Surface Area Determination of Particle-Based Mesoporous Films Using Krypton Physisorption.

ABSTRACT: One of the key characteristics of mesoporous films, making them attractive in many applications, is the surface enhancement gained by the porosity. Today, this attribute is rarely presented for particle-based mesoporous films. This work shows that krypton physisorption can be used to determine the available surface area of particle-based silica films synthesized by the direct growth (DiG) method. The surface area per substrate area of the films was measured to be 50-170 m²/m² and the surface area per film volume was 310-490 m²/cm³ when the film thickness was varied between 100 and 520 nm. For comparison, a 105 nm thick film synthesized using dip-coating was used, as this technique renders more smooth films. The corresponding values for the dip-coated film was 90 m²/m² and 880 m²/cm³, showing a higher surface area per film volume for the continuous film. The method is hence suitable for the characterization of mesoporous films synthesized with various techniques and can be used for the optimization of catalysts, drug delivery systems, and sensors.

SUBMITTER: Bjork EM

PROVIDER: S-EPMC10851385 | biostudies-literature | 2024 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Surface Area Determination of Particle-Based Mesoporous Films Using Krypton Physisorption.

Björk Emma M EM

ACS omega 20240127 5

One of the key characteristics of mesoporous films, making them attractive in many applications, is the surface enhancement gained by the porosity. Today, this attribute is rarely presented for particle-based mesoporous films. This work shows that krypton physisorption can be used to determine the available surface area of particle-based silica films synthesized by the direct growth (DiG) method. The surface area per substrate area of the films was measured to be 50-170 m<sup>2</sup>/m<sup>2</su ...[more]

PMID: 38343931

Similar Datasets

Project description:The selective recovery of ultrafine, <10 μm, particles remains a significant challenge in the minerals industry. Indeed, these particles often report to tailings impoundments, resulting in under-utilization of mined resources and the need for tailings dams. Recently, a technique has been developed offering the potential to selectively recover particles down to <1 μm in size. This technique, originally inspired by oil agglomeration, uses a high internal-phase water in oil emulsion as a binder to selectively agglomerate hydrophobic particles. Due to the significant concentration of the dispersed aqueous phase, ~95%, the continuous organic phase forms a network of very thin, permeable films, estimated to be 60 nm thick. These are stabilized by an emulsifier. In the high shear field of the agglomeration process, the binder is fragmented into smaller hydrophobic portions, delivering its thin film coating to the adhering hydrophobic particles. Permeation of water across the thin films eliminates the viscous hydrodynamic resistance, permitting sub-micron particle recovery to occur at rates similar to those for particles considerably larger in size. This recovery occurs within seconds under intense mixing. In this study, a model system consisting of magnetite, with a Sauter mean diameter of 11.4 μm, was agglomerated using the water in oil emulsion binder. The binder, which contained the emulsifier sorbitan monooleate, appeared to also act as a collector for the magnetite, thus no separate particle conditioning step was required. Curiously, however, the binder requirements were higher than expected. Further investigations concerning the stability of the binder revealed that the magnetite particles were causing rapid binder degradation. Therefore, prior to agglomeration using the binder, the particles were conditioned with sorbitan monooleate to render them hydrophobic. This pre-conditioning led to significant reductions in the binder dosage required to achieve agglomeration. Moreover, the resulting dosage matched that predicted by a model silica system for the same specific hydrophobic surface area, thus allowing a model to be validated based on the required binder dosage for a known hydrophobic surface area. Examination of binder stability in the presence of conditioned magnetite revealed that the now hydrophobic particles stabilized the binder.

Dataset Information

Surface Area Determination of Particle-Based Mesoporous Films Using Krypton Physisorption.

Publications

Surface Area Determination of Particle-Based Mesoporous Films Using Krypton Physisorption.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets