Differences in Nanoplastic Formation Behavior Between High-Density Polyethylene and Low-Density Polyethylene.

ABSTRACT: High-Density Polyethylene (HDPE) and Low-Density Polyethylene (LDPE) films were used to create nanoplastic (NP) models, with the shape of delamination occurring during degradation. In the case of HDPE, selective degradation occurred not only in the amorphous part, but also in the crystalline part at the same time. Some of the lamellae that extend radially to form the spherulite structure were missing during the 30-day degradation. The length of these defects was less than 1 µm. HDPE disintegrated within units of spherulite structure by conformational defects in lamellae, and the size of the fragments obtained had a wide distribution. LDPE was synthesized by radical polymerization, so it contained a cross-linked part. The part was not sufficiently fused, and when it degraded, it delaminated