Biodegradable high-nitrogen iron alloy anastomotic staples: In vitro and in vivo studies.

ABSTRACT: For gastrointestinal anastomosis, metallic biodegradable staples have a broad application potential. However, both magnesium and zinc alloys have relatively low strength to withstand the repeated peristalsis of the gastrointestinal tract. In this study, we developed a novel kind of biodegradable high-nitrogen iron (HN-Fe) alloy wires (0.23 mm), which were fabricated into the staples. The tensile results showed that the ultimate tensile strength and elongation of HN-Fe wires were 1023.2 MPa and 51.0 %, respectively, which was much higher than those of other biodegradable wires. The degradation rate in vitro of HN-Fe wires was slightly higher than that of pure Fe wires. After 28 days of immersion, the tensile strength of HN-Fe wires remained not less than 240 MPa, meeting the clinical