Mitigating Silicon Amorphization in Si-Gr Anodes: A Pathway to Stable, High-Energy Density Anodes for Li-Ion Batteries.

ABSTRACT: Silicon-Graphite (SiGr) blended anodes represent a promising approach for enhancing the energy density of commercial Li-ion batteries (LIBs). However, the ≈300% volume change of the silicon component during lithiation and delithiation induces significant mechanical stress, leading to particle cracking and pulverization that compromise electrode stability. This study presents the first evidence of controlled Si lithiation in Si-rich blended anodes, where a crystalline silicon (c-Si) core remains unreacted while the outer shell undergoes complete amorphization. Operando synchrotron X-ray diffraction analysis of SiGr anodes over five consecutive cycles reveals a reversible lithiation of c-Si, which was not previously reported. Complementary transmission electron microscopy (TEM) analysis of f