Programming Crystallographic Orientation in Additive-Manufactured Beta-Type Titanium Alloy.

ABSTRACT: Additively manufactured metallic materials typically exhibit preferential <001> or <110> crystallographic orientations along the build direction. Nowadays, the challenge is to program crystallographic orientation along arbitrary 3D direction in additive-manufactured materials. In this work, it is established a technique of multitrack coupled directional solidification (MTCDS) to program the <001> crystallographic orientation along an arbitrary 3D direction in biomedical beta-type Ti-Nb-Zr-Ta alloys via laser powder bed fusion (LPBF). MTCDS can be achieved via directional solidification of coupled multi-track melt pools with a specific temperature gradient direction. This results in continuous epitaxial growth of the β-Ti phase and consequently sets the <001> crystallographic orientation along an arbitrary 3D direction. This way, relatively low elastic modulus values of approximately 60 ± 1.2 GPa are customized along an arbitrary 3D direction. It is expected that MTCDS can be generalized to a wide range of applications for programming specific crystallographic orientations and, respectively, tailoring desired properties of different metallic materials.

SUBMITTER: Luo X

PROVIDER: S-EPMC10558665 | biostudies-literature | 2023 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Programming Crystallographic Orientation in Additive-Manufactured Beta-Type Titanium Alloy.

Luo Xuan X Song Tao T Gebert Annett A Neufeld Kai K Kaban Ivan I Ma Hongwei H Cai Weisi W Lu Haizhou H Li Dongdong D Li Ning N Li Yuanyuan Y Yang Chao C

Advanced science (Weinheim, Baden-Wurttemberg, Germany) 20230728 28

Additively manufactured metallic materials typically exhibit preferential <001> or <110> crystallographic orientations along the build direction. Nowadays, the challenge is to program crystallographic orientation along arbitrary 3D direction in additive-manufactured materials. In this work, it is established a technique of multitrack coupled directional solidification (MTCDS) to program the <001> crystallographic orientation along an arbitrary 3D direction in biomedical beta-type Ti-Nb-Zr-Ta all ...[more]

PMID: 37507830

Similar Datasets

Project description:In this work, a near β-type Ti5.1Al2.5Cr0.5Fe4.5Mo1.1Sn1.8Zr2.9Zn alloy was hot-rolled at the temperature of 800-880 °C with a thickness reduction of 87.5% and then heat-treated with the strategy of 880 °C/1 h/air cooling (AC) + 650 °C/3 h/AC. The microstructure difference between the hot-rolled and heat-treated titanium alloys and its influence on the ballistic impact behavior of the hot-rolled and heat-treated titanium alloys were analyzed. The microstructural investigation revealed that the average size of the acicular secondary α phase (αs) dropped from 75 to 42 nm, and the corresponding amount of this phase increased significantly after heat treatment. In addition, the dislocation density of the α and β phases decreased from 0.3340 × 1015/m2 and 4.6746 × 1015/m2 for the hot-rolled titanium alloy plate to 0.2806 × 1015/m2 and 1.8050 × 1015/m2 for the heat-treated one, respectively. The high strength of the heat-treated titanium alloy was maintained, owing to the positive contribution of the acicular secondary α phase. Furthermore, the critical fracture strain increased sharply from 19.9% for the hot-rolled titanium alloy plate to 23.1% for the heat-treated one, thereby overcoming (to some extent) the constraint of the strength-ductility trade-off. This is mainly attributed to the fact that the dislocation density and the difference between the dislocation densities of the α and β phases decreased substantially, and deformation localization was effectively suppressed after heat treatment. Damage to the hot-rolled and heat-treated titanium alloy plates after the penetration of a 7.62 mm ordinary steel core projectile at a distance of 100 m was assessed via industrial computer tomography and microstructure observation. The results revealed that a large crack (volume: 2.55 mm3) occurred on the rear face and propagated toward the interior of the hot-rolled titanium alloy plate. The crack tip was connected to a long adiabatic shear band with a depth of 3 mm along the thickness direction. However, good integrity of the heat-treated titanium alloy plate was maintained, owing to its excellent deformation capability. Ultimately, the failure mechanism of the hot-rolled and heat-treated titanium alloy plates was revealed by determining the crack-forming reasons in these materials.

Project description:The objective of the systematic review is to find an answer to a question: "Do surface treatments on titanium implants produced by additive manufacturing improve osseointegration, compared to untreated surfaces?". This review followed the Preferred Reporting Items for Systematic Review and Meta-Analysis (PRISMA 2020) and was registered in the International Prospective Register of Systematic Reviews (PROSPERO) (CRD42022321351). Searches were performed in PubMed, Scopus, Science Direct, Embase, and Google Scholar databases on March 22nd, 2022. Articles were chosen in 2 steps by 2 blinded reviewers based on previously selected inclusion criteria: articles in animals that addressed the influence of surface treatments on osseointegration in implants produced by additive manufacturing. Articles were excluded that (1) did not use titanium surface, 2) that did not evaluate surface treatments, 3) that did not described osseointegration, 4) Studies with only in vitro analyses, clinical studies, systematic reviews, book chapters, short communications, conference abstracts, case reports and personal opinions.). 1003 articles were found and, after applying the eligibility criteria, 17 were used for the construction of this review. All included studies found positive osseointegration results from performing surface treatments on titanium. The risk of bias was analyzed using the SYRCLE assessment tool. Surface treatments are proposed to promote changes in the microstructure and composition of the implant surface to favor the adhesion of bone cells responsible for osseointegration. It is observed that despite the benefits generated by the additive manufacturing process in the microstructure of the implant surface, surface treatments are still indispensable, as they can promote more suitable characteristics for bone-implant integration. It can be concluded that the surface treatments evaluated in this systematic review, performed on implants produced by additive manufacturing, optimize osseointegration, as it allows the creation of a micro-nano-textured structure that makes the surface more hydrophilic and allows better contact bone-implant.

Dataset Information

Programming Crystallographic Orientation in Additive-Manufactured Beta-Type Titanium Alloy.

Publications

Programming Crystallographic Orientation in Additive-Manufactured Beta-Type Titanium Alloy.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets