Construction and performance of a simple and efficient g-C₃N₄ photocatalytic hydrogen production system.

ABSTRACT: Surface and bulk structure modification is an effective strategy to improve the photocatalytic performance of g-C₃N₄ (CN). In this work, dilute NaOH solution was used in situ to regulate the CN structure for enhanced photocatalytic hydrogen evolution reaction (HER). Characterization results indicate that after treatment with dilute NaOH solution, the surface of CN was hydroxylated, resulting in the change of CN structure and the increase of BET specific surface area. Furthermore, some Na⁺ ions can be intercalated into the framework of CN, and form the Na-N bond. These modifications boost the HER activity of CN. The test carried out in 7.5 mM NaOH solution shows the highest activity and it is almost 3.7 times higher than that performed in water. Control tests indicate that hydroxides of other alkali and alkali earth metals such as LiOH, KOH, Ca(OH)₂, and Ba(OH)₂ have similar promotion effects. This work demonstrates a valid and simple way to enhance the HER activity of CN through performing the reaction in a weakly alkaline solution.

SUBMITTER: Xu Y

PROVIDER: S-EPMC9043151 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Construction and performance of a simple and efficient g-C3N4 photocatalytic hydrogen production system.

Xu Yun Y Wang Xuewei X Zhu LingFeng L An Ran R Qi Zhulin Z Wu Haisu H Miao Tifang T Li Longfeng L Fu Xianliang X

RSC advances 20211108 57

Surface and bulk structure modification is an effective strategy to improve the photocatalytic performance of g-C3N4 (CN). In this work, dilute NaOH solution was used in situ to regulate the CN structure for enhanced photocatalytic hydrogen evolution reaction (HER). Characterization results indicate that after treatment with dilute NaOH solution, the surface of CN was hydroxylated, resulting in the change of CN structure and the increase of BET specific surface area. ...[more]

PMID: 35492762

Similar Datasets

Project description:A facile and cost-effective approach assisted by ball milling (BM) of commercial titanium dioxide (TiO2), has been utilized to develop cheaper and efficient construction materials. At least three of the commercial and cheaper TiO2 samples (BA01-01, BA01-01+ and R996, designated as A1, A4 and R1, respectively) were selected and subjected to BM treatment to enhance their photocatalytic efficiencies, if possible. It was noted, that the samples A1, A4 and R1 were typical composites of TiO2 and calcium carbonate (CaCO3) and contained varying proportions of anatase, and rutile phases of TiO2 and CaCO3. Two of the highly efficient commercial TiO2 samples, Degussa P25 (simply designated as P25) and ST01 (Ishihara Ind.) were selected for making benchmark comparisons of photocatalytic efficiencies. The BM treated TiO2 samples (designated as TiO2-BM with respect to A1, A4 and R1) were evaluated for photocatalytic efficiencies both in both aqueous (methylene blue (MB)) and gaseous (NOx) photodegradation reactions. Based on detailed comparative investigations, it was observed that A1-BM photocatalyst exhibited superior photocatalytic performances over A4-BM and R1-BM, towards both MB and NOx photodegradation reactions. The difference of NOx photodegradation efficiency between the mortar mixed with A1-BM and that mixed with ST01, and P-25 at 15% were 16.6%, and 32.4%, respectively. Even though the mortar mixed with A1-BM at 15% composition exhibited a slightly lower NOx photodegradation efficiency as compared to mortar mixed with the expensive ST01 and P-25 photocatalysts, the present work promises an economic application in the eco-friendly construction materials for air purification considering the far lower cost of A1. The reasons for the superior performance of A1-BM were deduced through characterization of optical properties, surface characteristics, phase composition, morphology, microstructure and particle size distribution between pristine and BM treated A1 using characterization techniques such as diffuse reflectance spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction analysis, field emission scanning electron microscopy and particle size analysis.

Dataset Information

Construction and performance of a simple and efficient g-C₃N₄ photocatalytic hydrogen production system.

Publications

Construction and performance of a simple and efficient g-C<sub>3</sub>N<sub>4</sub> photocatalytic hydrogen production system.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets