Adsorption enhancement of nitrogen gas by atomically heterogeneous nanospace of boron nitride.

ABSTRACT: In this study, porous boron nitride (p-BN) with hexagonal phase boron nitride (h-BN) pore walls was synthesized using high-temperature calcination. Negligible variation in pore-wall structure can be observed in powder X-ray diffraction (XRD) profiles and infrared (IR) spectra. However, a highly stable p-BN with a stable pore structure even at 973 K under the oxidative conditions is obtained when synthesized at higher than 1573 K under nitrogen gas flow. For p-BN, this stability is obtained by generating h-BN microcrystals. Nitrogen adsorption-desorption isotherms at 77 K provide type-IV features and typical adsorption-desorption hysteresis, which suggests micropore and mesopore formation. Moreover, adsorption-desorption isotherms of Ar at 87 K are measured and compared with those of nitrog