Fabricated Flexible Composite for a UV-LED Color Filter and Anti-Counterfeiting Application of Calcium Molybdate Phosphor Synthesized at Room Temperature.

ABSTRACT: Crystalline CaMoO4 and rare-earth-doped CaMoO4:RE3+ (RE = Tb, Eu) phosphors were synthesized at room temperature using a co-precipitation method. The crystal structure of the synthesized powder was a tetragonal structure with a main diffraction peak (112) phase. When CaMoO4 was excited at 295 nm, it showed a central peak of 498 nm and light emission in a wide range of 420 to 700 nm. Rare-earth-ion-doped CaMoO4:Tb3+ was excited at 288 nm and a green light emission was observed at 544 nm, and CaMoO4:Eu3+ was excited at 292 nm and a red light emission was observed at 613 nm. To take advantage of the light-emitting characteristics, a flexible composite was manufactured and a color filter that could be used for UV-LEDs was manufactured. In addition, it was suggested that an ink that could be ch