Structural characterization and magnetic response of poly(p-xylylene)-MnSb and MnSb films deposited at cryogenic temperature.

ABSTRACT: In this study, we employed several experimental techniques to investigate structure and magnetic properties of poly(p-xylylene)-MnSb composites synthesized by low-temperature vapor deposition polymerization technique and MnSb films deposited at various temperatures. The presence of MnSb nanocrystallites in the studied films was verified by the results of X-ray diffraction, electron microscopy and Raman spectroscopy studies. The obtained data revealed the formation of Sb-rich sublayer with well-oriented Sb grains near the susbtrate, which seems to act as a buffer for the consequent poly(p-xylylene)-MnSb or MnSb layer growth. Increasing the polymer content results in qualitative change of surface morphology of studied films. At high polymer content the hybrid nanocomposite with MnSb nanoparticles embedded into poly(p-xylylene) matrix is formed. All investigated samples demonstrated detectable ferromagnetic response at room temperature, while the parameters of this response revealed a complex correlation with nominal composition, presented crystal phases and surface morphology of studied films. Estimated values of the Curie temperature of the samples are close to that of bulk MnSb.

SUBMITTER: Oveshnikov LN

PROVIDER: S-EPMC8346481 | biostudies-literature | 2021 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Structural characterization and magnetic response of poly(p-xylylene)-MnSb and MnSb films deposited at cryogenic temperature.

Oveshnikov L N LN Zav'yalov S A SA Trunkin I N IN Streltsov D R DR Chumakov N K NK Dmitryakov P V PV Prutskov G V GV Kondratev O A OA Nesmelov A A AA Chvalun S N SN

Scientific reports 20210806 1

In this study, we employed several experimental techniques to investigate structure and magnetic properties of poly(p-xylylene)-MnSb composites synthesized by low-temperature vapor deposition polymerization technique and MnSb films deposited at various temperatures. The presence of MnSb nanocrystallites in the studied films was verified by the results of X-ray diffraction, electron microscopy and Raman spectroscopy studies. The obtained data revealed the formation of Sb-rich sublayer with well-o ...[more]

PMID: 34362988

Similar Datasets

Project description:Conjugated polymers such as poly(3,4-ethylenedioxythiphene) (PEDOT) are of interest for a variety of applications including interfaces between electronic biomedical devices and living tissue. The mechanical properties, strength, and adhesion of these materials to solid substrates are all vital for long-term applications. We have been developing methods to quantify the mechanical properties of conjugated polymer thin films. In this paper, the stiffness, strength and the interfacial shear strength (adhesion) of electrochemically deposited PEDOT and PEDOT-co-1,3,5-tri[2-(3,4-ethylene dioxythienyl)]-benzene (EPh) were studied. The estimated Young's modulus of the PEDOT films was 2.6±1.4GPa, and the strain to failure was around 2%. The tensile strength was measured to be 56±27MPa. The effective interfacial shear strength was estimated with a shear-lag model by measuring the crack spacing as a function of film thickness. For PEDOT on gold/palladium-coated hydrocarbon film substrates an interfacial shear strength of 0.7±0.3MPa was determined. The addition of 5mole% of a tri-functional EDOT crosslinker (EPh) increased the tensile strength of the films to 283±67MPa, while the strain to failure remained about the same (2%). The effective interfacial shear strength was increased to 2.4±0.6MPa.Statement of significanceThis paper describes methods for estimating the ultimate mechanical properties of electrochemically deposited conjugated polymer (here PEDOT and PEDOT copolymers) films. Of particular interest and novelty is our implementation of a cracking test to quantify the shear strength of the PEDOT thin films on these solid substrates. There is considerable interest in these materials as interfaces between biomedical devices and living tissue, however potential mechanisms and modes of failure are areas of continuing concern, and establishing methods to quantify the strengths of these interfaces are therefore of particular current interest. We are confident that these results will be useful to the broader biological materials community and are worthy of broader dissemination.

Dataset Information

Structural characterization and magnetic response of poly(p-xylylene)-MnSb and MnSb films deposited at cryogenic temperature.

Publications

Structural characterization and magnetic response of poly(p-xylylene)-MnSb and MnSb films deposited at cryogenic temperature.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets