Silver-modified octahedral anatase particles as plasmonic photocatalyst.

ABSTRACT: Octahedral anatase particles (OAPs) were modified with silver nanoparticles (NPs) by photodeposition method. The properties of OAPs influenced the properties of silver deposits, and thus the photocatalytic activity of the obtained silver-modified OAPs. Photocatalytic activities were tested under UV and vis irradiation for oxidative decomposition of acetic acid and oxidation of 2-propanol, respectively. The properties of silver-modified OAPs were investigated by XRD, STEM, DRS, XPS and time-resolved microwave conductivity (TRMC) method. It was found that electron traps (ETs) worked as nucleation sites for silver, resulting in formation of smaller silver NPs on smaller OAPs with larger content of ETs. The modification with silver resulted in enhanced photocatalytic activity under both UV and vis irradiation. It was found that larger crystallite size of silver NPs, and thus larger polydispersity of silver deposits resulted in broad and intense plasmon resonance peak causing enhanced visible activity. The correlation between photocatalytic activity and TRMC data, e.g., slower decay of TRMC signal for more active samples, allowed discussion on property-governed photocatalytic activities of silver-modified titania.

SUBMITTER: Wei Z

PROVIDER: S-EPMC5946688 | biostudies-literature | 2018 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Silver-modified octahedral anatase particles as plasmonic photocatalyst.

Wei Z Z Janczarek M M Endo M M Colbeau-Justin C C Ohtani B B Kowalska E E

Catalysis today 20180701

Octahedral anatase particles (OAPs) were modified with silver nanoparticles (NPs) by photodeposition method. The properties of OAPs influenced the properties of silver deposits, and thus the photocatalytic activity of the obtained silver-modified OAPs. Photocatalytic activities were tested under UV and vis irradiation for oxidative decomposition of acetic acid and oxidation of 2-propanol, respectively. The properties of silver-modified OAPs were investigated by XRD, STEM, DRS, XPS and time-resol ...[more]

PMID: 30018465

Similar Datasets

Project description:Octahedral anatase particles (OAPs), prepared by ultrasonication-hydrothermal reaction (US-HT), were modified with 2 wt% of gold by photodeposition. Conditions of US-HT process such as durations of US and durations of HT were varied to obtain OAPs products different by physicochemical and morphological properties. Au/OAPs samples were characterized by X-ray diffraction (XRD), scanning transmission electron microscopy (STEM), X-ray photoelectron spectroscopy (XPS) and diffuse reflectance spectroscopy (DRS). The photocatalytic activity was tested under UV irradiation for decomposition of acetic acid (CO2 system) and dehydrogenation of methanol (H2 system) under aerobic and anaerobic conditions, respectively, and for oxidation of 2-propanol under visible light irradiation. Photodeposition of gold was very fast for all OAPs samples (0.5-10 min) under Ar atmosphere, and the clear correlation between the content of electron traps (ETs) and the induction period, during which nanoparticles (NPs) of gold are formed, indicates that ETs in titania samples are a key-factor for rapidity of gold photodeposition on titania surface. It was found that better morphology of titania (larger content of faceted particles) resulted in formation of larger gold NPs, while small gold NPs were deposited on structural defects. Modification of OAPs with gold NPs resulted in significant enhancement of photocatalytic activity, being e.g., 1.5 (CO2 system), 7.7 (H2 system), and even more than 40 under vis irradiation. It was found that both the properties of titania and gold are crucial for resultant photocatalytic activity, but a direct correlation between one structural/physical property and photocatalytic activity could not be obtained since all structural properties changed simultaneously when conditions of photocatalyst preparation (US-HT) were changed. Therefore, gold NPs of controlled sizes were deposited on OAPs product with the best morphology by modified photodeposition method. Clear correlation between photocatalytic activity under visible light and the size of gold NPs indicates that gold properties are decisive for visible light activity rather than titania properties. 3D-FDTD simulations confirm that an increase in the size of gold NPs results in extended surface areas with field enhancement.

Project description:Octahedral anatase particles (OAP) with eight exposed and thermodynamically most stable (101) facets were prepared by an ultrasonication-hydrothermal (US-HT) reaction from potassium titanate nanowires (TNW). The precursor (TNW) and the product (OAP) of US-HT reaction were modified with nanoparticles of noble metals (Au, Ag or Pt) by photodeposition. Samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), diffuse reflectance spectroscopy (DRS), scanning transmission electron microscopy (STEM) and time-resolved microwave conductivity (TRMC). The photocatalytic activity was investigated in three reaction systems, i.e., anaerobic dehydrogenation of methanol and oxidative decomposition of acetic acid under UV/vis irradiation, and oxidation of 2-propanol under vis irradiation. It was found that hydrogen liberation correlated with work function of metals, and thus the most active were platinum-modified samples. Photocatalytic activities of bare and modified OAP samples were much higher than those of TNW samples, probably due to anatase presence, higher crystallinity and electron mobility in faceted NPs. Interestingly, noble metals showed different influence on the activity depending on the semiconductor support, i.e., gold-modified TNW and platinum-modified OAP exhibited the highest activity for acetic acid decomposition, whereas silver- and gold-modified samples were the most active under vis irradiation, respectively. It is proposed that the form of noble metal (metallic vs. oxidized) as well as the morphology (well-organized vs. uncontrolled) have a critical effect on the overall photocatalytic performance. TRMC analysis confirmed that fast electron transfer to noble metal is a key factor for UV activity. It is proposed that the efficiency of plasmonic photocatalysis (under vis irradiation) depends on the oxidation form of metal (zero-valent preferable), photoabsorption properties (broad localized surface plasmon resonance (LSPR)), kind of metal (silver) and counteraction of "hot" electrons back transfer to noble metal NPs (by controlled morphology and high crystallinity).

Project description:Flavivirus envelope (E) and precursor M (prM) proteins, when ectopically expressed, assemble into empty, virus-like particles (VLPs). Cleavage of prM to M and loss of the pr fragment converts the VLPs from immature to mature particles, mimicking a similar maturation of authentic virions. Most of the VLPs obtained by prM-E expression are smaller than virions; early, low-resolution cryo-EM studies suggested a simple, 60-subunit, icosahedral organization. We describe here the cryo-EM structure of immature, small VLPs (smVLPs) from dengue virus type 2 and show that they have octahedral rather than icosahedral symmetry. The asymmetric unit of the octahedral particle is an asymmetric trimer of prM-E heterodimers, just as it is on icosahedral immature virions; the full, octahedrally symmetric particle thus has 24 such asymmetric trimers or 72 prM-E heterodimers in all. Cleavage of prM and release of pr generates ovoid, somewhat irregular, mature particles. Previous work has shown that mature smVLPs have fusion properties identical to those of virions, consistent with local, virion-like clustering of 36 E dimers on their surface. The cryo-EM structure and the properties of the smVLPs described here relate directly to ongoing efforts to use them as vaccine immunogens.ImportanceEctopic expression of flavivirus envelope (E) and precursor M (prM) proteins leads to the formation and secretion of empty, virus-like particles (VLPs). We show that a major class of VLPs, of smaller diameter than those of virion size ("small VLPs": smVLPs), are octahedrally symmetric particles. The known characteristics of immature virions (asymmetric trimers of prM-E heterodimers) allow us to understand the assembly of an octahedral (rather than icosahedral) surface lattice. Cleavage of prM and formation of mature, fusogenic smVLPs yield somewhat irregular, ovoid particles. These observations are directly relevant to proposals for using immunogenic but non-infectious VLPs as components of specific flavivirus vaccines.

Dataset Information

Silver-modified octahedral anatase particles as plasmonic photocatalyst.

Publications

Silver-modified octahedral anatase particles as plasmonic photocatalyst.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets