ABSTRACT: This study focuses on the development of adsorptive materials to retain degraded 5w40 motor oil. The materials were prepared using xanthan (XG) and XG esterified with acrylic acid (XGAC) as the polymeric matrix. LignoBoost lignin (LB), LB esterified with oleic (LBOL), stearic acid (LBST) and montmorillonite (CL) were added into XG and XGAC matrices to obtain the adsorbents. Adsorption experiments revealed that XG/CL/LBOL had the highest adsorption capacity at 46.80 g/g, followed by XGAC/CL at 45.73 g/g, and XG/CL at 37.58 g/g. The kinetic studies, employing the pseudo-second-order (PSO) model, indicated rapid sorption rates with a good correlation to experimental data. FTIR spectra analysis have evidenced the physical nature of adsorption process, involving interactions such as hydrogen bonding, van der Waals forces, and π-π interactions. Equilibrium data fitting to the Henry, Freundlich, and Temkin isotherm models showed that the adsorption occurs within materials diverse pore structures, enhancing oil retention. Structural parameters like density, porosity, and surface area were pivotal, with XG/CL/LBOL showing the most favorable properties for high oil adsorption. Additionally, it was found that the adsorption efficiency was influenced by the material's morphology and the presence of chemical modifications. This comprehensive evaluation highlights the potential of these novel adsorptive materials for environmental remediation applications, offering an efficient and sustainable approach to reducing degraded motor oil pollution.

SUBMITTER: Apostol I

PROVIDER: S-EPMC11314923 | biostudies-literature | 2024 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

A Green Approach to Oil Spill Mitigation: New Hybrid Materials for Wastewater Treatment.

Apostol Irina I Dinu Maria Valentina MV Anghel Narcis N Spiridon Iuliana I

Polymers 20240805 15

This study focuses on the development of adsorptive materials to retain degraded 5w40 motor oil. The materials were prepared using xanthan (XG) and XG esterified with acrylic acid (XGAC) as the polymeric matrix. LignoBoost lignin (LB), LB esterified with oleic (LBOL), stearic acid (LBST) and montmorillonite (CL) were added into XG and XGAC matrices to obtain the adsorbents. Adsorption experiments revealed that XG/CL/LBOL had the highest adsorption capacity at 46.80 g/g, followed by XGAC/CL at 45 ...[more]

PMID: 39125252

Similar Datasets

Project description:The presence of metal with microwave irradiation has always invited controversial arguments as the metal will catch on fire easily. But interestingly, researchers found that arc discharge phenomena provide a promising way for molecule cracking to synthesize nanomaterials. This study developed a single-step yet affordable synthesis approach that combines microwave heating and arcing in transforming crude palm oil into magnetic nanocarbon (MNC), which can be considered a new alternative for the palm oil sectors. It involves synthesizing the medium at a partial inert condition with constant coiled stainless steel metal wire (dielectric media) and ferrocene (catalyst). This approach successfully demonstrates heating at a temperature ranging from 190.9 to 472.0 °C with different synthesis times (10-20 min). The produced MNC shows formations of spheres with average sizes of 20.38-31.04 nm, mesoporous structure (SBET: 14.83-151.95 m2/g), and high content of fixed carbon (52.79-71.24wt%), and the ratio of the D and G bands (ID/IG) is 0.98-0.99. The formation of new peaks in the FTIR spectra (522.29-588.48 cm-1) supports the appearance of the FeO compounds from the ferrocene. The magnetometer shows high magnetization saturation (22.32-26.84 emu/g) in ferromagnetic materials. The application of the MNC in wastewater treatment has been demonstrated by evaluating their adsorbent capability with Methylene Blue (MB) adsorption test at a different concentrations varying between 5 and 20 ppm. The MNC produced at synthesis time (20 min) shows the highest adsorption efficiency (10.36 mg/g) compared to others, with 87.79% removal of MB dye. As a result, the value for Langmuir is not promising compared to Freundlich, with R2 being around 0.80, 0.98, and 0.99 for MNC synthesized at 10 min (MNC10), 15 min (MNC15), and 20 min (MNC20), respectively. Hence, the adsorption system is in a heterogeneous condition. The microwave-assisted arcing thereby presents a promising approach to transforming CPO into MNC that could remove the hazardous dye.

Dataset Information

A Green Approach to Oil Spill Mitigation: New Hybrid Materials for Wastewater Treatment.

Publications

A Green Approach to Oil Spill Mitigation: New Hybrid Materials for Wastewater Treatment.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets