Characteristics of Carbon Material Formation on SBA-15 and Ni-SBA-15 Templates by Acetylene Decomposition and Their Bioactivity Effects.

ABSTRACT: Carbon spheres and tubes were formed from acetylene decomposition on SBA-15 and Ni-SBA-15 at 650-850 °C. At 650 °C, the decomposed carbons covered the surface of the support, and no carbon spheres and filament materials were formed. Carbon sphere formation occurred at 750 °C-850 °C; with diameters ranging from 0.8 μm-1.1 μm. For Ni-SBA-15, the diameters of the spheres and filaments were 0.8 μm and 62 nm, respectively, at 650 °C. At 750 °C, the diameter of the ball carbon materials ranged from 0.7 μm-0.8 μm, the diameter of the carbon tubes formed was 120-130 nm, and their pore diameter was 8.0 nm-11 nm. At 850 °C, the diameters of ball carbon materials and carbon tubes were similar to those of the materials at the formation temperature, 750 °C. Si, O and C were the main constituents of SBA