Pyridine as an additive to improve the deposition of continuous electrospun filaments.

ABSTRACT: Electrospun filaments are leading to a new generation of medical yarns that have the ability to enhance tissue healing through their biophysical cues. We have recently developed a technology to fabricate continuous electrospun filaments by depositing the submicron fibres onto a thin wire. Here we investigate the influence of pyridine on the fibre deposition. We have added pyridine to polydioxanone solutions at concentrations ranging from 0 to 100 ppm, increasing the conductivity of the solutions almost linearly from 0.04 uS/cm to 7 uS/cm. Following electrospinning, this led to deposition length increasing from 1 cm to 14 cm. The samples containing pyridine easily underwent cold drawing. The strength of drawn filaments increased from 0.8 N to 1.5 N and this corresponded to a decrease in fibre diameter, with values dropping from 2.7 μm to 1 μm. Overall, these findings are useful to increase the reliability of the manufacturing process of continuous electrospun filaments and to vary their biophysical properties required for their application as medical yarns such as surgical sutures.

SUBMITTER: Lach AA

PROVIDER: S-EPMC6483168 | biostudies-literature | 2019

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Pyridine as an additive to improve the deposition of continuous electrospun filaments.

Lach Antonina A AA Morris Hayley L HL Martins Joana A JA Stace Edward T ET Carr Andrew J AJ Mouthuy Pierre-Alexis PA

PloS one 20190425 4

Electrospun filaments are leading to a new generation of medical yarns that have the ability to enhance tissue healing through their biophysical cues. We have recently developed a technology to fabricate continuous electrospun filaments by depositing the submicron fibres onto a thin wire. Here we investigate the influence of pyridine on the fibre deposition. We have added pyridine to polydioxanone solutions at concentrations ranging from 0 to 100 ppm, increasing the conductivity of the solutions ...[more]

PMID: 31022203

Similar Datasets

Project description:Despite efforts to mature human pluripotent stem cell-derived cardiomyocytes (hPSC-CMs) for disease modeling and high throughput screening, cells remain immature and may not reflect adult biology. Recent advancements utilize electro-mechanical and paracrine stimulation to functionally mature cardiomyocytes, but the resulting engineered constructs continue to lack a microenvironment conducive to electrical signal propagation and maturity. Conductive polymers are attractive candidates to facilitate electrical communication between gaps in sparse hPSC-CM clusters or between hPSC-CMs to repair conduction defects. To create a conductive polymer platform for improved electrical signal propagation between hPSC-CMs and achieve electrical maturity, we electrospun poly(3,4-ethylendioxythiophene):polystyrene sulfonate (PEDOT:PSS) blended with 8% (w/v) poly(vinyl alcohol) (PVA). Matrix fiber structure remained stable over 4 weeks in buffer, stiffness remains near cardiac stiffness in vivo, and electrical conductivity scaled with PEDOT:PSS concentration. When fibroblasts were added to fibers, cells had higher initial attachment to PEDOT:PSS compared to PVA-only scaffolds, and after 5 days, over 90% of fibroblasts remained viable on PEDOT:PSS scaffolds compared to PVA-only scaffolds. Electrically excitable hPSC-CMs cultured on conductive substrates exhibited an upregulation of cardiac and muscle-related genes as opposed to non-conductive substrates. These cells further displayed increased desmoplakin (DP) localization on conductive scaffolds, indicating an improvement in the mechanical stability of our hPSC-CMs. Sarcomere organization also scaled with increasing PEDOT:PSS concentration, even in sub-monolayer cell densities, suggesting that improved organization of the contractile machinery in these cells was due to the electrical condition of the matrix. Calcium handling indicated higher calcium flux with a shorter time to peak, further suggesting improved electrical maturity, even when sub-confluent. Taken together, these data suggest that PEDOT:PSS/PVA scaffolds are stable, of a stiffness relevant to cardiomyocytes, and supportive of electrical coupling even in the absence of a monolayer, which may improve cardiac disease modeling and drug development.

Project description:Electrospun filaments represent a new generation of medical textiles with promising applications in soft tissue repair. A potential strategy to improve their design is to combine them with bioactive molecules. Curcumin, a natural compound found in turmeric, is particularly attractive for its antioxidant, anti-inflammatory, and antimicrobial properties. However, investigating the range of relevant doses of curcumin in materials designed for tissue regeneration has remained limited. In this paper, a wide range of curcumin concentrations was explored and the potential of the resulting materials for soft tissue repair applications was assessed. Polydioxanone (PDO) filaments were prepared with various amounts of curcumin: 0%, 0.001%, 0.01%, 0.1%, 1%, and 10% (weight to weight ratio). The results from the present study showed that, at low doses (≤0.1%), the addition of curcumin has no influence on the spinning process or on the physicochemical properties of the filaments, whereas higher doses lead to smaller fiber diameters and improved mechanical properties. Moreover, filaments with 0.001% and 0.01% curcumin stimulate the metabolic activity and proliferation of normal human dermal fibroblasts (NHDFs) compared with the no-filament control. However, this stimulation is not significant when compared to the control filaments (0%). Highly dosed filaments induce either the inhibition of proliferation (with 1%) or cell apoptosis (with 10%) as a result of the concentrations of curcumin found in the medium (9 and 32 μM, respectively), which are near or above the known toxicity threshold of curcumin (~10 μM). Moreover, filaments with 10% curcumin increase the catalase activity and glutathione content in NHDFs, indicating an increased production of reactive oxygen species resulting from the large concentration of curcumin. Overall, this study suggested that PDO electrospun filaments loaded with low amounts of curcumin are more promising compared with higher concentrations for stimulating tissue repair. This study also highlighted the need to explore lower concentrations when using polymers as PDO, such as those with polycaprolactone and other degradable polyesters.

Dataset Information

Pyridine as an additive to improve the deposition of continuous electrospun filaments.

Publications

Pyridine as an additive to improve the deposition of continuous electrospun filaments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets