Grafting of Hindered Phenol Groups onto Ethylene/α-Olefin Copolymer by Nitroxide Radical Coupling.

ABSTRACT: The covalent immobilization of hindered phenol groups, with potential antioxidant activity, onto an ethylene/α-olefin (EOC) copolymer was carried out by the nitroxide radical coupling (NRC) reaction performed in the melt with a peroxide and the 3,5-di-tert-butyl-4-hydroxybenzoyl-2,2,6,6-tetramethylpiperidine-1-oxyl radical (BHB-T). Functionalized EOC (EOC-g-(BHB-T)) was exposed to photo- and thermo-oxidation. By comparison with some model compounds bearing the (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO) moiety or the hindered phenol unit, it was observed that the grafted BHB-T could effectively help the stabilization of the polymer matrix both under photo- and thermo-oxidation. In addition, the immobilization of BHB-T can effectively increase the service life of the functionalized polymers when polymer films were put in contact with ethanol solution thus simulating a possible application of the modified polymer.

SUBMITTER: Coiai S

PROVIDER: S-EPMC6418857 | biostudies-literature | 2017 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Grafting of Hindered Phenol Groups onto Ethylene/α-Olefin Copolymer by Nitroxide Radical Coupling.

Coiai Serena S Cicogna Francesca F Yang Chengcheng C Tempesti Veronika V Carroccio Sabrina Carola SC Gorrasi Giuliana G Mendichi Raniero R Dintcheva Nadka Tz NT Passaglia Elisa E

Polymers 20171204 12

The covalent immobilization of hindered phenol groups, with potential antioxidant activity, onto an ethylene/α-olefin (EOC) copolymer was carried out by the nitroxide radical coupling (NRC) reaction performed in the melt with a peroxide and the 3,5-di-<i>tert</i>-butyl-4-hydroxybenzoyl-2,2,6,6-tetramethylpiperidine-1-oxyl radical (BHB-T). Functionalized EOC (EOC-<i>g</i>-(BHB-T)) was exposed to photo- and thermo-oxidation. By comparison with some model compounds bearing the (2,2,6,6-tetramethylp ...[more]

PMID: 30965973

Similar Datasets

Project description:The ethylene/norbornene content within cyclic olefin copolymer (COC) is well known to affect the chemical and physical properties of the copolymer, such as the glass transition temperature (Tg) and transparency. However, no work has been reported evaluating the effects of the ethylene/norbornene content on the surface properties of COC following UV/O3 or O2 plasma activation. Activation with either O2 plasma or UV/O3 is often used to assist in thermal assembly of fluidic devices, increasing the wettability of the surfaces, or generating functional scaffolds for the attachment of biological elements. Thus, we investigated differences in the physiochemical surface properties of various ethylene/norbornene compositions of COC following activation using analytical techniques such as water contact angle (WCA), ATR-FTIR, XPS, TOF-SIMS, UV-VIS, AFM and a colorimetric assay utilizing Toluidine Blue O (TBO). Results showed that increased norbornene content led to the generation of more oxygen containing functionalities such as alcohols, ketones, aldehydes and carboxyl groups when activated with either UV/O3 or O2 plasma. Specifically, COC with ∼60% norbornene content showed a significantly higher -COOH functional group density when compared to COC with a 50% norbornene content and COC with a 35% norbornene content following UV/O3 or O2 plasma activation. Furthermore, COC with large norbornene contents showed a smaller average RMS roughness (0.65 nm) when compared to COC containing low norbornene contents (0.95 nm) following activation making this substrate especially suited for nanofluidic applications, which require smooth surfaces to minimize effects arising from dielectrophoretic trapping or non-specific adsorption. Although all COC substrates showed >90% transparency at wavelengths >475 nm, COC possessing high norbornene contents showed significantly less transparency at wavelengths below 475 nm following activation, making optical detection in this region difficult. Our data showed distinct physiochemical differences in activated COC that was dependent upon the ethylene/norbornene content of the thermoplastic and thus, careful selection of the particular COC grade must be considered for micro- and nanofluidics.

Dataset Information

Grafting of Hindered Phenol Groups onto Ethylene/α-Olefin Copolymer by Nitroxide Radical Coupling.

Publications

Grafting of Hindered Phenol Groups onto Ethylene/α-Olefin Copolymer by Nitroxide Radical Coupling.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets