Modification of Thermal and Mechanical Properties of PEG-PPG-PEG Copolymer (F127) with MA-POSS.

ABSTRACT: Pluronic F127 exhibits thermogelling behaviour at 20⁻30 °C via a micelle packing mechanism. Disruption of the micelle packing increases the sol-gel temperature, but results in the decrease of modulus. Herein, we reported a method to modify F127 with polyhedral oligosilsesquioxane (POSS) to impart a higher gelling temperature without yielding the property and strength of the thermogel. The thermal degradation temperature was enhanced to 15 °C after POSS incorporation and the gelling temperature shifted 10 °C higher, without sacrificing the modulus of the gel. Rheological studies supported the claim that the gel property was reinforced after POSS incorporation. F127-POSS copolymer matrix stored more energy from POSS reinforcement, which saw larger Lissajous curve areas before the collapse of the microstructure for the same amount of stress applied. These results indicated that modification with POSS would raise the sol-gel transition temperature without sacrificing the modulus of the gel.

SUBMITTER: Dou Q

PROVIDER: S-EPMC6432308 | biostudies-literature | 2016 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Modification of Thermal and Mechanical Properties of PEG-PPG-PEG Copolymer (F127) with MA-POSS.

Dou Qingqing Q Abdul Karim Anis A Loh Xian Jun XJ

Polymers 20160915 9

Pluronic F127 exhibits thermogelling behaviour at 20⁻30 °C via a micelle packing mechanism. Disruption of the micelle packing increases the sol-gel temperature, but results in the decrease of modulus. Herein, we reported a method to modify F127 with polyhedral oligosilsesquioxane (POSS) to impart a higher gelling temperature without yielding the property and strength of the thermogel. The thermal degradation temperature was enhanced to 15 °C after POSS incorporation and the gelling temperature s ...[more]

PMID: 30974616

Similar Datasets

Project description:Proton exchange membranes (PEMs) suffer performance degradation under certain conditions-temperatures greater than 80 °C, relative humidity less than 50%, and water retention less than 22%. Novel materials are needed that have improved water retention, stability at higher temperatures, flexibility, conductivity, and the ability to function at low humidity. This work focuses on polyimide-poly(ethylene glycol) (PI-PEG) segmented block copolymer (SBC) membranes with high conductivity and mechanical strength. Membranes were prepared with one of two ionic liquids (ILs), either ethylammonium nitrate (EAN) or propylammonium nitrate (PAN), incorporated within the membrane structure to enhance the proton exchange capability. Ionic liquid uptake capacities were compared for two different temperatures, 25 and 60 °C. Then, conductivities were measured for a series of combinations of undoped or doped unannealed and undoped or doped annealed membranes. Stress and strain tests were performed for unannealed and thermally annealed undoped membranes. Later, these experiments were repeated for doped unannealed and thermally annealed. Mechanical and conductivity data were interpreted in the context of prior small angle X-ray scattering (SAXS) studies on similar materials. We have shown that varying the compositions of polyimide-poly(ethylene glycol) (PI-PEG) SBCs allowed the morphology in the system to be tuned. Since polyimides (PI) are made from the condensation of dianhydrides and diamines, this was accomplished using components having different functional groups. Dianhydrides having either fluorinated or oxygenated functional groups and diamines having either fluorinated or oxygenated diamines were used as well as mixtures of these species. Changing the morphology by creating macrophase separation elevated the IL uptake capacities, and in turn, increased their conductivities by a factor of three or more compared to Nafion 115. The stiffness of the membranes synthesized in this work was comparable to Nafion 115 and, thus, sufficient for practical applications.

Dataset Information

Modification of Thermal and Mechanical Properties of PEG-PPG-PEG Copolymer (F127) with MA-POSS.

Publications

Modification of Thermal and Mechanical Properties of PEG-PPG-PEG Copolymer (F127) with MA-POSS.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets