The Reinforced Electromagnetic Interference Shielding Performance of Thermal Reduced Graphene Oxide Films via Polyimide Pyrolysis.


ABSTRACT: In this work, thin reduced graphene oxide (GO) composite films were fabricated for electromagnetic interference (EMI) shielding application. High solid content GO slurry (7 wt %) was obtained by dispersing GO clay in polymer solution under high-speed mechanical stirring. A composite film with varied thickness (10-150 μm) could be fabricated in pilot scale. After an optimized thermal annealing procedure, the final product showed good conductivity, which reached 500 S·cm-1. The thin sample (thickness < 0.1 mm) containing 10% polymer showed an enhanced EMI shielding performance of 55-65 dB. The outstanding EMI shielding efficiency as well as good suppleness and industrialized potential of thermal reduced graphene oxide polymer composite films could make a progress on their application in flexible devices as an EMI shielding material.

SUBMITTER: Xu L 

PROVIDER: S-EPMC8991919 | biostudies-literature | 2022 Apr

REPOSITORIES: biostudies-literature

altmetric image

Publications

The Reinforced Electromagnetic Interference Shielding Performance of Thermal Reduced Graphene Oxide Films via Polyimide Pyrolysis.

Xu Lijian L   Wang Ledong L   Zhang Wenqian W   Xue Jie J   Hou Shifeng S  

ACS omega 20220324 13


In this work, thin reduced graphene oxide (GO) composite films were fabricated for electromagnetic interference (EMI) shielding application. High solid content GO slurry (7 wt %) was obtained by dispersing GO clay in polymer solution under high-speed mechanical stirring. A composite film with varied thickness (10-150 μm) could be fabricated in pilot scale. After an optimized thermal annealing procedure, the final product showed good conductivity, which reached 500 S·cm<sup>-1</sup>. The thin sam  ...[more]

Similar Datasets

| S-EPMC9992768 | biostudies-literature
| S-EPMC8145072 | biostudies-literature
| S-EPMC8828842 | biostudies-literature
| S-EPMC8912556 | biostudies-literature
| S-EPMC6641376 | biostudies-literature
| S-EPMC9470028 | biostudies-literature
| S-EPMC7905797 | biostudies-literature
| S-EPMC9070049 | biostudies-literature
| S-EPMC9464893 | biostudies-literature