Key Parameters to Promote Granularization of Lath-Like Bainite/Martensite in FeNiC Alloys during Isothermal Holding.

ABSTRACT: The stability of lath-like microstructures during low-temperature isothermal ageing was analyzed in a Fe5Ni0.33C (in wt %) steel. The microstructures were characterized using Scanning Electron Microscopy (SEM) coupled with Electron Backscatter Diffraction (EBSD). Advanced orientation data processing was applied to quantify the hierarchical and multiscale organization of crystallographic variants subdividing Prior Austenite Grains (PAG) into packets/blocks/sub-blocks. The result shows that ferrite laths of martensite or lower bainite are stable, whatever the ageing temperature (up to 380 °C). On the contrary, a granularization process is triggered when microstructures contain a fraction of upper bainite. This metallurgical evolution corresponds to a rapid and significant change of the ferrite matrix involving a disappearance of 60° disoriented blocks. The phenomenon affects in turn the mechanical properties. The final microstructures obtained after isothermal holding look like granular bainite, which raises some questions about the classification of bainite.

SUBMITTER: Ben Haj Slama M

PROVIDER: S-EPMC6213765 | biostudies-literature | 2018 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Key Parameters to Promote Granularization of Lath-Like Bainite/Martensite in FeNiC Alloys during Isothermal Holding.

Ben Haj Slama Meriem M Gey Nathalie N Germain Lionel L Zhu Kangying K Allain Sébastien S

Materials (Basel, Switzerland) 20180924 10

The stability of lath-like microstructures during low-temperature isothermal ageing was analyzed in a Fe5Ni0.33C (in wt %) steel. The microstructures were characterized using Scanning Electron Microscopy (SEM) coupled with Electron Backscatter Diffraction (EBSD). Advanced orientation data processing was applied to quantify the hierarchical and multiscale organization of crystallographic variants subdividing Prior Austenite Grains (PAG) into packets/blocks/sub-blocks. The result shows that ferrit ...[more]

PMID: 30249989

Similar Datasets

Project description:Coating system(s) will be required for Nb-silicide based alloys. Alumina forming alloys that are chemically compatible with the Nb-silicide based alloy substrate could be components of such systems. The intermetallic alloys Nb1.45Si2.7Ti2.25Al3.25Hf0.35 (MG5) and Nb1.35Si2.3Ti2.3Al3.7Hf0.35 (MG6) were studied in the cast, heat treated and isothermally oxidised conditions at 800 and 1200 °C to find out if they are αAl₂O₃ scale formers. A (Al/Si)alloy versus Nb/(Ti + Hf)alloy map, which can be considered to be a map for Multi-Principle Element or Complex Concentrated Nb-Ti-Si-Al-Hf alloys, and a [Nb/(Ti + Hf)]Nb5Si3 versus [Nb/(Ti + Hf)]alloy map were constructed making use of the alloy design methodology NICE and data from a previously studied alloy, and were used to select the alloys MG5 and MG6 that were expected (i) not to pest, (ii) to form αAl₂O₃ scale at 1200 °C, (iii) to have no solid solution, (iv) to form only hexagonal Nb₅Si₃ and (v) to have microstructures consisting of hexagonal Nb₅Si₃, Ti₅Si₃, Ti₅Si₄, TiSi silicides, and tri-aluminides and Al rich TiAl. Both alloys met the requirements (i) to (v). The alumina scale was able to self-heal at 1200 °C. Liquation in the alloy MG6 at 1200 °C was linked with the formation of a eutectic like structure and the TiAl aluminide in the cast alloy. Key to the oxidation of the alloys was the formation (i) of "composite" silicide grains in which the Nb₅Si₃ core was surrounded by the Ti₅Si₄ and TiSi silicides, and (ii) of tri-aluminides with high Al/Si ratio, particularly at 1200 °C and very low Nb/Ti ratio forming in-between the "composite" silicide grains. Both alloys met the "standard definition" of high entropy alloys (HEAs). Compared with HEAs with bcc solid solution and intermetallics, the VEC values of both the alloys were outside the range of reported values. The parameters VEC,  and  of Nb-Ti-Si-Al-Hf coating alloys and non-pesting Nb-silicide based alloys were compared and trends were established. Selection of coating alloys with possible "layered" structures was discussed and alloy compositions were proposed.

Dataset Information

Key Parameters to Promote Granularization of Lath-Like Bainite/Martensite in FeNiC Alloys during Isothermal Holding.

Publications

Key Parameters to Promote Granularization of Lath-Like Bainite/Martensite in FeNiC Alloys during Isothermal Holding.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets