Tuning the Integration Rate of Ce(Ln)O2 Nanoclusters into Nanoparticulated ZrO2 Supports: When the Cation Size Matters.

ABSTRACT: Three nanostructured catalysts with low total rare earth elements (REEs) content (i.e., 15 mol.%) were prepared by depositing CeO2 or Ln3+-doped CeO2 (Ln3+ = Y3+ or La3+; Ln/Ce = 0.15) on the surface of ZrO2 nanoparticles, as nanometre-thick, fluorite-type clusters. These samples were subjected to successive reduction treatments at increasing temperatures, from 500 to 900 °C. A characterisation study by XPS was performed to clarify the diffusion process of cerium into the bulk of ZrO2 crystallites upon reduction to yield CexZr1-xO2-δ surface phases, and the influence of the incorporation of non-reducible trivalent REE cations, with sizes smaller (Y3+) and larger (La3+) than Ce4+ and Ce3+. For all nanocatalysts, a reduction treatment at a minimum temperature of 900 °C was required to accomp