Immobilization of Laccase Through Inorganic-Protein Hybrids Using Various Metal Ions.

ABSTRACT: In this study, the inorganic-protein hybrid strategy was employed for immobilization of laccase from Rhus vernicifera (Rvlac) using various metals calcium, cobalt, copper, and zinc (Zn). The efficient synthesis of hybrids for Rvlac immobilization was noted at 4 °C for incubation of 24 h. Among these hybrids, the maximum encapsulation yields (EY) of 90.1% and relative activity (RA) of 225% to free enzyme were recorded for Zn and Rvlac based inorganic-protein hybrids as Zn₃(PO₄)₂-Rvlac. The upper optimum pH, and temperature values were observed of 4.0, and 45 °C after immobilization as compared to 3.5, and 40 °C for the free enzyme, respectively. After encapsulation, Rvlac showed a significant improvement up to 11.4-fold in pH and 5.7-fold in temperature the activity profiles. Free enzyme completely lost its activity at 60 °C after 2 h of incubation, whereas Zn₃(PO₄)₂-Rvlac retained its residual activity of 56.7% under similar conditions. After ten cycles of reusability, Zn₃(PO₄)₂-Rvlac possessed high residual activity of 90.8%. This study showed that the variation in the metal ions for immobilization of Rvlac as inorganic-protein hybrids significantly altered EY and RA. Also, Zn₃(PO₄)₂-Rvlac proved more efficient as compared to free laccase that can be beneficially employed for biotechnological applications.

Supplementary information

The online version contains supplementary material available at 10.1007/s12088-022-01000-5.

SUBMITTER: Patel SKS

PROVIDER: S-EPMC8980120 | biostudies-literature | 2022 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Immobilization of Laccase Through Inorganic-Protein Hybrids Using Various Metal Ions.

Patel Sanjay K S SKS Kalia Vipin C VC Kim Sang-Yong SY Lee Jung-Kul JK Kim In-Won IW

Indian journal of microbiology 20220127 2

In this study, the inorganic-protein hybrid strategy was employed for immobilization of laccase from Rhus vernicifera (Rvlac) using various metals calcium, cobalt, copper, and zinc (Zn). The efficient synthesis of hybrids for Rvlac immobilization was noted at 4 °C for incubation of 24 h. Among these hybrids, the maximum encapsulation yields (EY) of 90.1% and relative activity (RA) of 225% to free enzyme were recorded for Zn and Rvlac based inorganic-protein hybrids as ...[more]

PMID: 35462708

Similar Datasets

Project description:In this study, we used solvent assisted mechano-synthesis strategies to form multifunctional organic-inorganic nanocomposites capable of removing both organic and inorganic contaminants. A zeolite X (Ze) and activated carbon (AC) composite was synthesized via state-of-the-art mechanical mixing in the presence of few drops of water to form Ze/AC. The second composite (Ze/L/AC) was synthesized in a similar fashion, however this composite had the addition of disodium terephthalate as a linker. Both materials, Ze/AC and Ze/L/AC, were characterized using scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDS), Powdered X-ray diffraction (P-XRD), Fourier-transform infrared spectrometry (FTIR), Accelerated Surface Area and Porosimetry System (ASAP), and thermal gravimetric analysis (TGA). The SEM-EDS displayed the surface structure and composition of each material. The sodium, oxygen and carbon contents increased after linker connected Ze and AC. The P-XRD confirmed the crystallinity of each material as well as the composites, while FTIR indicated the function groups (C=C, O-H) in Ze/L/AC. The contaminant adsorption experiments investigated the effects of pH, temperature, and ionic strength on the adsorption of methylene blue (MB) and Co(II) for each material. In MB adsorption, the first-order reaction rate of Ze/L/AC (0.02 h-1) was double that of Ze/AC (0.01 h-1). The reaction rate of Ze/L/AC (4.8 h-1) was also extraordinarily higher than that of Ze/AC (0.6 h-1) in the adsorption of Co(II). Ze/L/AC composite achieved a maximum adsorption capacity of 44.8 mg/g for MB and 66.6 mg/g for Co(II) ions. The MB adsorption of Ze/AC and Ze/L/AC was best fit in Freundlich model with R2 of 0.96 and 0.97, respectively, which indicated the multilayer adsorption. In the Co(II) adsorption, the data was highly fit in Langmuir model with R2 of 0.94 and 0.92 which indicated the monolayer adsorption. These results indicated both materials exhibited chemisorption. The activation energy of Ze/L/AC in MB adsorption (34.9 kJ mol-1) was higher than that of Ze/L/AC in Co (II) adsorption (26 kJ mol-1).

Dataset Information

Immobilization of Laccase Through Inorganic-Protein Hybrids Using Various Metal Ions.

Supplementary information

Publications

Immobilization of Laccase Through Inorganic-Protein Hybrids Using Various Metal Ions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets