Preparation and Application of Nb2O5 Nanofibers in CO2 Photoconversion.

ABSTRACT: Increasing global warming due to NOx, CO2, and CH4, is significantly harming ecosystems and life worldwide. One promising methodology is converting pollutants into valuable chemicals via photocatalytic processes (by reusable photocatalysts). In this context, the present work aimed to produce a Nb2O5 photocatalyst nanofiber system by electrospinning to convert CO2. Based on the collected data, the calcination at 600 ∘C for 2 h resulted in the best condition to obtain nanofibers with homogeneous surfaces and an average diameter of 84 nm. As a result, the Nb2O5 nanofibers converted CO2 mostly into CO and CH4, reaching values around 8.5 μmol g-1 and 0.55 μmol g-1, respectively.

SUBMITTER: Prado ACF

PROVIDER: S-EPMC8704612 | biostudies-literature | 2021 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Preparation and Application of Nb2O5 Nanofibers in CO2 Photoconversion.

Prado A C F ACF Malafatti J O D JOD Oliveira J A JA Ribeiro C C Joya M R MR Luz A P AP Paris E C EC

Nanomaterials (Basel, Switzerland) 20211201 12

Increasing global warming due to NOx, CO2, and CH4, is significantly harming ecosystems and life worldwide. One promising methodology is converting pollutants into valuable chemicals via photocatalytic processes (by reusable photocatalysts). In this context, the present work aimed to produce a Nb2O5 photocatalyst nanofiber system by electrospinning to convert CO2. Based on the collected data, the calcination at 600 ∘C for 2 h resulted in the best condition to obtain nanofibers with homogeneous s ...[more]

PMID: 34947617

Similar Datasets

The preparation of liquefied bio-stalk carbon nanofibers and their application in supercapacitors.

Project description:Carbon nanofibers (CNFs) have been widely used in electrochemical energy storage devices because of their excellent conductivity, extremely large surface area and structural stability. Herein, we obtained a viscous, liquefied bio-stalk carbon via the simple chemical treatment of biomass, and mixed it with polyacrylonitrile to prepare a spinning solution. Subsequent electrospinning and high temperature activation resulted in the successful preparation of liquefied lignin-based activated carbon nanofibers. The as-prepared liquefied bio-stalk carbon nanofibers exhibited an outstanding electrochemical performance (specific capacitance of 273 F g-1 at 0.5 A g-1 current density), and a capacitance retention of 210 F g-1 even under a large current density of 10 A g-1. Besides its high specific capacitance and outstanding rate capability, the symmetrical supercapacitor cell based on the liquefied carbon-based nanofiber electrodes also exhibited an excellent cycling performance with 92.76% capacitance retention after 5000 charge-discharge cycles. This study provides a new strategy for the future development of supercapacitor electrode materials and enhances the development of biomass energy.

| S-EPMC9067254 | biostudies-literature

Preparation of Polypropylene Micro and Nanofibers by Electrostatic-Assisted Melt Blown and Their Application.

Project description:In this paper, a novel electrostatic-assisted melt blown process was reported to produce polypropylene (PP) microfibers with a diameter as fine as 600 nm. The morphology, web structure, pore size distribution, filtration efficiency, and the stress and strain behavior of the PP nonwoven fabric thus prepared were characterized. By introducing an electrostatic field into the conventional melt-blown apparatus, the average diameter of the melt-blown fibers was reduced from 1.69 to 0.96 μm with the experimental setup, and the distribution of fiber diameters was narrower, which resulted in a filter medium with smaller average pore size and improved filtration efficiency. The polymer microfibers prepared by this electrostatic-assisted melt blown method may be adapted in a continuous melt blown process for the production of filtration media used in air filters, dust masks, and so on.

| S-EPMC6403903 | biostudies-literature

Preparation of Amidoxime Polyacrylonitrile Chelating Nanofibers and Their Application for Adsorption of Metal Ions.

Project description:Polyacrylonitrile (PAN) nanofibers were prepared by electrospinning and they were modified with hydroxylamine to synthesize amidoxime polyacrylonitrile (AOPAN) chelating nanofibers, which were applied to adsorb copper and iron ions. The conversion of the nitrile group in PAN was calculated by the gravimetric method. The structure and surface morphology of the AOPAN nanofiber were characterized by a Fourier transform infrared spectrometer (FT-IR) and a scanning electron microscope (SEM), respectively. The adsorption abilities of Cu2+ and Fe3+ ions onto the AOPAN nanofiber mats were evaluated. FT-IR spectra showed nitrile groups in the PAN were partly converted into amidoxime groups. SEM examination demonstrated that there were no serious cracks or sign of degradation on the surface of the PAN nanofibers after chemical modification. The adsorption capacities of both copper and iron ions onto the AOPAN nanofiber mats were higher than those into the raw PAN nanofiber mats. The adsorption data of Cu2+ and Fe3+ ions fitted particularly well with the Langmuir isotherm. The maximal adsorption capacities of Cu2+ and Fe3+ ions were 215.18 and 221.37 mg/g, respectively.

| S-EPMC5512958 | biostudies-other

Preparation of Chitin Nanofibers from Mushrooms.

Project description:Chitin nanofibers were isolated from the cell walls of five different types of mushrooms by the removal of glucans, minerals, and proteins, followed by a simple grinding treatment under acidic conditions. The Chitin nanofibers thus obtained have a uniform structure and a long fiber length. The width of the nanofibers depended on the type of mushrooms and varied in the range 20 to 28 nm. The Chitin nanofibers were characterized by elemental analyses, FT-IR spectra, and X-ray diffraction profiles. The results showed that the α-chitin crystal structure was maintained and glucans remained on the nanofiber surface.

| S-EPMC5448680 | biostudies-other

Single-crystalline nanoporous Nb2O5 nanotubes.

Project description:Single-crystalline nanoporous Nb2O5 nanotubes were fabricated by a two-step solution route, the growth of uniform single-crystalline Nb2O5 nanorods and the following ion-assisted selective dissolution along the [001] direction. Nb2O5 tubular structure was created by preferentially etching (001) crystallographic planes, which has a nearly homogeneous diameter and length. Dense nanopores with the diameters of several nanometers were created on the shell of Nb2O5 tubular structures, which can also retain the crystallographic orientation of Nb2O5 precursor nanorods. The present chemical etching strategy is versatile and can be extended to different-sized nanorod precursors. Furthermore, these as-obtained nanorod precursors and nanotube products can also be used as template for the fabrication of 1 D nanostructured niobates, such as LiNbO3, NaNbO3, and KNbO3.

| S-EPMC3211185 | biostudies-literature

Nanoarchitectured Nb2O5 hollow, Nb2O5@carbon and NbO2@carbon Core-Shell Microspheres for Ultrahigh-Rate Intercalation Pseudocapacitors.

Project description:Li-ion intercalation materials with extremely high rate capability will blur the distinction between batteries and supercapacitors. We construct a series of nanoarchitectured intercalation materials including orthorhombic (o-) Nb2O5 hollow microspheres, o-Nb2O5@carbon core-shell microspheres and tetragonal (t-) NbO2@carbon core-shell microspheres, through a one-pot hydrothermal method with different post-treatments. These nanoarchitectured materials consist of small nanocrystals with highly exposed active surface, and all of them demonstrate good Li(+) intercalation pseudocapacitive properties. In particular, o-Nb2O5 hollow microspheres can deliver the specific capacitance of 488.3 F g(-1), and good rate performance of 126.7 F g(-1) at 50 A g(-1). The o-Nb2O5@carbon core-shell microspheres show enhanced specific capacitance of 502.2 F g(-1) and much improved rate performance (213.4 F g(-1) at 50 A g(-1)). Furthermore, we demonstrate for the first time, t-NbO2 exhibits much higher rate capability than o-Nb2O5. For discharging time as fast as 5.9 s (50 A g(-1)), it still exhibits a very high specific capacitance of 245.8 F g(-1), which is 65.2% retention of the initial capacitance (377.0 F g(-1) at 1 A g(-1)). The unprecedented rate capability is an intrinsic feature of t-NbO2, which may be due to the conductive lithiated compounds.

| S-EPMC4754730 | biostudies-literature

Photoconversion of MC38

Project description:MC38 tumors were photoconverted in Kade mice to assess the effect of photo conversion on the transcriptome

2022-04-08 | GSE193654 | GEO

TEPA impregnation of electrospun carbon nanofibers for enhanced low-level CO2 adsorption.

Project description:The CO2 adsorption selectivity of plain activated carbon nanofibers (ANF) is generally low. For enhancement, nitrogen functionalities favorable for CO2 adsorption are usually tethered to the ANF. In the current study, we adopted chemical impregnation using 0.5 wt% tetraethylenepentamine (TEPA) solution as an impregnant. To enhance the impregnation of TEPA further, preliminary oxidation of the nanofibers with 70% HNO3 was conducted. The effects of HNO3 and TEPA treatments on the modified ANFs were investigated for physical (using N2 monosorb, thermogravimetric analyzer, scanning electron microscopy) and chemical (X-ray photoelectron spectrometer) changes. From the results, we found that although TEPA impregnation reduced the specific surface area and pore volume of the ANFs (from 673.7 and 15.61 to 278.8 m2/g and 0.284 cm3/g, respectively), whereas the HNO3 pre-oxidation increased the number of carboxylic groups on the ANF. Upon TEPA loading, pyridinic nitrogen was tethered and further enhanced by pre-oxidation. The surface treatment cumulatively increased the amine content from 5.81% to 13.31%. Consequently, the final adsorption capacity for low (0.3%) and pure CO2 levels were enhanced from 0.20 and 1.89 to 0.33 and 2.96 mmol/g, respectively. Hence, the two-step pre-oxidation and TEPA treatments were efficient for improved CO2 affinity.

| S-EPMC7024689 | biostudies-literature

Carbon Nanotube-Incorporated Nanofibers for Immunosensor Preparation against CD36

Project description:The increased serum concentration of CD36 is significantly

| S-EPMC9933220 | biostudies-literature

Preparation of Perfluorosulfonated Ionomer Nanofibers by Solution Blow Spinning.

Project description:In this work, we report the preparation of high-purity perfluorosulfonated ionomer (Nafion) nanofibers (NFs) via solution blow spinning (SBS). Fiber formation in solution jet spinning is strongly dependent on the structure of the spinning solution. Upon adding a small amount of poly(ethyleneoxide) (PEO) as a spinning aid to Nafion dispersion, most of the highly ordered Nafion aggregate disappeared, allowing the stable production of bead-free and smooth high-purity NFs (Nafion/PEO = 99/1) by SBS. The microstructure of the blowspun Nafion NFs differed from that of electrospun NFs. In the blowspun NFs, incomplete microphase separation between hydrophilic (ionic) and hydrophobic domains was observed, but the crystallization of CF2-CF2 chains was enhanced owing to the high extensional strain rate and rapid solidification during SBS. These findings provide fundamental information for the preparation and characterization of blowspun Nafion NFs.

| S-EPMC8228795 | biostudies-literature