Sustainable UV-Crosslinkable Acrylic Pressure-Sensitive Adhesives for Medical Application.

ABSTRACT: This study aimed to investigate the potential of photoreactive acrylate patches as systems for transdermal drug delivery, in particular, using more renewable alternatives and more environmentally friendly synthesis routes of transdermal patches. Therefore, the aim of this study was to develop a transdermal patch containing ibuprofen and investigate its performance in vitro through the pigskin. Transparent patches were prepared using four acrylate copolymers with an incorporated photoinitiator. Two types of transdermal patches based on the photocrosslinking acrylic prepolymers with isobornyl methacrylate as biocomponent and monomer increasing Tg ("hard") were manufactured. The obtained patches were characterized for their adhesive properties and tested for permeability of the active substance. It turns out that patches whose adhesive matrix is photoreactive polyacrylate copolymers have a higher cohesion than patches from commercial adhesives, while the modification of the copolymers with isobornyl methacrylate resulted in an improvement in adhesion and tack. This study demonstrates the feasibility of developing photoreactive acrylic-based transdermal patches that contain biocomponents that can deliver a therapeutically relevant dose of ibuprofen.

SUBMITTER: Ossowicz-Rupniewska P

PROVIDER: S-EPMC8584108 | biostudies-literature | 2021 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Sustainable UV-Crosslinkable Acrylic Pressure-Sensitive Adhesives for Medical Application.

Ossowicz-Rupniewska Paula P Bednarczyk Paulina P Nowak Małgorzata M Nowak Anna A Duchnik Wiktoria W Kucharski Łukasz Ł Rokicka Joanna J Klimowicz Adam A Czech Zbigniew Z

International journal of molecular sciences 20211031 21

This study aimed to investigate the potential of photoreactive acrylate patches as systems for transdermal drug delivery, in particular, using more renewable alternatives and more environmentally friendly synthesis routes of transdermal patches. Therefore, the aim of this study was to develop a transdermal patch containing ibuprofen and investigate its performance in vitro through the pigskin. Transparent patches were prepared using four acrylate copolymers with an incorporated photoinitiator. T ...[more]

PMID: 34769271

Similar Datasets

Project description:Pressure-sensitive adhesives (PSAs) are usually made from viscoelastic, high-molecular-weight copolymers, which are fine-tuned by adjusting the comonomer ratios, molecular weights, and cross-link densities to optimize the adhesion properties for the desired end-use. To create a lightly cross-linked network, an ultraviolet (UV) photoinitiator can be incorporated. Here, we present the first use of perfluorophenylazide chemistry to control precisely a polyacrylate network for application as a PSA. Upon UV irradiation, the highly reactive nitrene from the azide moiety reacts with nearby molecules through a C-H insertion reaction, resulting in cross-linking via covalent bonding. This approach offers three benefits: (1) a means to optimize adhesive properties without the addition of an external photoinitiator; (2) the ability to switch off the tack adhesion on demand via a high cross-linking density; and (3) a platform for additional chemical modification. A series of poly(n-butyl acrylate-co-2,3,4,5,6-pentafluorobenzyl acrylate) or poly(PFBA-co-BA) copolymers were synthesized and modified post-polymerization into the photo-reactive poly(n-butyl acrylate-co-4-azido-2,3,5,6-tetrafluorobenzyl acrylate) [azide-modified poly(PFBA-co-BA)] with various molar contents. When cast into films, the azide-modified copolymers with a high azide content achieved a very high shear resistance after UV irradiation, whereas the tack and peel adhesion decreased strongly with the increase in azide content, indicating that excessive cross-linking occurred. These materials are thus photo-switchable. However, in the low range of azide content, an optimum probe tack adhesion energy was obtained in films with a 0.3 mol % azide content, where a long stress plateau (indicating good fibrillation) with a high plateau stress was observed. An optimum peel adhesion strength was achieved with 0.5 mol % azide. Thus, the adhesion was finely controlled by the degree of cross-linking of the PSA, as determined by the azide content of the copolymer chain. Finally, as a demonstration of the versatility and advantages of the material platform, we show an azide-aldehyde-amine multicomponent modification of the azide copolymer to make a dye-functionalized film that retains its adhesive properties. This first demonstration of using azide functionality has enormous potential for functional PSA design.

Dataset Information

Sustainable UV-Crosslinkable Acrylic Pressure-Sensitive Adhesives for Medical Application.

Publications

Sustainable UV-Crosslinkable Acrylic Pressure-Sensitive Adhesives for Medical Application.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets