Structural and Electrochemical Evolution of Water Hyacinth-Derived Activated Carbon with Gamma Pretreatment for Supercapacitor Applications
Ontology highlight
ABSTRACT:
SUBMITTER:
PROVIDER: S-EPMC11242469 | biostudies-literature | 2024 Jul
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Activated carbon monoliths of kenaf (ACMKs) were prepared by moulding kenaf fibers into a column-shape monolith and then carrying out pyrolysis at 500, 600, 700 or 800 °C, followed by activation with KOH at 700 °C. Then, the sample was characterized using thermogravimetric analyzer (TGA), field-emission scanning electron microscopy (FE-SEM), field-emission transmission electron microscopy (FE-TEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, X-ray diffraction (XRD) and N2 sorption instruments. The prepared ACMK was subjected to electrochemical property evaluation via cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) and electrochemical impedance spectroscopy (EIS). The GCD study using a three-electrode system showed that the specific capacitance decreased with higher pyrolysis temperature (PYT) with the ACMK pyrolyzed at 500 °C (ACMK-500) exhibiting the highest specific capacitance of 217 F g-1. A two-electrode system provided 95.9% retention upon a 5000 cycle test as well as the specific capacitance of 212 F g-1, being converted to an energy density of 6 W h kg-1 at a power density of 215 W kg-1.
| S-EPMC9044192 | biostudies-literature
Project description:Activated carbon xerogel monoliths were prepared from resorcinol and formaldehyde via a catalyst-free and template-free hydrothermal polycondensation reaction, followed by pyrolysis and activation. The ratio of resorcinol (R) to distilled water (W) was varied to afford an interconnected pore structure with controlled pore size, while the pyrolysis temperature was optimized to give high specific surface area. Activation was carried out at 700 °C after soaking the samples in 6 M KOH aqueous solution. The same process, called "heat treatment", was also carried out without soaking in KOH for comparison. The weight loss upon pyrolysis, activation and heat treatment and the weight gain via KOH soaking were measured. Field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, X-ray diffraction (XRD), thermogravimetric analysis (TGA) and an N2 sorption instrument were utilized for characterization. Additionally, electrochemical properties were evaluated using cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) and electrochemical impedance spectroscopy (EIS) with a 3-electrode system, while a 2-electrode system was also employed for selected samples. The highest specific capacitance of 323 F g-1 via GCD at 1 A g-1 was obtained at the R/W ratio of 45 and with 500 °C pyrolysis. In addition, this sample also exhibited 89.4% retention at 20 A g-1 in the current density variation and 100% retention in 5000 cycling tests.
| S-EPMC9042302 | biostudies-literature
Project description:A facile strategy, engineered for low-cost mass production, to synthesize biomass-derived activated carbon/reduced graphene oxide composite electrodes (GBPCs) by one-pot carbonization of blotting papers containing graphene oxide (GO) and zinc chloride (ZnCl2) was proposed. Benefitting from the water absorption characteristic of blotting papers in which the voids between the celluloses can easily absorb the GO/ZnCl2 solution, the chemical activation and reduction of GO can synchronously achieve via one-step carbonization process. As a result, the GBPCs deliver a large specific surface area to accumulate charge. Simultaneously, it provides high conductivity for electron transfer. The symmetric supercapacitor assembled with the optimal GBPCs in 6 M KOH electrolyte exhibits an excellent specific capacitance of 204 F g-1 (0.2 A g-1), outstanding rate capability of 100 F g-1 (20 A g-1). Meanwhile, it still keeps 90% of the initial specific capacitance over 10,000 cycles. The readily available raw material, effective chemical activation, simple rGO additive, and resulting electrochemical properties hold out the promise of hope to achieve low-cost, green, and large-scale production of practical activated carbon composite materials for high-efficiency energy storage applications.
| S-EPMC6943556 | biostudies-literature
Project description:Troublesome aquatic weed, water hyacinth (Eichhornia crassipes) was converted into solid and liquid fractions via green and energy-saving hydrothermal carbonization (HTC). The solid product, hydrochar, was employed as a precursor to prepare magnetic carbon materials by simple activation and magnetization using KOH and Fe3+ ions, respectively. The obtained magnetic adsorbent possessed good magnetic properties and presented outstanding capacities to adsorb methylene blue (524.20 mg g-1), methyl orange (425.15 mg g-1) and tetracycline (294.24 mg g-1) with rapid adsorption kinetics even at high concentrations (up to 500 mg L-1), attributed to high specific surface area and mesopore porosity. Besides the solid hydrochar, the water-soluble liquid product was used to fabricate carbon-based supercapacitors through facile KOH activation with a considerably lower KOH amount in comparison to conventional activation. The supercapacitor electrode made from activated liquid product possessed an extremely high specific surface area of 2545 cm2 g-1 and showed excellent specific capacitance (100 F g-1 or 50 F cm-3 at 1 A g-1) and good retention of capacitance (92% even after 10 000 cycles). This work demonstrated that both solid and liquid HTC fractions from this bio-waste can serve as effective sources to prepare functional carbon materials, making this approach a sustainable zero-waste biomass conversion process.
| S-EPMC9069585 | biostudies-literature
Project description:Biochar carbon YP-50 exposed to gamma radiation at 50 kGy, 100 kGy, and 150 kGy was used as an electrode for an electric double-layer capacitor. The gamma radiation affected the pore structure and pore volume of the biochar electrodes. The optimized surface morphology, pore structure, and pore volume of the biochar with an irradiation dose of 100 kGy showed outstanding specific capacitance of 246.2 F g-1 compared to the untreated biochar (115.3 F g-1). The irradiation dose of 100 kGy exhibited higher specific power and specific energy of 0.1 kW kg-1 and 34.2 W h kg-1 respectively, with a capacity retention of above 96% after 10 000 cycles at a current density of 2 A g-1. This improvement can be attributed to the decrease in average particle size, an increase in the porosity of biochar carbon. Besides, the charge transfer resistance of supercapacitor is significantly reduced from 21.7 Ω to 7.4 Ω after treating the biochar carbon with 100 kGy gamma radiation, which implies an increase in conductivity. This gamma radiation strategy to pretreat the carbon material for improving the properties of carbon materials can be promising for the development of high-performance supercapacitors for large-scale applications.
| S-EPMC9056314 | biostudies-literature
Project description:The MoS2 nanobelts/Carbon hybrid nanostructure was synthesized by the simple hydrothermal method. The MoS2 nanobelts were distributed in the interlayers of Lemon grass-derived carbon (LG-C), provides the active sites and avoid restacking of the sheets. The structural and morphological characterization of MoS2/LG-C and LG-C were performed by Raman spectroscopy, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy. The electrochemical measurements were studied with cyclic voltammetry, the galvanostatic charge-discharge method, and electrochemical impedance spectroscopy. The specific capacitance of MoS2/LG-C and LG-C exhibits 77.5 F g−1 and 30.1 F g−1 at a current density of 0.5 A g−1. The MoS2/LG-C-based supercapacitor provided the maximum power density and energy density of 273.2 W kg−1 and 2.1 Wh kg−1, respectively. Furthermore, the cyclic stability of MoS2/LG-C was tested using charging-discharging up to 3,000 cycles, confirming only a 71.6% capacitance retention at a current density of 3 A g−1. The result showed that MoS2/LG-C is a superior low-cost electrode material that delivered a high electrochemical performance for the next generation of electrochemical energy storage.
| S-EPMC10477701 | biostudies-literature
Project description:Sustainable and effective electrochemical materials for supercapacitors are greatly needed for solving the global problems of energy storage. In this regard, a facile nanocomposite of Pd/NiOPdO was synthesized using foliar phyto eco-friendly agents and examined as an electrochemical electrode active material for supercapacitor application. The nanocomposite showed a mixed phase of a ternary nano metal oxide phase of rhombohedral NiO and tetragonal PdO confirmed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and XPS (X-rays photoelectron spectroscopy). The optical (direct) energy value of the synthesized nanocomposite was 3.14 eV. The phyto-functionalized nanocomposite was studied for electrochemical supercapacitor properties and revealed a specific capacitance of 88 F g-1 and low internal resistance of 0.8 Ω. The nanoscale and phyto organic species functionalized nanocomposite exhibited enhanced electrochemical properties for supercapacitor application.
| S-EPMC9742768 | biostudies-literature
Project description:Graphene-based materials have been widely studied in the field of supercapacitors. However, their electrochemical properties and applications are still restricted by the susceptibility of graphene-based materials to curling and agglomeration during production. This study introduces a facile method for synthesizing reduced graphene oxide (rGO) nanosheets and activated carbon based on olive stones (OS) with polyaniline (PAni) surface decoration for the development of supercapacitors. Several advanced techniques were used to examine the structural properties of the samples. The obtained PAni@OS-rGO (1:1) electrode exhibits a high electrochemical capacity of 582.6 F·g-1 at a current density of 0.1 A·g-1, and an energy density of 26.82 Wh·kg-1; thus, it demonstrates potential for efficacious energy storage. In addition, this electrode material exhibits remarkable cycling stability, retaining over 90.07% capacitance loss after 3000 cycles, indicating a promising long cycle life. Overall, this research highlights the potential of biomass-derived OS in the presence of PAni and rGO to advance the development of high-performance supercapacitors.
| S-EPMC10857362 | biostudies-literature
Project description:An activated carbon (AC) electrode-based capacitor soft-pack was incorporated into a gas bag, and the gases, if produced during the charge and discharge of the capacitor, can be online analyzed by Gas chromatography. This method is effective to test the stability of capacitors using PC-based organic electrolytes up to 4 V. The kinetics of gas production was obtained and the components of the gases were analyzed quantitatively. Salts in the organic electrolyte were firstly decomposed, rather than the solvent, under the conditions of less water and AC with few functional groups. It provided new insight into understanding the stability of capacitors in high potential.
| S-EPMC9086215 | biostudies-literature
Project description:Activated carbon granules present in our household filters used in water purification are significant waste. Activated carbon waste (ACW) was ground to a fine powder, then impregnation of SnO2 on ACW was performed under mild conditions followed by calcination of SnO2-ACW at 700 °C for 2 h, producing a SnO2-ACW hybrid composite. This hybrid composite material was used in the preparation of electrodes for supercapacitor and capacitive deionization applications. The electrochemical performance of the electrodes was investigated by using cyclic voltammetry, galvanostatic charge-discharge, and electrochemical impedance spectroscopy. Calcination and addition of SnO2 contributed to an obtained electrode with a high specific capacitance of 30.46 F g-1 in a solution of 1 M Na2SO4 compared to the original ACW (0.122 F g-1) and calcined-ACW (1.42 F g-1) at an actual current of 1 mA. This electrode was also investigated for water desalination through the capacitive deionization technique and exhibited an electrosorption capacity of 6.44 mg/g compared to the commercial AC (8.9 mg/g) so it is a highly promising and economic electrode.
| S-EPMC9202029 | biostudies-literature