Firing Increases Arsenic Leaching from Ceramic Water Filters via Arsenic and Iron Phase Transformations.

ABSTRACT: Ceramic water filters (CWFs) are produced globally using local clay sources and can effectively remove bacterial pathogens during point-of-use water treatment. The ceramic production process involves firing clay mixed with burnout material at temperatures of 800-1100 °C, which induces mineralogical changes leading to increased arsenic (As) leaching from CWF material compared to source clay. Unfired clay and fired CWFs from Cambodia, Canada, and Mexico, CWF from Laos, and test-fired clay from the United States were analyzed to determine the extent of As leaching from CWFs that range in As (<1 to 16 mg kg^-1) and iron (Fe) (0.6 to 5%) content. Deionized water, NaOH, HCl, and oxalate extractions showed that firing increased As solubility and decreased Fe solubility compared to unfir