Influence of Modified Epoxy Resins on Peroxide Curing, Mechanical Properties and Adhesion of SBR, NBR and XNBR to Silver Wires-Part II: Application of Carboxy-Containing Peroxy Oligomer (CPO).

ABSTRACT: This research was aimed at verifying the effect of carboxy-containing peroxy oligomer (CPO) addition on the possibility of rubber crosslinking and a subsequent adhesion of the modified rubber to silver wires. Three commonly industrially used rubbers were selected for the study: styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR) and carboxylated acrylonitrile-butadiene rubber (XNBR), together with carboxy-containing peroxy oligomer (CPO). An improvement in the adhesion of rubbers to silver wires was observed when applying the oligomeric peroxide with functional groups, with no deterioration of mechanical properties of the vulcanizates. Crosslinking synergy between dicumyl peroxide (DCP) and the modifier could hardly be observed. Nevertheless, the studies demonstrated, that to a small extent, even the CPO itself can crosslink NBR and especially XNBR, resulting in a material of notable elasticity and adhesion to silver wires.

SUBMITTER: Chudzik J

PROVIDER: S-EPMC7962661 | biostudies-literature | 2021 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Influence of Modified Epoxy Resins on Peroxide Curing, Mechanical Properties and Adhesion of SBR, NBR and XNBR to Silver Wires-Part II: Application of Carboxy-Containing Peroxy Oligomer (CPO).

Chudzik Joanna J Bieliński Dariusz M DM Bratychak Michael M Demchuk Yuriy Y Astakhova Olena O Jędrzejczyk Marcin M Celichowski Grzegorz G

Materials (Basel, Switzerland) 20210308 5

This research was aimed at verifying the effect of carboxy-containing peroxy oligomer (CPO) addition on the possibility of rubber crosslinking and a subsequent adhesion of the modified rubber to silver wires. Three commonly industrially used rubbers were selected for the study: styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR) and carboxylated acrylonitrile-butadiene rubber (XNBR), together with carboxy-containing peroxy oligomer (CPO). An improvement in the adhesion of rubber ...[more]

PMID: 33800322

Similar Datasets

Project description:One-component epoxy resins (OCERs) with improved stability (shelf life) and controlled curing temperatures were prepared using epoxy resins and polyoxazoline-imidazole (POZ-Im) based thermal latent curing agents (TLCs). POZ homopolymers with molar masses of 1000, 2000, and 5000 g/mol were obtained via cationic ring-opening polymerization (CROP) of 2-ethyl-2-oxazoline, 2-propyl-2-oxazoline, 2-pentyl-2-oxazoline, and 2-phenyl-2-oxazoline. TLCs were prepared by physically entrapping imidazole, the curing agent, in the POZ matrix at the homopolymer/Im (HP/Im) ratios of 1:1 and 5:1 and characterized by FTIR and TGA. TLCs were then mixed with bisphenol A diglycidyl ether (DGEBA) to obtain OCERs with Im concentrations of 1, 3, and 5 wt %. Dynamic DSC tests were performed to determine the effect of the pendant group and molar mass of POZ, the POZ/Im ratio, and Im concentration on the curing behavior of the OCERs, whereas isothermal DSC tests were carried out to examine their thermal stability and optimal curing temperatures. Optical microscopy was performed to study the compatibility of the TLCs with DGEBA. This study showed that the dispersion quality of TLCs is highly associated with the compatibility of POZs and DGEBA, which affected the release of Im, thus left limit temperatures of curing. In addition, higher left limit temperatures were obtained when the POZ/Im ratio increased. Isothermal DSC results conformed to the improved stability and better thermal latency of the samples with a POZ/Im ratio of 5:1. Moreover, the higher left limit temperatures were obtained with the lowest molar mass of POZ due to the better interaction between the -OH end group of POZ and Im. The shelf life of PEOZ 1K-Im 5:1 1% OCER was predicted at -20, 0, and 20 °C, with an estimated 15.3 days at 20 °C using isothermal DSC and rheology at 50, 60, and 70 °C. Overall, this research contributes to the development of OCERs by introducing POZ-Im complexes as novel TLCs. The findings shed light on the importance of compatibility in achieving optimal dispersion and release of Im and the role of the POZ/Im ratio and POZ molar mass in controlling left limit temperatures, ultimately influencing the curing behavior of OCERs.

Dataset Information

Influence of Modified Epoxy Resins on Peroxide Curing, Mechanical Properties and Adhesion of SBR, NBR and XNBR to Silver Wires-Part II: Application of Carboxy-Containing Peroxy Oligomer (CPO).

Publications

Influence of Modified Epoxy Resins on Peroxide Curing, Mechanical Properties and Adhesion of SBR, NBR and XNBR to Silver Wires-Part II: Application of Carboxy-Containing Peroxy Oligomer (CPO).

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets