New Principles of Polymer Composite Preparation. MQ Copolymers as an Active Molecular Filler for Polydimethylsiloxane Rubbers.

ABSTRACT: Colorless transparent vulcanizates of silicone elastomers were prepared by mixing the components in a common solvent followed by solvent removal. We studied the correlation between the mechanical behavior of polydimethylsiloxane (PDMS)-rubber compositions prepared using MQ (mono-(M) and tetra-(Q) functional siloxane) copolymers with different ratios of M and Q parts as a molecular filler. The composition and molecular structure of the original rubber, MQ copolymers, and carboxyl-containing PDMS oligomers were also investigated. The simplicity of the preparation of the compositions, high strength and elongation at break, and their variability within a wide range allows us to consider silicone elastomers as a promising alternative to silicone materials prepared by traditional methods.

SUBMITTER: Meshkov IB

PROVIDER: S-EPMC8433927 | biostudies-literature | 2021 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

New Principles of Polymer Composite Preparation. MQ Copolymers as an Active Molecular Filler for Polydimethylsiloxane Rubbers.

Meshkov Ivan B IB Kalinina Aleksandra A AA Gorodov Vadim V VV Bakirov Artem V AV Krasheninnikov Sergey V SV Chvalun Sergei N SN Muzafarov Aziz M AM

Polymers 20210825 17

Colorless transparent vulcanizates of silicone elastomers were prepared by mixing the components in a common solvent followed by solvent removal. We studied the correlation between the mechanical behavior of polydimethylsiloxane (PDMS)-rubber compositions prepared using MQ (mono-(M) and tetra-(Q) functional siloxane) copolymers with different ratios of M and Q parts as a molecular filler. The composition and molecular structure of the original rubber, MQ copolymers, and carboxyl-containing PDMS ...[more]

PMID: 34502890

Similar Datasets

Manufacturing Technology of Composite Materials-Principles of Modification of Polymer Composite Materials Technology Based on Polytetrafluoroethylene.

Project description:The results of the investigations into the technological formation of new wear-resistant polymer composites based on polytetrafluoroethylene (PTFE) filled with disperse synthetic and natural compounds are presented. The efficiency of using PTFE composites reinforced with carbon fibers depends on many factors, which influence the significant improvement of physicomechanical characteristics. The results of this research allow stating that interfacial and surface phenomena of the polymer-solid interface and composition play a decisive role in PTFE composites properties. Fillers hinder the relative movement of the PTFE molecules past one another and, in this way, reduce creep or deformation of the parts, reducing the wear rate of parts used in dynamic applications as well as the coefficient of thermal expansion. The necessary structural parameters of such polymer composites are provided by regimes of process equipment.

| S-EPMC5506908 | biostudies-other

Electroconductive Composites from Polystyrene Block Copolymers and Cu-Alumina Filler.

Project description:Technological advancements and development of new materials may lead to the manufacture of sustainable energy-conducting devices used in the energy sector. This research attempts to fabricate novel electroconductive and mechanically stable nanocomposites via an electroless deposition (ELD) technique using electrically insulating materials. Metallic Cu is coated onto Al₂O₃ by ELD, and the prepared filler is then integrated (2-14 wt %) into a matrix of polystyrene-block-poly(ethylene-ran-butylene)-block-polystyrene-graft-maleic anhydride (PS-b-(PE-r-B)-b-PS-g-MA). Considerable variations in composite phases with filler inclusion exist. The Cu crystallite growth onto Al₂O₃ was evaluated by X-ray diffraction (XRD) analysis and energy dispersive spectrometry (EDS). Scanning electron microscopy (SEM) depicts a uniform Cu coating on Al₂O₃, while homogeneous filler dispersion is exhibited in the case of composites. The electrical behavior of composites is enhanced drastically (7.7 × 10-5 S/cm) upon incorporation of Cu-Al₂O₃ into an insulating polymer matrix (4.4 × 10-16 S/cm). Moreover, mechanical (Young's modulus, tensile strength and % elongation at break) and thermal (thermogravimetric analysis (TGA), derivative thermogravimetry (DTG), and differential scanning calorimetry (DSC)) properties of the nanocomposites also improve substantially. These composites are likely to meet the demands of modern high-strength electroconductive devices.

| S-EPMC5456950 | biostudies-other

Fouling Release Coatings Based on Acrylate-MQ Silicone Copolymers Incorporated with Non-Reactive Phenylmethylsilicone Oil.

Project description:Copolymers containing MQ silicone and acrylate were synthesized by controlling the additive amount of compositions. Subsequently, fouling release coatings based on the copolymer with the incorporation of non-reactive phenylmethylsilicone oil were prepared. The surface properties of the coating (CAMQ40) were consistent with that of the polydimethylsiloxane (PDMS) elastomer, which ensured good hydrophobicity. Moreover, the seawater volume swelling rate of all prepared coatings was less than 5%, especially for CAMQ40 with only 1.37%. Copolymers enhanced the mechanical properties of the coatings, while the enhancement was proportional to the molar content of structural units from acrylate in the copolymer. More importantly, the adhesion performance between the prepared coatings and substrates indicated that pull-off strength values were more than 1.6 MPa, meaning a high adhesion strength. The phenylmethylsilicone oil leaching observation determined that the oil leaching efficiency increased with the increase in the structural unit's molar content from MQ silicone in the copolymer, which was mainly owing to the decrease in compatibility between oil and the cured coating, as well as the decrease in mechanical properties. High oil leaching efficiency could make up for the decrease in the biofouling removal rate due to the enhancement of the elastic modulus. For CAMQ40, it had an excellent antifouling performance at 30 days of exposure time with more than 92% of biofouling removal rate, which was confirmed by biofilm adhesion assay.

| S-EPMC8469071 | biostudies-literature

Synthesis of BaTiO<sub>3</sub> nanoparticles as shape modified filler for high dielectric constant ceramic-polymer composite.

Project description:Coral-like structured barium titanate (BaTiO3) nanoparticles were synthesized as filler for a high dielectric elastomer. The nanoparticle size, and shape, and the reactivity of the synthesis were modified according to temperature, time, pH, and precursor materials. Dielectric properties of poly(dimethylsiloxane) (PDMS) composites were estimated by volume fractions of BaTiO3 of 5, 10, and 15 vol% for both sphere and coral-like shapes. As a result, coral-like BaTiO3-PDMS composites had the highest dielectric constant of 10.97, which was 64% higher than the spherical BaTiO3-PDMS composites for the 15 vol% fraction. Furthermore, the phase transition process and surface modification were applied to increase the dielectric properties through calcination and improved particle dispersion in the elastomer using polyvinylpyrrolidone (PVP). The dispersion of the PVP coated BaTiO3-PDMS composite was improved compared to pristine BaTiO3 as shown by SEM imaging. The coral-like BaTiO3 embedded composite could be used for electronic devices such as piezoelectric devices or electro-adhesive grippers, which require flexible and high dielectric materials.

| S-EPMC9055919 | biostudies-literature

Rapid Preparation of Novel Ionic Polymer-Metal Composite for Improving Humidity Sensing Effect.

Project description:Ionic polymer-metal composites (IPMCs) have attracted attention in recent years due to their integration of actuation and sensing functions. As one of the main sensing functions of IPMCs, humidity sensing has been of consistent interest in wearable health monitors and artificial skin. However, there are still some technical challenges in that classical IPMCs have poor humidity sensing performance due to their dense surface electrode, and IPMCs are damaged easily due to an electrode/membrane mismatch. In this work, through the spraying and electrodepositing process, we developed an efficient method to rapidly prepare a Au-shell-Ag-NW (silver nanowire)-based IPMC with high strength, low surface resistance and excellent humidity sensing performance. Meanwhile, we optimized the preparation method by clarifying the influence of solvent type and electrodepositing time on the performance of the Au-shell-Ag-NW-based IPMC, thus effectively improving the humidity sensing effect and strength of the IPMC. Compared with previous research, the humidity electrical response (~9.6 mV) of the Au-shell-Ag-NW-based IPMC is at least two orders of magnitude higher than that of the classical IPMC (~0.41 mV), which is mainly attributed to the sparse gap structure for promoting the exchange of water molecules in the environment and Nafion membrane, a low surface resistance (~3.4 Ohm/sq) for transmitting the signal, and a seamless connection between the electrode and Nafion membrane for fully collecting the ion charges in the Nafion membrane. Additionally, the Au-shell-Ag-NW-based IPMC could effectively monitor the human breathing process, and the humidity sensing performance did not change after being exposed to the air for 4 weeks, which further indicates that the Au-shell-Ag-NW-based IPMC has good application potential due to its efficient preparation technology, high stability and good reproducibility.

| S-EPMC9921886 | biostudies-literature

Electrorheological Properties of Polydimethylsiloxane/TiO2-Based Composite Elastomers.

Project description:Electrorheological elastomers based on polydimethylsiloxane filled with hydrated titanium dioxide with a particle size of 100-200 nm were obtained by polymerization of the elastomeric matrix, either in the presence, or in the absence, of an external electric field. The viscoelastic and dielectric properties of the obtained elastomers were compared. Analysis of the storage modulus and loss modulus of the filled elastomers made it possible to reveal the influence of the electric field on the Payne effect in electrorheological elastomers. The elastomer vulcanized in the electric field showed high values of electrorheological sensitivity, 250% for storage modulus and 1100% for loss modulus. It was shown, for the first time, that vulcanization of filled elastomers in the electric field leads to a significant decrease in the degree of crosslinking in the elastomer. This effect should be taken into account in the design of electroactive elastomeric materials.

| S-EPMC7569977 | biostudies-literature

A resorbable antibiotic-eluting polymer composite bone void filler for perioperative infection prevention in a rabbit radial defect model.

Project description:Nearly 1.3 million total joint replacement procedures are performed in the United States annually, with numbers projected to rise exponentially in the coming decades. Although finite infection rates for these procedures remain consistently low, device-related infections represent a significant cause of implant failure, requiring secondary or revision procedures. Revision procedures manifest several-fold higher infection recurrence rates. Importantly, many revision surgeries, infected or not, require bone void fillers to support the host bone and provide a sufficient tissue bed for new hardware placement. Antibiotic-eluting bone void fillers (ABVF), providing both osteoconductive and antimicrobial properties, represent one approach for reducing rates of orthopedic device-related infections. Using a solvent-free, molten-cast process, a polymer-controlled antibiotic-eluting calcium carbonate hydroxyapatite (HAP) ceramic composite BVF (ABVF) was fabricated, characterized, and evaluated in vivo using a bacterial challenge in a rabbit radial defect window model. ABVF loaded with tobramycin eliminated the infectious burden in rabbits challenged with a clinically relevant strain of Staphylococcus aureus (inoculum as high as 10⁷ CFU). Histological, microbiological, and radiographic methods were used to detail the effects of ABVF on microbial challenge to host bone after 8 weeks in vivo. In contrast to the HAP/BVF controls, which provided no antibiotic protection and required euthanasia 3 weeks post-operatively, tobramycin-releasing ABVF animals showed no signs of infection (clinical, microbiological, or radiographic) when euthanized at the 8-week study endpoint. ABVF sites did exhibit fibrous encapsulation around the implant at 8 weeks. Local antibiotic release from ABVF to orthopedic sites requiring bone void fillers eliminated the periprosthetic bacterial challenge in this 8-week in vivo study, confirming previous in vitro results.

| S-EPMC4376868 | biostudies-literature

Preparation and Characterization of Polymer Composite Materials Based on PLA/TiO₂ for Antibacterial Packaging.

Project description:Polymer composite materials based on polylactic acid (PLA) filled with titanium dioxide (TiO₂) nanoparticles were prepared. The aim of this work was to investigate the antibacterial action of TiO₂ against a strain of E. coli (DH5α) to obtain information on their potential uses in food and agro-alimentary industry. PLA/TiO₂ systems were prepared by a two-step process: Solvent casting followed by a hot-pressing step. Characterization was done as a function of particle size (21 nm and <100 nm) and particle content (0%, 1%, 5%, 10%, and 20%, wt %). Structural characterization carried out by X-ray diffraction (XRD) and Fourier Transformed Infrared spectroscopy (FTIR) did not reveal significant changes in polymer structure due to the presence of TiO₂ nanoparticles. Thermal characterization indicated that thermal transitions, measured by differential scanning calorimetry (DSC), did not vary, irrespective of size or content, whereas thermogravimetric analysis (TGA) revealed a slight increase in the temperature of degradation with particle content. Bacterial growth and biofilm formation on the surface of the composites against DH5α Escherichia coli was studied. Results suggested that the presence of TiO₂ nanoparticles decreases the amount of extracellular polymeric substance (EPS) and limits bacterial growth. The inhibition distances estimated with the Kirby-Bauer were doubled when 1% TiO₂ nanoparticles were introduced in PLA, though no significant differences were obtained for higher contents in TiO₂ NPs.

| S-EPMC6401929 | biostudies-literature

Piezoelectric nanofiber/polymer composite membrane for noise harvesting and active acoustic wave detection.

Project description:Being one of the most common forms of energy existing in the ambient environment, acoustic waves have a great potential to be an energy source. However, the effective energy conversion of an acoustic wave is a great challenge due to its low energy density and broad bandwidth. In this work, we developed a new piezoelectric nanogenerator (PENG), which is mainly composed of a piece of piezoelectric nanofiber/polymer composite membrane. As an energy harvester, the PENG can effectively scavenge a broad low-frequency (from 50 Hz to 400 Hz) acoustic energy from the ambient environment, and it can even scavenge a very weak acoustic energy with a minimum pressure of only 0.18 Pa. When a drum was used as an excitation source, the maximum open-circuit voltage and short-circuit current density of the PENG reached 1.8 V and 1.67 mA m-2, respectively. In addition, the PENG had a good stability and its output frequency and amplitude were closely related to the driving sound wave, which made the PENG capable of detecting acoustic signals in the living environment and have the potential to be applied as a self-powered active acoustic detector.

| S-EPMC9416852 | biostudies-literature

Polydimethylsiloxane/Nanodiamond Composite Sponge for Enhanced Mechanical or Wettability Performance.

Project description:Polydimethylsiloxane (PDMS) is widely utilized in material science, chemical engineering, and environmental science due to its excellent properties. By utilizing fillers, so-called composite materials can be obtained with enhanced mechanical, wettability, or thermal conductivity performance. Here, we present a simple, cost-effective approach to vary either the mechanical properties (Young's modulus) or surface wettability of bulk PDMS and PDMS sponges simply by adding nanodiamond filler with different surface terminations, either oxidized (oND) or hydrogenated (reduced, rND) nanodiamond. Minuscule amounts of oxidized nanodiamond particles as filler showed to benefit the compressive Young's modulus of composite sponges with up to a 52% increase in its value, while the wettability of composite sponges was unaffected. In contrast, adding reduced nanodiamond particles to PDMS yielded inclined water contact angles on the PDMS/nanodiamond composite sponges. Finally, we show that the PDMS/rND composites are readily utilized as an absorbent for oil/water separation problems. This signifies that the surface termination of the ND particle has a crucial effect on the performance of the composite.

| S-EPMC6631953 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data