Impact of Annealing Temperature on the Morphological, Optical and Photoelectrochemical Properties of Cauliflower-like CdSe0.6Te0.4 Photoelectrodes; Enhanced Solar Cell Performance.

ABSTRACT: We are reporting on the impact of air annealing temperatures on the physicochemical properties of electrochemically synthesized cadmium selenium telluride (CdSe0.6Te0.4) samples for their application in a photoelectrochemical (PEC) solar cell. The CdSe0.6Te0.4 samples were characterized with several sophisticated techniques to understand their characteristic properties. The XRD results presented the pure phase formation of the ternary CdSe0.6Te0.4 nanocompound with a hexagonal crystal structure, indicating that the annealing temperature influences the XRD peak intensity. The XPS study confirmed the existence of Cd, Se, and Te elements, indicating the formation of ternary CdSe0.6Te0.4 compounds. The FE-SEM results showed that the morphological engineering of the CdSe0.6Te0.4 samples can be achieved simply by changing the annealing temperatures from 300 to 400 °C with intervals of 50 °C. The efficiencies (ƞ) of the CdSe0.6Te0.4 photoelectrodes were found to be 2.0% for the non-annealed and 3.1, 3.6, and 2.5% for the annealed at 300, 350, and 400 °C, respectively. Most interestingly, the PEC cell analysis indicated that the annealing temperatures played an important role in boosting the performance of the photoelectrochemical properties of the solar cells.

SUBMITTER: Ghodake GS

PROVIDER: S-EPMC8583999 | biostudies-literature | 2021 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Impact of Annealing Temperature on the Morphological, Optical and Photoelectrochemical Properties of Cauliflower-like CdSe0.6Te0.4 Photoelectrodes; Enhanced Solar Cell Performance.

Ghodake Gajanan S GS Kim Dae-Young DY Shinde Surendra K SK Dubal Deepak P DP Yadav Hemraj M HM Magotra Verjesh Kumar VK

International journal of molecular sciences 20211027 21

We are reporting on the impact of air annealing temperatures on the physicochemical properties of electrochemically synthesized cadmium selenium telluride (CdSe0.6Te0.4) samples for their application in a photoelectrochemical (PEC) solar cell. The CdSe0.6Te0.4 samples were characterized with several sophisticated techniques to understand their characteristic properties. The XRD results presented the pure phase formation of the ternary CdSe0.6</sub ...[more]

PMID: 34769039

Similar Datasets

Project description:One of the emerging and environmentally friendly technologies is the photoelectrochemical generation of green hydrogen; however, the cheap cost of production and the need for customizing photoelectrode properties are thought to be the main obstacles to the widespread adoption of this technology. The primary players in hydrogen production by photoelectrochemical (PEC) water splitting, which is becoming more common on a worldwide basis, are solar renewable energy and widely available metal oxide based PEC electrodes. This study attempts to prepare nanoparticulate and nanorod-arrayed films to better understand how nanomorphology can impact structural, optical, and PEC hydrogen production efficiency, as well as electrode stability. Chemical bath deposition (CBD) and spray pyrolysis are used to create ZnO nanostructured photoelectrodes. Various characterization methods are used to investigate morphologies, structures, elemental analysis, and optical characteristics. The crystallite size of the wurtzite hexagonal nanorod arrayed film was 100.8 nm for the (002) orientation, while the crystallite size of nanoparticulate ZnO was 42.1 nm for the favored (101) orientation. The lowest dislocation values for (101) nanoparticulate orientation and (002) nanorod orientation are 5.6 × 10-4 and 1.0 × 10-4 dislocation/nm2, respectively. By changing the surface morphology from nanoparticulate to hexagonal nanorod arrangement, the band gap is decreased to 2.99 eV. Under white and monochromatic light irradiation, the PEC generation of H2 is investigated using the proposed photoelectrodes. The solar-to-hydrogen conversion rate of ZnO nanorod-arrayed electrodes was 3.72% and 3.12%, respectively, under 390 and 405 nm monochromatic light, which is higher than previously reported values for other ZnO nanostructures. The output H2 generation rates for white light and 390 nm monochromatic illuminations were 28.43 and 26.11 mmol.h-1cm-2, respectively. The nanorod-arrayed photoelectrode retains 96.6% of its original photocurrent after 10 reusability cycles, compared to 87.4% for the nanoparticulate ZnO photoelectrode. The computation of conversion efficiencies, H2 output rates, Tafel slope, and corrosion current, as well as the application of low-cost design methods for the photoelectrodes, show how the nanorod-arrayed morphology offers low-cost, high-quality PEC performance and durability.

Dataset Information

Impact of Annealing Temperature on the Morphological, Optical and Photoelectrochemical Properties of Cauliflower-like CdSe0.6Te0.4 Photoelectrodes; Enhanced Solar Cell Performance.

Publications

Impact of Annealing Temperature on the Morphological, Optical and Photoelectrochemical Properties of Cauliflower-like CdSe<sub>0.6</sub>Te<sub>0.4</sub> Photoelectrodes; Enhanced Solar Cell Performance.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets