Titania-Based Oxide Catalysts for Removing Nitrogen Oxides.

ABSTRACT: Titania catalysts containing cerium, copper, or iron were obtained using the sol-gel method and tested in the selective reduction of nitrogen oxide. Samples with cerium and iron showed high activity at temperatures ranging from 200 to 400 °C, without the formation of N₂O. The materials crystallized in anatase structure, and only a small amount of ceria was detected by XRD. Their crystallites were nanometric in size. The solids were mesoporous, with a specific surface area between 74 and 160 m²/g, determined based on nitrogen sorption at low temperature. The optimum Ce/Ti and Fe/Ti atomic ratio was 0.1 to 0.9, and such catalysts were composed of small anatase crystallites, although the presence of ceria also resulted in high catalytic activity. This activity was due to