Surface related laser induced white emission of Cr:YAG ceramic.

ABSTRACT: In this work we report the white light emission in transparent Cr:YAG ceramic pellet upon irradiation with focused beam of CW infrared laser diode. It was found that this phenomenon is specifically related to interaction of laser beam with a surface of the pellet. The white light was emitted outside an irradiated spot at the surface of the pellet and did not penetrate inside the pellet. Moreover, the red emission related to two-photon absorption along the laser beam penetrating the Cr³⁺:YAG pellet was observed. Interaction of the laser beam with the surface of the pellet leads to an efficient white light emission from an outer side of the pellet. The resulting white light emission did not entry back the pellet. Multiphoton ionization leading to intervalence charge transfer followed by light emission was proposed as the mechanism of experimentally observed white light emission.

SUBMITTER: Chaika M

PROVIDER: S-EPMC8263758 | biostudies-literature | 2021 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Surface related laser induced white emission of Cr:YAG ceramic.

Chaika M M Tomala R R Strek W W

Scientific reports 20210707 1

In this work we report the white light emission in transparent Cr:YAG ceramic pellet upon irradiation with focused beam of CW infrared laser diode. It was found that this phenomenon is specifically related to interaction of laser beam with a surface of the pellet. The white light was emitted outside an irradiated spot at the surface of the pellet and did not penetrate inside the pellet. Moreover, the red emission related to two-photon absorption along the laser beam penetrating the Cr<sup>3+</su ...[more]

PMID: 34234267

Similar Datasets

Project description:In orthodontic practice, due to the increased interest among patients in smile aesthetics, different types of brackets are now being used, with those most frequently applied being ones made of polycrystalline and monocrystalline ceramic. The aim of this study was to evaluate the laser Er:YAG-assisted debonding technique compared to conventional methods for removing monocrystalline ceramic brackets from human teeth. The study sample included 60 vital teeth (frontals of the upper jaw) from 10 patients who had monocrystalline ceramic brackets and were in the final phase of orthodontic treatment. The debonding procedure was carried out following a split-mouth study design, using either the conventional technique or laser Er:YAG 2940 nm radiation. For each tooth, three variables were evaluated: the patient's sujective tooth sensitivity associated with the debonding, the time required for debonding, and pulp blood flow microdynamics after the debonding. Three evaluation instruments were used to assess and quantify the treatment effects: (i) the Wong-Baker FACES Pain Rating Scale for pain assessment; (ii) a digital stopwatch/timer to measure the time required to remove the bracket; and (iii) laser Doppler flowmetry (LDF) for recording the pulp blood flow evolution. The statistical analysis of the recorded data showed a statistically significant difference between the two debonding methods regarding the tooth sensitivity during the debonding and the time required for the procedure. The subjective tooth sensitivity was reduced from a mean ± standard deviation of 3.07 ± 1.46 to 0.47 ± 0.86 on the Wong-Baker FACES scale (Wilcoxon signed rank, p < 0.001). The necessary time for debonding was reduced by 0.697 ± 0.703 s per tooth (paired t-test, p < 0.001). There was no difference in the blood microdynamics between the two debonding techniques. According to the results of this study, the laser Er:YAG-assisted debonding technique may be a viable alternative to the conventional method for monocrystalline ceramic brackets.

Project description:We investigated the biofilm removal effects of laser activated irrigation (LAI) using a pig model, focusing on the impact of the fiber tip position, and used a high-speed camera to observe the occurrence and positioning of the cavitation associated with laser irradiation. A total of 16 roots of deciduous mandibular second premolars from 4 pigs were used. After a pulpectomy, the canals were left open for 2 weeks and sealed for 4 weeks to induce intraradicular biofilm. Root canal irrigation was then performed with Er:YAG laser activation. The fiber tip was inserted at two different positions, i.e., into the root canal in the intracanal LAI group and into the pulp chamber in the coronal LAI group. Intracanal needle irrigation with saline or 5% NaOCl was utilized in the positive control and conventional needle irrigation (CNI) groups. SEM and qPCR were carried out to evaluate treatment efficacy. Statistical analysis was performed using ANOVA and a Tukey-Kramer post-hoc test for qPCR and with a Steel-Dwass test to compare the SEM scores, with α = 0.05. A high-speed camera was used to observe the generation of cavitation bubbles and the movement of the induced bubbles after laser irradiation. The intracanal and coronal LAI groups showed significantly lower amounts of bacteria than either the positive control or CNI groups. There was no significant difference found between the intracanal and coronal LAI groups. SEM images revealed opened dentinal tubules with the destruction of biofilm in both LAI groups. High-speed camera images demonstrated cavitation bubble production inside the root canal after a single pulse irradiation pulse. The generated bubbles moved throughout the entire internal multi-rooted tooth space. Coronal LAI can generate cavitation in the root canal with a simply placed fiber inside the pulp chamber, leading to effective biofilm removal. This method could thus contribute to the future development of endodontic treatments for refractory apical periodontitis caused by intraradicular biofilm.

Dataset Information

Surface related laser induced white emission of Cr:YAG ceramic.

Publications

Surface related laser induced white emission of Cr:YAG ceramic.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets