Defect visualization of Cu(InGa)(SeS)2 thin films using DLTS measurement.

ABSTRACT: Defect depth profiles of Cu (In1-x,Gax)(Se1-ySy)2 (CIGSS) were measured as functions of pulse width and voltage via deep-level transient spectroscopy (DLTS). Four defects were observed, i.e., electron traps of ~0.2 eV at 140 K (E1 trap) and 0.47 eV at 300 K (E2 trap) and hole traps of ~0.1 eV at 100 K (H1 trap) and ~0.4 eV at 250 K (H2 trap). The open circuit voltage (VOC) deteriorated when the trap densities of E2 were increased. The energy band diagrams of CIGSS were also obtained using Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS), and DLTS data. These results showed that the valence band was lowered at higher S content. In addition, it was found that the E2 defect influenced the VOC and could be interpreted as an extended defect. Defect depth profile images