PH-sensitive thiamethoxam nanoparticles based on bimodal mesoporous silica for improving insecticidal efficiency.

ABSTRACT: In this study, we synthesized pH-sensitive thiamethoxam-3-(2-aminoethylamino) propyl-bimodal mesoporous silica (P/Thi-NN-BMMs) nanoparticles (NPs). We used this bimodal mesoporous silica (BMMs) mesoporous material as a carrier based on the principle of free radical polymerization. The size of the P/Thi-NN-BMMs NPs was about 891.7 ± 4.9 nm, with a zeta potential of about -25.7 ± 2.5 mV. X-ray powder diffraction analysis, N₂-sorption measurements and thermogravimetric analysis indicated that thiamethoxam (Thi) was loaded into the pores of the mesoporous structure and that the mesopore surface was coated with polyacrylic acid (PAA). The loading rate of P/Thi-NN-BMMs was about 25.2%. The controlled-release NPs had excellent anti-photolysis performance and storage stability. The NPs showed significant pH sensitivity, and the Thi release rate in pH 10.0 phosphate buffer was higher than those in pH 7.4 and pH 3.0 phosphate buffers. We described the sustained-release curves according to the Weibull model. The relative toxicity of P/Thi-NN-BMMs against peach aphid was 1.44 times that of commercial Thi. This provides a promising instrument for effective insect control and environment protection.

SUBMITTER: Li W

PROVIDER: S-EPMC8074711 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

pH-sensitive thiamethoxam nanoparticles based on bimodal mesoporous silica for improving insecticidal efficiency.

Li Wenjing W Wang Qi Q Zhang Fang F Shang Hui H Bai Shiyang S Sun Jihong J

Royal Society open science 20210217 2

In this study, we synthesized pH-sensitive thiamethoxam-3-(2-aminoethylamino) propyl-bimodal mesoporous silica (P/Thi-NN-BMMs) nanoparticles (NPs). We used this bimodal mesoporous silica (BMMs) mesoporous material as a carrier based on the principle of free radical polymerization. The size of the P/Thi-NN-BMMs NPs was about 891.7 ± 4.9 nm, with a zeta potential of about -25.7 ± 2.5 mV. X-ray powder diffraction analysis, N<sub>2</sub>-sorption measurements and thermogravimetric analysis indicated ...[more]

PMID: 33972874

Similar Datasets

Project description:Tunable glutathione (GSH)-sensitive hollow mesoporous silica nanoparticles (HMSiO2 NPs) were developed using a structural difference-based selective etching strategy. These organosilica hollow nanoparticles contained disulfide linkages (S-S) in the outer shell which were degraded by GSH. The particles were compared with their nonGSH-sensitive tetraethyl orthosilicate (TEOS) HMSiO2 counterparts in terms of their synthesis method, characterization, doxorubicin (DOX) release profile, and in vitro cytotoxicity in MCF-7 breast cancer cells. Transmission electron microscopy (TEM) of the particles indicated that the fabricated HMSiO2 NPs had an average diameter of 130 ± 5 nm. Thermogravimetric analysis (TGA) revealed that GSH-sensitive particles had approximately 5.3% more weight loss than TEOS HMSiO2 NPs. Zeta potential of these redox-responsive particles was -23 ± 1 mV at pH 6 in deionized (DI) water. Nitrogen adsorption-desorption isotherm revealed that the surface area of the hollow mesoporous nanoreservoirs was roughly 446 ± 6 m2 g-1 and the average diameter of the pores was 2.3 ± 0.5 nm. TEM images suggest that the nanoparticles started to lose mass integrity from Day 1. The particles showed a high loading capacity for DOX (8.9 ± 0.5%) as a model drug, due to the large voids existing in the hollow structures. Approximately 58% of the incorporated DOX released within 14 days in phosphate buffered saline (PBS) at pH 6 and in the presence of 10 mM of GSH, mimicking intracellular tumor microenvironment while release from TEOS HMSiO2 NPs was only c.a. 18%. The uptake of these hollow nanospheres by MCF-7 cells and RAW 264.7 macrophages was evaluated using TEM and confocal microscopy. The nanospheres were shown to accumulate in the endolysosomal compartments after incubation for 24 h with the maximum uptake of c.a. 2.1 ± 0.3% and 5.2 ± 0.4%, respectively. Cytotoxicity of the nanospheres was investigated using CCK-8 assay. Results indicate that intact hollow particles (both GSH-sensitive and TEOS HMSiO2 NPs) were nontoxic to MCF-7 cells after incubation for 24 h within the concentration range of 0-1000 μg ml-1. DOX-loaded GSH-sensitive nanospheres containing 6 μg ml-1 of DOX killed c.a. 51% of MCF-7 cells after 24 h while TEOS HMSiO2 NPs killed c.a. 20% with the difference being statistically significant. Finally, cytotoxicity data in RAW 264.7 macrophages and NIH 3 T3 fibroblasts shows that intact GSH-sensitive HMSiO2 NPs did not show any toxic effects on these cells with the concentrations equal or <125 μg ml-1.

Dataset Information

PH-sensitive thiamethoxam nanoparticles based on bimodal mesoporous silica for improving insecticidal efficiency.

Publications

pH-sensitive thiamethoxam nanoparticles based on bimodal mesoporous silica for improving insecticidal efficiency.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets