Effects of Temperature and Blinking on Contact Lens Dehydration of Contemporary Soft Lens Materials Using an In Vitro Blink Model.

ABSTRACT:

Purpose

The purpose of this study was to evaluate the effects of temperature and blinking on contact lens (CL) dehydration using an in vitro blink model.

Methods

Three silicone hydrogel (delefilcon A, senofilcon A, and comfilcon A) and two conventional hydrogel (etafilcon A and omafilcon A) CL materials were evaluated at 1 and 16 hours. The water content (WC) of the CLs was measured using a gravimetric method. Lenses were incubated on a blink model, internally heated to achieve a clinically relevant surface temperature of 35°C. An artificial tear solution (ATS) was delivered to the blink model at 4.5 µL/min with a blink rate of 6 blinks/min. A comparison set of lenses were incubated in a vial containing either 2 mL of ATS or phosphate-buffered saline (PBS) at 35°C.

Results

Increasing temperature to 35°C resulted in a decrease in WC for all tested CLs over time (P ≤ 0.0052). For most CLs, there was no significant difference in WC over time between ATS or PBS in the vial (P > 0.05). With the vial system, WC decreased and plateaued over time. However, on the blink model, for most CLs, the WC significantly decreased after 1 hour but returned toward initial WC levels after 16 hours (P > 0.05).

Conclusions

The reduction in WC of CLs on the eye is likely due to both an increase in temperature and dehydration from air exposure and blinking.

Translational relevance

This study showed that the novel, heated, in vitro blink model could be used to provide clinical insights into CL dehydration on the eye.