Microfluidic spinning of the fibrous alginate scaffolds for modulation of the degradation profile.

ABSTRACT: In tissue engineering, alginate has been an attractive material due to its biocompatibility and ability to form hydrogels, unless its uncontrollable degradation could be an undesirable feature. Here, we developed a simple and easy method to tune the degradation profile of the fibrous alginate scaffolds by the microfluidic wet spinning techniques, according with the use of isopropyl alcohol for dense packing of alginate chains in the microfiber production and the increase of crosslinking with Ca²⁺ ion. The degradation profiling was analyzed by mass losses, swelling ratios, and also observation of the morphologic changes. The results demonstrated that high packing density might be provided by self-aggregation of polymer chains through high dipole interactions between sheath and core fluids and that the increase of crosslinking rates could make degradation of alginate scaffold controllable. We suggest that the tunable degradation of the alginate fibrous scaffolds may expand its utilities for biomedical applications such as drug delivery, in vitro cell culture, wound healing, tissue engineering and regenerative medicine.

Electronic supplementary material

Supplementary material is available for this article at 10.1007/s13770-016-9048-7 and is accessible for authorized users.

SUBMITTER: Mun CH

PROVIDER: S-EPMC6170856 | biostudies-literature | 2016 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Microfluidic spinning of the fibrous alginate scaffolds for modulation of the degradation profile.

Mun Cho Hay CH Hwang Ji-Young JY Lee Sang-Hoon SH

Tissue engineering and regenerative medicine 20160405 2

In tissue engineering, alginate has been an attractive material due to its biocompatibility and ability to form hydrogels, unless its uncontrollable degradation could be an undesirable feature. Here, we developed a simple and easy method to tune the degradation profile of the fibrous alginate scaffolds by the microfluidic wet spinning techniques, according with the use of isopropyl alcohol for dense packing of alginate chains in the microfiber production and the increase of crosslinking with Ca< ...[more]

PMID: 30603393

Similar Datasets

Project description:Fabrication of micro- and nanofibers are critical for a wide range of applications from microelectronics to biotechnology. Alginate microfibers with diameters of tens to hundreds of microns play an important role in tissue engineering and fibers of these diameters are impossible to fabricate via electrospinning and can only be produced via fluidic spinning. Typically, microfluidic spinning based on photopolymerization produces fibers that are not easily dissolvable, while fluidic spinning with chemical cross-linking employs complex setups of microfabricated chips or coaxial needles, aimed at precise control of the fiber diameter; however, fluidic spinning introduces significant cost and complexity to the microfluidic setup. We demonstrate immersed microfluidic spinning where a calcium alginate microfiber is produced via displacement of alginate solution through a single needle that is immersed in a cross-linking bath of calcium chloride solution. The resulting diameter of the fiber is characterized and the fiber diameter and topology of the deposited fiber is related to the concentration of the alginate solution (2 wt%, 4 wt%, and 6 wt%), needle gauge (30 g, 25 g, and 20 g), and the volumetric flow rate of the alginate solution (1 mL/min, 2 mL/min, and 2.7 mL/min). The resulting fiber diameter is smaller than the internal diameter of the needle and this dependence is explained by the continuity of the flow and increased rate of fall of the liquid jet upon its issuing from the needle. The fiber diameter (demonstrated diameter of fibers range from 100 microns to 1 mm) depends weakly on the volumetric flow rate and depends strongly on the needle diameter. It also seems that for a smaller needle size, a greater concentration of alginate results in smaller diameter fibers and that this trend is not evident as the needle diameter is increased. In terms of topology of the deposited fiber, the higher wt% alginate fiber produces larger loops, while smaller wt% alginate solution yields a denser topology of the overlaid fiber loops. These fibers can be dissolved in DMEM/EDTA/DSC solution in 20-30 min (depending on the fiber diameter), leaving behind the hollow channels in the hydrogel matrix. We believe that the demonstrated simple setup of the immersed microfluidic spinning of the calcium alginate microfibers will be useful for creating tissue constructs, including the vascularized tissue implants.

Dataset Information

Microfluidic spinning of the fibrous alginate scaffolds for modulation of the degradation profile.

Electronic supplementary material

Publications

Microfluidic spinning of the fibrous alginate scaffolds for modulation of the degradation profile.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets