Effect of the Fluorination of Graphene Nanoflake on the Dispersion and Mechanical Properties of Polypropylene Nanocomposites.

ABSTRACT: In order to investigate the effect of fluorination of graphene nanoflake on the dispersibility in polypropylene (PP) composites, fluorinated graphene oxide (FGO) was prepared by solvo-thermal reaction and applied as a filler of the PP nanocomposite. Due to the weakened inter-particle attraction among the graphene nanoflake and reduced surface energy difference between PP and the filler, PP/FGO composites showed better exfoliation and dispersion state of the filler compared with that of PP/graphene oxide (GO) or PP/reduced graphene oxide (RGO) composites. The improved exfoliation and dispersion of graphene nanoflake resulted in a significant reinforcement on the composites. The Young's modulus and tensile strength of PP composites filled with 2 wt% of FGO increased by 31% and 15%, respectively, compared with those of PP.

SUBMITTER: Lee MG

PROVIDER: S-EPMC7353096 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Effect of the Fluorination of Graphene Nanoflake on the Dispersion and Mechanical Properties of Polypropylene Nanocomposites.

Lee Min Gyu MG Lee Sangwoon S Cho Jaehyun J Bae Seokyoung S Jho Jae Young JY

Nanomaterials (Basel, Switzerland) 20200616 6

In order to investigate the effect of fluorination of graphene nanoflake on the dispersibility in polypropylene (PP) composites, fluorinated graphene oxide (FGO) was prepared by solvo-thermal reaction and applied as a filler of the PP nanocomposite. Due to the weakened inter-particle attraction among the graphene nanoflake and reduced surface energy difference between PP and the filler, PP/FGO composites showed better exfoliation and dispersion state of the filler compared with that of PP/graphe ...[more]

PMID: 32560084

Similar Datasets

Mechanical Behavior of Melt-Mixed 3D Hierarchical Graphene/Polypropylene Nanocomposites.

Project description:The mechanical properties of novel low percolation melt-mixed 3D hierarchical graphene/polypropylene nanocomposites are analyzed in this study. The analysis spans a broad range of techniques and time scales, from impact to tensile, dynamic mechanical behavior, and creep. The applicability of the time-temperature superposition principle and its limitations in the construction of the master curve for the isotactic polypropylene (iPP)-based graphene nanocomposites has been verified and presented. The Williams-Landel-Ferry method has been used to evaluate the dynamics and also Cole-Cole curves were presented to verify the thermorheological character of the nanocomposites. Short term (quasi-static) tensile tests, creep, and impact strength measurements were used to evaluate the load transfer efficiency. A significant increase of Young's modulus with increasing filler content indicates reasonably good dispersion and adhesion between the iPP and the filler. The Young's modulus results were compared with predicted modulus values using Halpin-Tsai model. An increase in brittleness resulting in lower impact strength values has also been recorded.

| S-EPMC7361869 | biostudies-literature

Mechanical Behavior of Melt-Mixed 3D Hierarchical Graphene/Polypropylene Nanocomposites.

| S-EPMC7361869 | biostudies-literature

Mesoscopic Modeling and Experimental Validation of Thermal and Mechanical Properties of Polypropylene Nanocomposites Reinforced By Graphene-Based Fillers.

Project description:The development of nanocomposites relies on structure-property relations, which necessitate multiscale modeling approaches. This study presents a modeling framework that exploits mesoscopic models to predict the thermal and mechanical properties of nanocomposites starting from their molecular structure. In detail, mesoscopic models of polypropylene (PP)- and graphene-based nanofillers (graphene (Gr), graphene oxide (GO), and reduced graphene oxide (rGO)) are considered. The newly developed mesoscopic model for the PP/Gr nanocomposite provides mechanistic information on the thermal and mechanical properties at the filler-matrix interface, which can then be exploited to enhance the prediction accuracy of traditional continuum simulations by calibrating the thermal and mechanical properties of the filler-matrix interface. Once validated through a dedicated experimental campaign, this multiscale model demonstrates that with the modest addition of nanofillers (up to 2 wt %), the Young's modulus and thermal conductivity show up to 35 and 25% enhancement, respectively, whereas the Poisson's ratio slightly decreases. Among the different combinations tested, the PP/Gr nanocomposite shows the best mechanical properties, whereas PP/rGO demonstrates the best thermal conductivity. This validated mesoscopic model can contribute to the development of smart materials with enhanced mechanical and thermal properties based on polypropylene, especially for mechanical, energy storage, and sensing applications.

| S-EPMC10753874 | biostudies-literature

Mechanical and Viscoelastic Properties of Wrinkled Graphene Reinforced Polymer Nanocomposites - Effect of Interlayer Sliding within Graphene Sheets.

Project description:Multilayer graphene sheets (MLGSs) are promising nano-reinforcements that can effectively enhance the properties of polymer matrices. Despite many studies on MLGSs-reinforced polymer nanocomposites, the effect of wrinkles formed in MLGSs on the reinforcement effect and the viscoelastic properties of polymer nanocomposites has remained unknown. In this study, building upon previously developed coarse-grained models of MLGSs and poly(methyl methacrylate) coupled with molecular dynamics simulations, we have systematically investigated nanocomposites with different numbers of graphene layers and various wrinkle configurations. We find that with decreasing degree of waviness and increasing numbers of layers, the elastic modulus of the nanocomposites increases. Interestingly, we observe a sudden stress drop during shear deformation of certain wrinkled MLGSs-reinforced nanocomposites. We further conduct small amplitude oscillatory shear simulations on these nanocomposites and find that the nanocomposites with these specific wrinkle configurations also show peculiarly large loss tangents, indicating an increasing capability of energy dissipation. These behaviors are attributed to the activation of the interlayer sliding among these wrinkled MLGSs, as their interlayer shear strengths are indeed lower than flat MLGSs measured by steered molecular dynamics technique. Our study demonstrates that the viscoelastic properties and deformation mechanisms of polymer nanocomposites can be tuned through MLGS wrinkle engineering.

| S-EPMC7990119 | biostudies-literature

Thermal, Rheological, Mechanical, and Electrical Properties of Polypropylene/Multi-Walled Carbon Nanotube Nanocomposites.

Project description:In this paper, nanocomposites based on polypropylene (PP) filled with up to 5 wt.% of multi-walled carbon nanotubes (MWCNTs) were investigated for determining the material property data used in numerical simulation of manufacturing processes such as the injection molding and extrusion. PP/MWCNT nanocomposite pellets were characterized for rheological behavior, crystallinity, specific volume and thermal conductivity, while injection-molded samples were characterized for mechanical and electrical properties. The addition of MWCNTs does not significantly change the melting and crystallization behavior of the PP/MWCNT nanocomposites. The effect of MWCNTs on melt shear viscosity is more pronounced at low shear rates and MWCNT loadings of 1-5 wt.%. However, with the addition of up to 5 wt.% of MWCNTs, the PP/MWCNT nanocomposite still behaves like a non-Newtonian fluid. The specific volume of the PP/MWCNT nanocomposites decreases with increasing MWCNT loading, especially in the MWCNT range of 1-5 wt.%, indicating better dimensional stability. The thermal conductivity, depending on the pressure, MWCNT wt.% and temperature, did not exceed 0.35 W/m·K. The PP/MWCNT nanocomposite is electrical non-conductive up to 3 wt.%, whereas after the percolating path is created, the nanocomposite with 5 wt.% becomes semi-conductive with an electrical conductivity of 10-1 S/m. The tensile modulus, tensile strength and stress at break increase with increasing MWCNT loading, whereas the elongation at break significantly decreases with increasing MWCNT loading. The Cross and modified 2-domain Tait models are suitable for predicting the melt shear viscosity and specific volume as a function of MWCNTs, respectively. These results enable users to integrate the PP/MWCNT nanocomposites into computer aided engineering analysis.

| S-EPMC7825608 | biostudies-literature

Effect of Graphite Nanoplatelet Size and Dispersion on the Thermal and Mechanical Properties of Epoxy-Based Nanocomposites.

Project description:This study investigated the effect of graphite nanoplatelet (GNP) size and dispersion on the thermal conductivities and tensile strengths of epoxy-based composites. GNPs of four different platelet sizes, ranging from 1.6 to 3 µm, were derived by mechanically exfoliating and breaking expanded graphite (EG) particles using high-energy bead milling and sonication. The GNPs were used as fillers at loadings of 0-10 wt%. As the GNP size and loading amount increased, the thermal conductivities of the GNP/epoxy composites increased, but their tensile strengths decreased. However, interestingly, the tensile strength reached a maximum value at the low GNP content of 0.3% and thereafter decreased, irrespective of the GNP size. Our observations of the morphologies and dispersions of the GNPs in the composites indicated that the thermal conductivity was more likely related to the size and loading number of fillers, whereas the tensile strength was more influenced by the dispersion of fillers in the matrix.

| S-EPMC10144909 | biostudies-literature

Effect of benzoic acid surface modified alumina nanoparticles on the mechanical properties and crystallization behavior of isotactic polypropylene nanocomposites.

Project description:The effect of benzoic acid (BA) surface modified alumina (Al2O3) nanoparticles (NPs) on the mechanical properties and crystallization behavior of isotactic polypropylene (iPP) nanocomposites was studied. Characterization of the modified Al2O3 NPs (BA-Al2O3) by FTIR and XRD analyses confirmed that benzoic acid molecules chemisorb on the surface of the NPs, forming benzene groups-rich microstructures. A considerable increase in the tensile strength, flexural modulus, and toughness was observed for the nanocomposites with only 0.2 wt% BA-Al2O3. Enhanced interfacial adhesion with the matrix was achieved, which enabled effective reinforcement of the nanocomposites. The higher crystallization temperature along with shorter crystallization halftime indicated the higher nucleation activity of BA-Al2O3. Furthermore, the interchain conformational ordering of iPP was significantly accelerated in the presence of the BA-Al2O3 NPs. The CH-π interaction between the polymer and BA-Al2O3 NPs was considered to facilitate the attachment of the iPP chains and stimulate conformational ordering, crystallization, as well as mechanical properties of nanocomposites.

| S-EPMC9080881 | biostudies-literature

Mechanical and Physical Properties of Short Carbon Fiber and Nanofiller-Reinforced Polypropylene Hybrid Nanocomposites.

Project description:The effect of various combinations of filler materials on the performance of polypropylene (PP)-based composites was investigated. PP in particulate form was used as the matrix. Milled short carbon fiber (SCF) micro-size, graphite nano-platelet (GNP), and titanium dioxide nanoparticles (nTiO2) were used as fillers. These fillers were incorporated in the polymer matrix to produce mono-filler (PP/SCF and PP/nanofiller) and hybrid composites. Hybrid composites consist of PP/10SCF/GNP, PP/10SCF/nTiO2, and PP/10SCF/GNP/nTiO2. The effect of the addition of SCF, GNP, and nTiO2 on PP-based composites was investigated by analyzing their morphological, mechanical, and physical properties. The addition of mono-filler to the PP matrix improved the mechanical properties of the composites when compared to the neat PP. The ultimate tensile strength (UTS), flexural modulus, flexural strength, and impact toughness of the hybrid composites with 15 wt % total loading of fillers, were higher than that of mono-filler composites with 15 wt % SCF (PP/15SCF). A maximum increase of 20% in the flexural modulus was observed in the hybrid composite with 10 wt % of SCF with the additional of 2.5 wt % GNP and 2.5 wt % nTiO2 when compared to PP/15SCF composite. The addition of 2.5 wt % nTiO2 to the 10 wt % SCF reinforced PP, resulted in increasing the strain at break by 15% when compared to the PP/10SCF composite. A scanning electron microscope image of the PP/10SCF composite with the addition of GNP improved the interfacial bonding between PP and SCF compared with PP/SCF alone. A decrease in the melt flow index (MFI) was observed for all compositions. However, hybrid composites showed a higher decrease in MFI.

| S-EPMC7761221 | biostudies-literature

Synergetic Effect of Graphene and MWCNTs on Microstructure and Mechanical Properties of Cu/Ti3SiC2/C Nanocomposites.

Project description:Multi-walled carbon nanotubes (MWCNTs) and graphenes have been taken for novel reinforcements due to their unique structure and performance. However, MWCNTs or graphenes reinforced copper matrix composites could not catch up with ideal value due to reinforcement dispersion in metal matrix, wettability to metal matrix, and composite material interface. Taking advantage of the superior properties of one-dimensional MWCNTs and two-dimensional graphenes, complementary performance and structure are constructed to create a high contact area between MWCNTs and graphenes to the Cu matrix. Mechanical alloying, hot pressing, and hot isostatic pressing techniques are used to fabricate Cu matrix self-lubricating nanocomposites. Effects of MWCNTs and graphenes on mechanical properties and microstructures of Cu/Ti3SiC2/C nanocomposites are studied. The fracture and strengthening mechanisms of Cu/Ti3SiC2/C nanocomposites are explored on the basis of structure and composition of Cu/Ti3SiC2/C nanocomposites with formation and function of interface.

| S-EPMC5704033 | biostudies-literature

Polypropylene/Ethylene-And Polar-Monomer-Based Copolymers/Montmorillonite Nanocomposites: Morphology, Mechanical Properties, and Oxygen Permeability.

Project description:This research reports the influence of polar monomer contents in ethylene vinyl acetate copolymer (EVA) and ethylene vinyl alcohol copolymer (EVOH) on the morphology, mechanical and barrier properties of polypropylene/ethylene copolymer (PP) reinforced with organically modified montmorillonite (MMT). PP/EVA and PP/EVOH (75/25 wt %) blends were reinforced with 3 wt % MMT in an internal mixer system. Samples were compression-molded into films of 300μ μm. The structural characterization was made using X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), the mechanical properties were obtained by tension tests and the barrier properties by oxygen transmission rate (OTR). XRD patterns showed a combination of intercalated/exfoliated morphologies for the MMT, with higher d-001 interplanar distance increments for the blends with higher content of polar functional groups. SEM and TEM micrographs complement the results of the XRD analysis and show differences in the morphologies depending on the miscibility of the polyolefin and the polar monomer copolymer. Mechanical properties and oxygen permeability of composites exhibited a higher improvement, by the addition of MMT, for higher intermolecular interactions and most miscible polymeric system of the EVA. These results show that the higher the number of interactions, given by the VA or OH polar functional groups, the morphology and the miscibility between polyolefin and copolymer imply dispersion improvements of the nanocomposites and, in consequence, a higher improvement on the mechanical and barrier properties of the composite material.

| S-EPMC7956292 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data