Analysis of Incremental Sheet Forming of Aluminum Alloy.

ABSTRACT: Recent developments in incremental sheet forming have resulted in the creation of novel manufacturing processes that are highly adaptable and could bring significant economic benefits for advanced technologies and low-volume production. In this manuscript, the following variables were examined: the variation in the deformation forces for a part with a pyramidal trunk shape; the variation in the deformations and thinning of the Al 3003 material during the incremental forming process; and the variation in the accuracy of the incrementally formed part and the quality of the surfaces (surface roughness). The components of the forces in the incremental forming have increasing values from the beginning of the process to the maximum value due to the hardening process. The TiN-coated tool ensures lower values of the forming components. Due to the kinematics of the forming process, deviations, especially in shape, from the part in the drawing are observed, which are shown by the radius of curvature of the side wall of the part, the appearance of a radius of connection between the wall and the bottom of the part, as well as dimensional deviations that are expressed by the variation in the forming depth. Concerning the smoothness of the surfaces, it was observed that the best roughness results were obtained in the case of the TiN-coated tool.

SUBMITTER: Coman CC

PROVIDER: S-EPMC10573285 | biostudies-literature | 2023 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Analysis of Incremental Sheet Forming of Aluminum Alloy.

Coman Costel Catalin CC Mazurchevici Simona-Nicoleta SN Carausu Constantin C Nedelcu Dumitru D

Materials (Basel, Switzerland) 20230923 19

Recent developments in incremental sheet forming have resulted in the creation of novel manufacturing processes that are highly adaptable and could bring significant economic benefits for advanced technologies and low-volume production. In this manuscript, the following variables were examined: the variation in the deformation forces for a part with a pyramidal trunk shape; the variation in the deformations and thinning of the Al 3003 material during the incremental forming process; and the vari ...[more]

PMID: 37834508

Similar Datasets

Project description:This study aims to solve the problem of springback control of aluminum alloy components in the rolling process, and the method of combining experiment and simulation is adopted. Firstly, a series of aluminum alloy samples are designed, and the four-axis flexible bending machine is used for precision roll bending. Secondly, the three-dimensional (3D) shape change data of the workpiece before and after roll bending is monitored and recorded in real-time by a high-precision 3D scanner. Meanwhile, aiming at different rolling process parameters of each group (including roll bend speed, feed rate, pre-deformation amount, mold curvature radius, and other factors), advanced finite element software is used to carry out detailed simulation and calculations. In addition, the coincidence is compared and analyzed between the actual experiment results and the simulation prediction. The stress-strain distribution and springback evolution of aluminum alloy during roll bending are described accurately. The experimental and simulation results show that the springback rate of aluminum alloy fluctuates in the range of 5% to 15% after four-axis flexible roll bending, and the specific springback value is influenced by various process parameters. For example, under the premise of keeping other conditions unchanged, when the roll bending speed is increased from 30mm/s to 60mm/s, the springback rate shows an upward trend of about 3%. By increasing the feed rate by 20%, an average decrease of about 7% in springback quantity is observed. It can be seen that the increase in roll bending speed can aggravate the springback phenomenon, and the appropriate increase in feed rate can play a certain role in restraining the springback. Further analysis shows that the choice of the mold curvature radius and pre-deformation amount also has a decisive influence on the springback characteristics. There is a nonlinear relationship between the two parameters and the amount of springback. Changing these two parameters in a specific range can effectively regulate the springback effect.

Dataset Information

Analysis of Incremental Sheet Forming of Aluminum Alloy.

Publications

Analysis of Incremental Sheet Forming of Aluminum Alloy.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets