T were created using the solvent evaporation/extraction technique. Then Cur was loaded in PCL-T micelles (PCL-T-M) by a self-assembly meth ...[more]

PMID: 37546220

Similar Datasets

Project description:Vascular endothelial growth factor (VEGF) is the major regulating factor for the formation of new blood vessels, also known as angiogenesis. VEGF is often incorporated in synthetic scaffolds to promote vascularization and to enhance the survival of cells that have been seeded in these devices. Such applications require sustained local delivery of VEGF of around 4 weeks for stable blood vessel formation. Most delivery systems for VEGF only provide short-term release for a couple of days, followed by a release phase with very low VEGF release. We now have developed VEGF-loaded polymeric microspheres that provide sustained release of bioactive VEGF for 4 weeks. Blends of two swellable poly(ε-caprolactone)-poly(ethylene glycol)-poly(ε-caprolactone)-b-poly(l-lactide) ([PCL-PEG-PCL]-b-[PLLA])-based multiblock copolymers with different PEG content and PEG molecular weight were used to prepare the microspheres. Loading of the microspheres was established by a solvent evaporation-based membrane emulsification method. The resulting VEGF-loaded microspheres had average sizes of 40-50 μm and a narrow size distribution. Optimized formulations of a 50:50 blend of the two multiblock copolymers had an average VEGF loading of 0.79 ± 0.09%, representing a high average VEGF loading efficiency of 78 ± 16%. These microspheres released VEGF continuously over 4 weeks in phosphate-buffered saline pH 7.4 at 37 °C. This release profile was preserved after repeated and long-term storage at -20 °C for up to 9 months, thereby demonstrating excellent storage stability. VEGF release was governed by diffusion through the water-filled polymer matrix, depending on PEG molecular weight and PEG content of the polymers. The bioactivity of the released VEGF was retained within the experimental error in the 4-week release window, as demonstrated using a human umbilical vein endothelial cells proliferation assay. Thus, the microspheres prepared in this study are suitable for embedment in polymeric scaffolds with the aim of promoting their functional vascularization.