Evaluation of Residual Stress Distribution and Relaxation on In Situ TiB₂/7050 Al Composites.

ABSTRACT: Interior residual stresses induced by quenching may cause distortion during subsequent machining processes. Hence, various strategies have been employed to relieve the interior residual stress, such as stretching, post treatment, and other techniques. In this study, the stress distribution inside TiB₂/7050 Al composite extrusions was investigated and the effects of different methods on relieving the quenching-induced stress were compared. Firstly, three TiB₂/7050 Al composite extrusions were treated by stretching, stretching and heat treatment, and stretching and cold treatment processes, respectively. Then, the multiple-cut contour method was employed to assess the residual stresses in the three workpieces. Experimental results indicate that the interior stress of TiB₂/7050 Al composite extrusions after stretching ranges from −89 MPa to +55 MPa, which is larger than that in 7050 aluminum alloy, which ranges from −25 Pa to +25 MPa. The heat treatment performs better than the cold treatment to reduce the post-stretching residual stress, with a reduction of 23.2⁻46.4% compared to 11.3⁻40.8%, respectively. From the stress map, it is found that the stress distribution after the heat treatment is more uniform compared with that after the cold treatment.

SUBMITTER: Lin K

PROVIDER: S-EPMC5978083 | biostudies-literature | 2018 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Evaluation of Residual Stress Distribution and Relaxation on In Situ TiB₂/7050 Al Composites.

Lin Kunyang K Wang Wenhu W Jiang Ruisong R Xiong Yifeng Y Zhao Dezhong D

Materials (Basel, Switzerland) 20180430 5

Interior residual stresses induced by quenching may cause distortion during subsequent machining processes. Hence, various strategies have been employed to relieve the interior residual stress, such as stretching, post treatment, and other techniques. In this study, the stress distribution inside TiB₂/7050 Al composite extrusions was investigated and the effects of different methods on relieving the quenching-induced stress were compared. Firstly, three TiB₂/7050 Al composite extrusions were tre ...[more]

PMID: 29710845

Similar Datasets

Project description:We use optical tweezers microrheology and fluorescence microscopy to characterize the nonlinear mesoscale mechanics and mobility of in vitro co-entangled actin-microtubule composites. We create a suite of randomly oriented, well-mixed networks of actin and microtubules by co-polymerizing varying ratios of actin and tubulin in situ. To perturb each composite far from equilibrium, we use optical tweezers to displace an embedded microsphere a distance greater than the lengths of the filaments at a speed much faster than their intrinsic relaxation rates. We simultaneously measure the force the filaments exert on the bead and the subsequent force relaxation. We find that the presence of a large fraction of microtubules (>0.7) is needed to substantially increase the measured force, which is accompanied by large heterogeneities in force response. Actin minimizes these heterogeneities by reducing the mesh size of the composites and supporting microtubules against buckling. Composites also undergo a sharp transition from strain softening to stiffening when the fraction of microtubules (ϕT) exceeds 0.5, which we show arises from faster poroelastic relaxation and suppressed actin bending fluctuations. The force after bead displacement relaxes via power-law decay after an initial period of minimal relaxation. The short-time relaxation profiles (t < 0.06 s) arise from poroelastic and bending contributions, whereas the long-time power-law relaxation is indicative of filaments reptating out of deformed entanglement constraints. The scaling exponents for the long-time relaxation exhibit a nonmonotonic dependence on ϕT, reaching a maximum for equimolar composites (ϕT = 0.5), suggesting that reptation is fastest in ϕT = 0.5 composites. Corresponding mobility measurements of steady-state actin and microtubules show that both filaments are indeed the most mobile in ϕT = 0.5 composites. This nonmonotonic dependence of mobility on ϕT demonstrates the important interplay between mesh size and filament rigidity in polymer networks and highlights the surprising emergent properties that can arise in composites.

Dataset Information

Evaluation of Residual Stress Distribution and Relaxation on In Situ TiB₂/7050 Al Composites.

Publications

Evaluation of Residual Stress Distribution and Relaxation on In Situ TiB₂/7050 Al Composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets