High-Temperature Nanoindentation of an Advanced Nano-Crystalline W/Cu Composite.

ABSTRACT: The applicability of nano-crystalline W/Cu composites is governed by their mechanical properties and microstructural stability at high temperatures. Therefore, mechanical and structural investigations of a high-pressure torsion deformed W/Cu nanocomposite were performed up to a temperature of 600 °C. Furthermore, the material was annealed at several temperatures for 1 h within a high-vacuum furnace to determine microstructural changes and surface effects. No significant increase of grain size, but distinct evaporation of the Cu phase accompanied by Cu pool and faceted Cu particle formation could be identified on the specimen's surface. Additionally, high-temperature nanoindentation and strain rate jump tests were performed to investigate the materials mechanical response at elevated temperatures. Hardness and Young's modulus decrease were noteworthy due to temperature-induced effects and slight grain growth. The strain rate sensitivity in dependent of the temperature remained constant for the investigated W/Cu composite material. Also, the activation volume of the nano-crystalline composite increased with temperature and behaved similar to coarse-grained W. The current study extends the understanding of the high-temperature behavior of nano-crystalline W/Cu composites within vacuum environments such as future fusion reactors.

SUBMITTER: Burtscher M

PROVIDER: S-EPMC8618606 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

High-Temperature Nanoindentation of an Advanced Nano-Crystalline W/Cu Composite.

Burtscher Michael M Zhao Mingyue M Kappacher Johann J Leitner Alexander A Wurmshuber Michael M Pfeifenberger Manuel M Maier-Kiener Verena V Kiener Daniel D

Nanomaterials (Basel, Switzerland) 20211103 11

The applicability of nano-crystalline W/Cu composites is governed by their mechanical properties and microstructural stability at high temperatures. Therefore, mechanical and structural investigations of a high-pressure torsion deformed W/Cu nanocomposite were performed up to a temperature of 600 °C. Furthermore, the material was annealed at several temperatures for 1 h within a high-vacuum furnace to determine microstructural changes and surface effects. No significant increase of grain size, b ...[more]

PMID: 34835714

Similar Datasets

Project description:Mudstones and shales serve as natural barrier rocks in various geoenergy applications. Although many studies have investigated their mechanical properties, characterizing these parameters at the microscale remains challenging due to their fine-grained nature and susceptibility to microstructural damage introduced during sample preparation. This study aims to investigate the micromechanical properties of clay matrix composite in mudstones by combining high-speed nanoindentation mapping and machine learning data analysis. The nanoindentation approach effectively captured the heterogeneity in high-resolution mechanical property maps. Utilizing machine learning-based k-means clustering, the mechanical characteristics of matrix clay, brittle minerals, as well as measurements on grain boundaries and structural discontinuities (e.g., cracks) were successfully distinguished. The classification results were validated through correlation with broad ion beam-scanning electron microscopy images. The resulting average reduced elastic modulus (E r ) and hardness (H) values for the clay matrix were determined to be 16.2 ± 6.2 and 0.5 ± 0.5 GPa, respectively, showing consistency across different test settings and indenter tips. Furthermore, the sensitivity of indentation measurements to various factors was investigated, revealing limited sensitivity to indentation depth and tip geometry (when comparing Cube corner and Berkovich tip in a small range of indentation depth variations), but decreased stability at lower loading rates. Box counting and bootstrapping methods were applied to assess the representativeness of parameters determined for the clay matrix. A relatively small dataset (indentation number = 60) is needed to achieve representativeness, while the main challenges is to cover a representative mapping area for clay matrix characterization. Overall, this study demonstrates the feasibility of high-speed nanoindentation mapping combined with data analysis for micromechanical characterization of the clay matrix in mudstones, paving the way for efficient analysis of similar fine-grained sedimentary rocks.Supplementary informationThe online version contains supplementary material available at 10.1007/s40948-024-00864-9.

Project description:The chemical and isotopic signatures of moderately volatile elements are useful for understanding processes of volatile depletion in planetary formation and differentiation. However, the fractionation factors between gas and melt phases during evaporation that are required to model these planetary volatile depletion processes are still sparse. In this study, twenty heating experiments were conducted in 1 atm gas-mixing furnaces to constrain the behavior of K, Cu, and Zn evaporation and isotopic fractionation from basaltic melts at high temperatures. The temperatures range from 1300 °C to 1400 °C, and durations are from 2 to 8 days. Oxygen fugacities (fO2) range from one log unit below to ten log units above that of the iron-wüstite buffer (IW-1 to IW+10, corresponding to logfO2 of -10.7 to -0.68 at 1400 °C). The conditions were selected to achieve an evaporation-dominated regime (where timescales of diffusion << evaporation for trace elements) in order to avoid diffusion-limited evaporation. Our results show during evaporation Zn behaved as the most volatile, followed by Cu and then K, regardless of temperature and oxygen fugacity. Partitioning of Zn into spinel layers within experimental capsules, however, has been observed, which has substantial effects on the Zn isotope fractionation factor. Therefore, Zn results are presented but further discussion is excluded. Element loss depends on both temperature and oxygen fugacity, where higher temperatures and lower oxygen fugacities promote evaporation. However, with varying temperature and oxygen fugacity, the kinetic isotopic fractionation factors, α (where, RR0=fα-1 ), for K and Cu remain constant, thus these factors can be applied to a wider range of conditions than those in this study. The experimentally determined fractionation factors for K, and Cu during evaporation from basaltic melts are 0.9944, and 0.9961, respectively. The fractionation factors for these elements with varying volatilities are all significantly larger than the "apparent observed fractionation factors," which approach one and are inferred from lunar basalts relative to the Bulk Silicate Earth. This observation suggests near-equilibrium conditions during volatile-element loss from the Moon as the "apparent observed fractionation factors" of lunar basalts are similar for all three elements.

Dataset Information

High-Temperature Nanoindentation of an Advanced Nano-Crystalline W/Cu Composite.

Publications

High-Temperature Nanoindentation of an Advanced Nano-Crystalline W/Cu Composite.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets