Synthesis of macroporous polystyrene by the polymerization of foamed emulsions.
Ontology highlight
ABSTRACT:
SUBMITTER: Schuler F
PROVIDER: S-EPMC3415665 | biostudies-literature | 2012 Feb
REPOSITORIES: biostudies-literature
Publications
Synthesis of macroporous polystyrene by the polymerization of foamed emulsions.
Schüler Fabian F Schamel Debora D Salonen Anniina A Drenckhan Wiebke W Gilchrist Michael D MD Stubenrauch Cosima C
Angewandte Chemie (International ed. in English) 20120120 9
Similar Datasets
Project description:Emulsion and foam templating allow the synthesis of tailor-made polymer foams. A complementary templating route is foamed emulsion templating. The concept is based on the generation of a monomer-in-water emulsion which is subsequently foamed. After polymerization of the foamed emulsion, one obtains open-cell polymer foams with porous pore walls. In the paper at hand, we generated foamed emulsions and synthesized polymer foams which are based on the monomer 1,4-butanediol dimethacrylate (1,4-BDDMA). The main challenge was to find the optimal composition of the emulsion by varying the components systematically. We will discuss that the composition of the monomer-in-water emulsion is key for the stability of the foamed emulsion and thus for the structure of the resulting polymer foam. The final composition of the continuous phase was found to be 65 vol% 1,4-BDDMA, 30 vol% water and 5 vol% glycerol. We foamed and polymerized this emulsion to check the foamed emulsion's suitability as a template for solid polymer foams. We generated a foamed emulsion with a mean bubble diameter of 151 μm ± 90 μm and obtained a highly porous poly(1,4-BDDMA) foam with a pore mean diameter of 366 μm ± 91 μm. Furthermore, the polymer foam has a "sub-porosity" within the pore walls.
| S-EPMC9050018 | biostudies-literature
Project description:Hydrophobic microporous polystyrene (PS) fibers are fabricated by a solvent-induced phase-separation-assisted electrospinning method. Zinc oxide (ZnO) and silver-doped zinc oxide (Ag-ZnO) nanomaterials with variable morphologies are added to the PS fibers, to investigate the influence of multifunctional nanofiller addition on the porosity and consequent oil-adsorbing properties for different oil types. The doping of silver as well as the uniformity in particle distribution are confirmed by scanning electron microscopy and the energy-dispersive spectral analyses. The porosity of the fibers and their crystallinity effect depend on the hydrophobicity and surface properties of these microporous nanofilled fibers. Ag-ZnO, specifically in 2 wt %, enhanced the pore size and distribution in PS porous fibers, thereby enhancing the oil-adsorbing property and its hydrophobicity. In-depth analysis of the oil adsorption mechanism is done for the fibers, both qualitatively and quantitatively, to demonstrate its correlation with the structural integrity of the fibers. The PS/2Ag-ZnO composite also exhibits the highest antibacterial performance against Staphylococcus aureus, a general indication of antibiological fouling properties of these oil-separating films. The antifouling/antibacterial activity of the nanoparticles and high oil sorption capacity of the highly porous PS composites show great potential for use in water-treatment-related applications.
| S-EPMC8014922 | biostudies-literature
Project description:In this work, we report a nonaqueous one-step method to synthesize polystyrene macroporous magnetic nanocomposites through high internal phase emulsions (HIPEs) formulated with the deep eutectic solvent (DES) composed of urea:choline chloride (U:ChCl, in a 2:1 molar ratio) as the internal phase and co-stabilized with mixtures of Span 60 surfactant and non-functionalized magnetite nanoparticles (Fe3O4 NPs). The porous structure and the magnetic and lipophilic properties of the nanocomposite materials were easily tailored by varying the amount of Fe3O4 NPs (0, 2, 5 and 10 wt %) and the surfactant Span 60 (0, 5, 10, and 20 wt %) used in the precursor emulsion. The resultant nanocomposite polyHIPEs exhibit high sorption capacity toward different oils (hexane, gasoline, and vegetable oil) due to their high porosity, interconnectivity, and hydrophobic surface. It was observed that the oil sorption capacity was improved when the amount of surfactant decreased and Fe3O4 NPs increased in HIPE formulation. Therefore, polyHIPE formulated with 5 and 10 wt % Span 60 and Fe3O4 NPs, respectively, showed the highest oil sorption capacities of 4.151, 3.556, and 3.266 g g-1 for gasoline, hexane, and vegetable oil, respectively. In addition, the magnetic monoliths were reused for more than ten sorption/desorption cycles without losing their oil sorption capacity.
| S-EPMC9245104 | biostudies-literature
Project description:Colloidal polystyrene (PS) latex particles in water can undergo interesting charge reversal in the presence of particular electrolytes. It is worth exploring the effect of charge reversal on the properties of Pickering emulsions they stabilize. Herein, emulsions stabilized by PS latex particles possessing different surface groups (sulfate, amidine, or carboxyl) were prepared in the presence of tetrapentylammonium bromide (TPeAB) or sodium thiocyanate (NaSCN) electrolytes. The effect of salt concentration on the charge of the particles and their colloid stability was measured. Emulsions were prepared from aqueous dispersions, and their type and stability were determined. The three-phase contact angle of particles at the planar oil-water interface was also measured using a gel trapping technique. It was found that the type of emulsion stabilized by latex particles is dominated by the hydrophobic PS portion on particle surfaces, although their surface charge is strongly affected by electrolyte addition. Preferred emulsions were always water-in-oil with dodecane, and charge reversal had little influence on the emulsion type and stability. However, transitional phase inversion of emulsions stabilized by carboxyl latex particles occurred on adding salt when the oil was a low-viscosity polydimethylsiloxane.
| S-EPMC9171833 | biostudies-literature
Project description:In this work, we present a novel synthetic route to diblock copolymers based on styrene and 3-vinylpyridine monomers. Surfactant-free water-based reversible addition-fragmentation chain transfer (RAFT) emulsion polymerization of styrene in the presence of the macroRAFT agent poly(3-vinylpyridine) (P3VP) is used to synthesize diblock copolymers with molecular weights of around 60 kDa. The proposed mechanism for the poly(3-vinylpyridine)-block-poly(styrene) (P3VP-b-PS) synthesis is the polymerization-induced self-assembly (PISA) which involves the in situ formation of well-defined micellar nanoscale objects consisting of a PS core and a stabilizing P3VP macroRAFT agent corona. The presented approach shows a well-controlled RAFT polymerization, allowing for the synthesis of diblock copolymers with high monomer conversion. The obtained diblock copolymers display microphase-separated structures according to their composition.
| S-EPMC6803976 | biostudies-literature
Project description:High internal phase emulsion (HIPE) templating is a well-established method for the generation of polymeric materials with high porosity (>74%) and degree of interconnectivity. The porosity and pore size can be altered by adjusting parameters during emulsification, which affects the properties of the resulting porous structure. However, there remain challenges for the fabrication of polyHIPEs, including typically small pore sizes (∼20-50 μm) and the use of surfactants, which can limit their use in biological applications. Here, we present the use of gelatin, a natural polymer, during the formation of polyHIPE structures, through the use of two biodegradable polymers, polycaprolactone-methacrylate (PCL-M) and polyglycerol sebacate-methacrylate (PGS-M). When gelatin is used as the internal phase, it is capable of stabilising emulsions without the need for an additional surfactant. Furthermore, by changing the concentration of gelatin within the internal phase, the pore size of the resulting polyHIPE can be tuned. 5% gelatin solution resulted in the largest mean pore size, increasing from 53 μm to 80 μm and 28 μm to 94 µm for PCL-M and PGS-M respectively. In addition, the inclusion of gelatin further increased the mechanical properties of the polyHIPEs and increased the period an emulsion could be stored before polymerisation. Our results demonstrate the potential to use gelatin for the fabrication of surfactant-free polyHIPEs with macroporous structures, with potential applications in tissue engineering, environmental and agricultural industries.
| S-EPMC10481965 | biostudies-literature
Project description:High Internal Phase Emulsions (HIPEs) of dicyclopentadiene (DCPD) were prepared using mixtures of surface-modified calcite (mCalcite) and a non-ionic surfactant. Twelve different emulsion formulations were created using an experimental design methodology. Three distinctive levels of the internal phase ratio, the amount of mCalcite loading, and the surfactant were used to prepare the HIPEs. Accordingly, macroporous polyDCPD composites were synthesized by performing ring-opening metathesis polymerization (ROMP) on the HIPEs. The variations in the morphological and physical properties of the composites were investigated in terms of experimental parameters. In the end, five different model equations were derived with a confidence level of 95%. The main and binary interaction effects of the experimental parameters on the responses, such as the average cavity size, interconnecting pore size, specific surface area, foam density, and compression modulus, were demonstrated. The synergistic interaction between the amount of surfactant, the amount of mCalcite loading, and the internal phase ratio appeared to have a dominant role in the average cavity diameter. The solo effect of the internal phase ratio on the interconnecting pore size, foam density, and compression modulus was confirmed. In addition, it was demonstrated that the specific surface area of the composites was mainly changed depending on the amount of mCalcite loading.
| S-EPMC9824432 | biostudies-literature
Project description:The combination of polymerization-induced self-assembly (PISA) and reversible-addition fragmentation chain transfer (RAFT) emulsion polymerization offers a powerful technique to synthesize diblock copolymers and polymeric nanoparticles in a controlled manner. The RAFT emulsion diblock copolymerization of styrene and methacrylic acid (MAA) by using a trithiocarbonate as surfactant and RAFT agent was investigated. The Z-group of the RAFT agent was modified with a propyl-, butyl- and dodecyl- sidechain, increasing the hydrophobicity of the RAFT agent to offer well-controlled polymerization of poly(methacrylic acid)-block-polystyrene (PMAA-b-PS) diblock copolymers at high solid contents between 30-50 wt% in water. The kinetic data of the PMAA homopolymerization with the three different RAFT agents for various solvents was investigated as well as the RAFT emulsion polymerization of the diblock copolymers in pure water. While the polymerization of PMAA-b-PS with a propyl terminus as a Z-group suffered from slow polymerization rates at solid contents above 30 wt%, the polymerization with a dodecyl sidechain as a Z-group led to full conversion within 2 h, narrow molar mass distributions and all that at a remarkable solid content of up to 50 wt%.
| S-EPMC8588034 | biostudies-literature
Project description:Phosphonate-functionalized polymer nanoparticles were synthesized by free-radical copolymerization of vinylphosphonic acid (VPA) with styrene or methyl methacrylate (MMA) using the miniemulsion technique. The influence of different parameters such as monomer and surfactant type, amount of vinylphosphonic acid on the average particle size, and size distribution was studied using dynamic light scattering and transmission electron microscopy. Depending on the amount and type of the surfactant used (ionic or non-ionic), phosphonate-functionalized particles in a size range from 102 to 312 nm can be obtained. The density of the phosphonate groups on the particle surface was higher in the case of using MMA as a basis monomer than polystyrene. The kinetic behavior of VPA copolymerization with styrene or MMA using a hydrophobic initiator was investigated by reaction calorimetry. Different kinetic curves were observed for miniemulsion (co)polymerization of styrene- and MMA-based nanoparticles indicating different nucleation mechanisms.
| S-EPMC2763176 | biostudies-other
Project description:Multifunctionality and effectiveness of macroporous solid foams in extreme environments have captivated the attention of both academia and industries. The most recent rapid, energy-efficient strategy to manufacture solid foams with directionality is the frontal polymerization (FP) of dicyclopentadiene (DCPD). However, there still remains the need for a time efficient one-pot approach to induce anisotropic macroporosity in DCPD foams. Here we show a rapid production of cellular solids by frontally polymerizing a mixture of DCPD monomer and allyl-functionalized cellulose nanocrystals (ACs). Our results demonstrate a clear correlation between increasing % allylation and AC wt%, and the formed pore architectures. Especially, we show enhanced front velocity (vf) and reduced reaction initiation time (tinit) by introducing an optimal amount of 2 wt% AC. Conclusively, the small- and wide-angle X-ray scattering (SAXS, WAXS) analyses reveal that the incorporation of 2 wt% AC affects the crystal structure of FP-mediated DCPD/AC foams and enhances their oxidation resistance. Polymeric solid foams have several beneficial properties such as their light weight, thermal insulation or shock absorbance, but it is still challenging to efficiently control the foam architecture. Here, the authors optimize the frontal polymerization of dicyclopentadiene with allyl-functionalized cellulose nanocrystals to rapidly achieve solid foams with modified structures and enhanced oxidation resistance.
| S-EPMC9814902 | biostudies-literature