Investigation of Er3+ Ions Reinforced Zinc-Phosphate Glasses for Ionizing Radiation Shielding Applications.

ABSTRACT: Melt quenching technique is used for preparing glasses with chemical formula (70P2O5)-(16 - x)CdO-(14ZnO)-(xEr2O3), (x = 1-6 mol%). These glasses were named Er1, Er2, Er3, Er4, Er5, and Er6, respectively. Photon buildup factors, fast neutron absorption, and electron stopping of the prepared glasses were examined. Glasses' density was varied from 3.390 ± 0.003 for the Er1 glass sample to 3.412 ± 0.003 for the Er6 glass sample. The Buildup factor (BUF) spectra have relatively higher values in the Compton Scattering (CS) dominated areas compared to both Photoelectric effect (PE), and Pair Production (PP) dominated energy regions. The highest BUF appeared at the Er atom K-absorption edge, whose intensity increases as the molar concentration of Er2O3 in the glasses increases. The photon absorption efficiency (PAE) of the glasses increases according to the trend (PAE)Er1 < (PAE)Er2 < (PAE)Er3 < (PAE)Er4 < (PAE)Er5 < (PAE)Er6. Fast neutron removal cross-section, FNRC (ΣR) values of the glasses obtained via calculation varied from 0.1045-0.1039 cm-1 for Er1-Er6. Furthermore, the continuous slowing down approximation mode (CSDA) range enhances the kinetic energy of electrons for all glasses. Generally, results revealed that the investigated glasses could be applied for radiation shielding and dosimetric media.

SUBMITTER: Zakaly HMH

PROVIDER: S-EPMC8618482 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Investigation of Er3+ Ions Reinforced Zinc-Phosphate Glasses for Ionizing Radiation Shielding Applications.

Zakaly Hesham M H HMH Ene Antoaneta A Olarinoye Oyeleke I OI Marzouk Samir Y SY Abdel-Hafez Shams H SH Shams Mohamed S MS Rammah Yasser S YS

Materials (Basel, Switzerland) 20211110 22

Melt quenching technique is used for preparing glasses with chemical formula (70P2O5)-(16 - x)CdO-(14ZnO)-(xEr2O3), (x = 1-6 mol%). These glasses were named Er1, Er2, Er3, Er4, Er5, and Er6, respectively. Photon buildup factors, fast neutron absorption, and electron stopping of the prepared glasses were examined. Glasses' density was varied from 3.390 ± 0.003 for the Er1 glass sample to 3.412 ± 0.003 for the Er6 glass sample. The Buildup factor (BUF) s ...[more]

PMID: 34832170

Similar Datasets

Project description:Glass and ceramic materials doped with rare earth (RE) ions have gained wide interest in photonics as active materials for lasers, optical amplifiers, and luminescent sensors. The emission properties of RE-doped glasses depend on their chemical composition, but they can also be tailored by modifying the surrounding active ions. Typically, this is achieved through heat treatment (including continuous-wave and pulsed lasers) after establishing the ordering mechanisms in the particular glass-RE system. Within the known systems, silicate glasses predominate, while much less work relates to materials with lower energy phonons, which allow more efficient radiation sources to be constructed for photonic applications. In the present work, the luminescent and structural properties of germanate glasses modified with phosphate oxide doped with Eu3+ ions were investigated. Europium dopant was used as a "spectroscopic probe" in order to analyze the luminescence spectra, which characterizes the changes in the local site symmetries of Eu3+ ions. Based on the spectroscopic results, a strong influence of P2O5 content was observed on the excitation and luminescence spectra. The luminescence study of the most intense 5D0→7F2 (electric dipole) transition revealed that the increase in the P2O5 content leads to the linewidth reduction (from 15 nm to 10 nm) and the blue shift (~2 nm) of the emission peak. According to the crystal field theory, the introduction of P2O5 into the glass structure changes the splitting number of sublevels of the 5D0→7F1 (magnetic dipole) transition, confirming the higher polymerization of fabricated glass. The slightly different local environment of Eu3+ centers the results in a number of sites and causes inhomogeneous broadening of spectral lines. It was found that the local asymmetry ratio estimated by the relation of (5D0→7F2)/(5D0→7F1) transitions also confirms greater changes in local symmetry around Eu3+ ions. Our results indicate that modification of germanate glass by P2O5 allows control of their structural properties in order to functionalize the emissions for application as luminescent light sources and sensors.

Dataset Information

Investigation of Er3+ Ions Reinforced Zinc-Phosphate Glasses for Ionizing Radiation Shielding Applications.

Publications

Investigation of Er<sup>3+</sup> Ions Reinforced Zinc-Phosphate Glasses for Ionizing Radiation Shielding Applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets