Novel ultra-low temperature co-fired microwave dielectric ceramic at 400 degrees and its chemical compatibility with base metal.

ABSTRACT: A novel NaAgMoO4 material with spinel-like structure was synthesized by using the solid state reaction method and the ceramic sample was well densified at an extreme low sintering temperature about 400°C. Rietveld refinement of the crystal structure was performed using FULLPROF program and the cell parameters are a = b = c = 9.22039 Å with a space group F D -3 M (227). High performance microwave dielectric properties, with a permittivity ~7.9, a Qf value ~33,000 GHz and a temperature coefficient of resonant frequency ~-120 ppm/°C, were obtained. From X-ray diffraction (XRD) and Energy Dispersive Spectrometer (EDS) analysis of the co-fired sample, it was found that the NaAgMoO4 ceramic is chemically compatible with both silver and aluminum at the sintering temperature and this makes it a pr