Optimization of Printing Parameters for Digital Light Processing 3D Printing of Hollow Microneedle Arrays.

ABSTRACT: 3D printing is an emerging technology aiming towards personalized drug delivery, among many other applications. Microneedles (MN) are a viable method for transdermal drug delivery that is becoming more popular for delivery through the skin. However, there is a need for a faster fabrication process with potential for easily exploring different geometries of MNs. In the current study, a digital light processing (DLP) method of 3D printing for fabrication of hollow MN arrays using commercial UV curable resin was proposed. Print quality was optimised by assessing the effect of print angle on needle geometries. Mechanical testing of MN arrays was conducted using a texture analyser. Angled prints were found to produce prints with geometries closer to the CAD designs. Curing times were found to affect the mechanical strength of MNs, with arrays not breaking when subjected to 300 N of force but were bent. Overall, DLP process produced hollow MNs with good mechanical strength and depicts a viable, quick, and efficient method for the fabrication of hollow MN arrays.

SUBMITTER: Mathew E

PROVIDER: S-EPMC8622592 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Optimization of Printing Parameters for Digital Light Processing 3D Printing of Hollow Microneedle Arrays.

Mathew Essyrose E Pitzanti Giulia G Gomes Dos Santos Ana L AL Lamprou Dimitrios A DA

Pharmaceutics 20211102 11

3D printing is an emerging technology aiming towards personalized drug delivery, among many other applications. Microneedles (MN) are a viable method for transdermal drug delivery that is becoming more popular for delivery through the skin. However, there is a need for a faster fabrication process with potential for easily exploring different geometries of MNs. In the current study, a digital light processing (DLP) method of 3D printing for fabrication of hollow MN arrays using commercial UV cur ...[more]

PMID: 34834250

Similar Datasets

Project description:Digital light processing (DLP) 3D printing has shown great advantages such as high resolution in the fabrication of 3D objects toward a range of applications. Despite the rapid development of photocurable materials for DLP printing, tailoring properties to meet the specific demands for various applications remains challenging. Herein, we introduce copolymers of caprolactone and allyl caprolactone offering built-in functionality for thiol-ene photochemistry, thereby omitting the need for postfunctionalization. A crystalline block copolymer and an amorphous statistical copolymer were synthesized with the same comonomer composition and molecular weight. Thio-ene photocuring with a tetrafunctional thiol cross-linker was studied at different thiol to double-bond ratios for the copolymers and their blends. All formulations undergo rapid photocuring within several seconds of irradiation with slightly higher gel fractions observed for the statistical copolymer over the block copolymer under the same conditions, suggesting a somewhat higher cross-link density. Thermal properties of the networks were dependent on the presence of the semicrystalline block copolymer, where higher melting enthalpies were reached at higher block copolymer content. Similarly, crystallinity was found to be the main contributor to the mechanical properties. For a comparable composition, the modulus of a block copolymer network was found to be 31 times higher than that of the statistical copolymer network (27.7 vs 0.89 MPa). Intermediate moduli could be obtained by blending the two copolymers. DLP-printed scaffolds from these copolymers retained their thermal properties, therefore offering an efficient approach to tailoring mechanical properties, through crystallinity. Moreover, the printed scaffold displayed shape memory properties as the first example of poly(carprolactone) (PCL) copolymers in DLP printing. These materials are readily synthesized, offer fast and high-resolution 3D printing, and are degradable and cell compatible. They offer a straightforward approach to tailoring properties of PCL-based biomaterials and devices.

Project description:Biofabrication allows for the templating of structural features in materials on cellularly-relevant size scales, enabling the generation of tissue-like structures with controlled form and function. This is particularly relevant for growing organoids, where the application of biochemical and biomechanical stimuli can be used to guide the assembly and differentiation of stem cells and form architectures similar to the parent tissue or organ. Recently, ablative laser-scanning techniques was used to create 3D overhang features in collagen hydrogels at size scales of 10-100µm and supported the crypt-villus architecture in intestinal organoids. As a complementary method, providing advantages for high-throughput patterning, we printed thioester functionalized poly(ethylene glycol) (PEG) elastomers using digital light processing (DLP) and created sacrificial, 3D shapes that could be molded into soft (G' < 1000 Pa) hydrogel substrates. Specifically, three-arm 1.3 kDa PEG thiol and three-arm 1.6 kDa PEG norbornene, containing internal thioester groups, were photopolymerized to yield degradable elastomers. When incubated in a solution of 300 mM 2-mercaptoethanol (pH 9.0), 1 mm thick 10 mm diameter elastomer discs degraded in <2 h. Using DLP, arrays of features with critical dimensions of 37 ± 4µm, resolutions of 22 ± 5µm, and overhang structures as small as 50µm, were printed on the order of minutes. These sacrificial thioester molds with physiologically relevant features were cast-molded into Matrigel and subsequently degraded to create patterned void spaces with high fidelity. Intestinal stem cells (ISCs) cultured on the patterned Matrigel matrices formed confluent monolayers that conformed to the underlying pattern. DLP printed sacrificial thioester elastomer constructs provide a robust and rapid method to fabricate arrays of 3D organoid-sized features in soft tissue culture substrates and should enable investigations into the effect of epithelial geometry and spacing on the growth and differentiation of ISCs.

Dataset Information

Optimization of Printing Parameters for Digital Light Processing 3D Printing of Hollow Microneedle Arrays.

Publications

Optimization of Printing Parameters for Digital Light Processing 3D Printing of Hollow Microneedle Arrays.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets